Sealing gasket material prepared by mixing three types of rubber and preparation method of sealing gasket material

A technology for rubber mixing and sealing gaskets, which is applied in the field of gasket materials and its preparation, can solve the problems of unsatisfactory sealing effect, poor wear resistance, low strength, etc., achieve good temperature resistance, improve process performance, and reduce toxic and side effects Effect

Inactive Publication Date: 2014-04-09
WUHU WANRUN MACHINERY
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sealing gasket material prepared by mixing three types of rubber and preparation method of sealing gasket material
  • Sealing gasket material prepared by mixing three types of rubber and preparation method of sealing gasket material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be described in detail below through specific examples.

[0010] A gasket material made by mixing three types of rubber, made of the following raw materials in parts by weight (kg): Silicone rubber 20, Chlorohydrin rubber (H45) 30, Nitrile rubber 20, Precipitated white carbon black 24 , diphenylsilanediol 3, ferric oxide 3, dicumyl peroxide 2, oleic acid 1.5, zinc oxide 2, butadiene 1, butyl rubber (BBK232) 10, triethyl citrate 3 , Tung oil 3, N220 carbon black 18, N339 carbon black 25, modified attapulgite 10;

[0011] The modified attapulgite is made of the following raw materials in parts by weight (kg): attapulgite 20, toluene diisocyanate 4, trimethylolpropane triacrylate 2, alum 1, polyisobutylene 2, aluminate diisocyanate Joint agent DL-4111, sodium tripolyphosphate 2, ricinoleic acid 1, aluminum nitride powder 2, methyl acrylate 2, pepper seed oil 1; the preparation method is to put attapulgite into a calciner at 700-720°C Calcined f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sealing gasket material prepared by mixing three types of rubber. The sealing gasket material is characterized by being prepared from the following raw materials in parts by weight: 20-25 parts of silicone rubber, 30-35 parts of epichlorohydrin rubber (H45), 20-24 parts of butadiene-acrylonitrile rubber, 24-28 parts of precipitated silica, 3-4 parts of diphenyl silanediol, 3-4 parts of ferric oxide, 2-3 parts of dicumyl peroxide, 1.5-2.5 parts of eleostearic acid, 2-5 parts of zinc oxide, 1-2 parts of butadiene, 10-15 parts of butyl rubber (BBK232), 3-5 parts of triethyl citrate, 3-5 parts of tung oil, 18-23 parts of N220 carbon black, 25-30 parts of N339 carbon black and 10-12 parts of modified attapulgite. By adding the modified attapulgite, the process performance of a rubber material is improved. By using an environment-friendly ingredient, the toxic and side effects and the environmental pollution are reduced. The sealing gasket material is high in temperature change resistance, high in oil resistance, high in corrosion resistance, high in ageing resistance and good in sealing performance.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to a gasket material prepared by mixing three types of rubber and a preparation method thereof. Background technique [0002] Gasket is a material used for sealing inside machinery, equipment, pipelines, etc. The gaskets currently used are mostly rubber gaskets, which are characterized by high temperature resistance, ozone resistance, natural aging resistance, vacuum resistance, fuel oil resistance, lubricating oil resistance, strong oxidant resistance, chemical resistance and good electrical insulation performance. Widely used in defense industry and civilian industry. However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore researching and developing a kind of high-performance rubber gasket has become the task of top priority. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L71/03C08L83/04C08L9/02C08L23/22C08L23/20C08K13/06C08K9/02C08K3/34C08K3/36C08K5/5419C08K3/22C08K5/14C08K5/09C08K5/11C08K5/01C08K3/04C08K5/29C08K3/30C08K5/10C08K3/32C08K3/28C08K5/101C08K5/103B29B7/28
Inventor 吴贤春
Owner WUHU WANRUN MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap