A rubber sheath and universal joint technology, applied in the field of rubber sheath, can solve the problems of poor electrical insulation, poor cold resistance, etc., and achieve the effects of strong wear resistance, good water and oil resistance, and superior comprehensive performance

Inactive Publication Date: 2014-04-16
WUHU JINYING MACHINERY SCI & TECH DEV
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Slightly poor cold resistanc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of rubber sheath of automobile universal joint, it is made up of the raw material of following parts by weight (kg):

[0016] Neoprene S40V 100, isooctyl dithioglycolate, di-n-octyl tin 0.6, chlorofluoroethrin 2, β-hydroxyalkylamide 3, anhydrous calcium chloride 8, acetyl triethyl citrate 8, iron oxide red 2. Glycerin triacetate 2, sodium sulfide 2, fly ash 14, calcium stearate 5, 2,6-di-tert-butyl-p-cresol 1, accelerator CZ 2, sulfur 1.2, composite filler 20;

[0017] Described composite filler is made up of the raw material of following weight part:

[0018] Black soil 45, Wannian ash 10, fly ash 13, soda powder 3, bis-imidazolidinyl urea 1, hexamethoxymethylmelamine resin 3, appropriate amount of water;

[0019] Add the above-mentioned soda powder into 2 times the water, stir evenly, add Wannian ash, heat and stir at 50°C until the water is dry, add hexamethoxymethylmelamine resin, stir and disperse at 200 rpm for 3 minutes to obtain a premix; The above-ment...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a rubber sheath for an automobile universal joint. The rubber sheath comprises the following raw materials in parts by weight: 96-100 parts of neoprene S40V, 0.6-1 part of imarcaptoacetate dioctyltin, 1-2 parts of chlorine fluorine ethofenprox, 2-3 parts of beta-hydroxyalkylamide, 6-8 parts of anhydrous calcium chloride, 6-8 parts of triethyl acetocitrate, 1-2 parts of iron oxide red, 2-3 parts of glycerol triacetate, 1-2 parts of sodium sulfide, 10-14 parts of coal ash, 3-5 parts of calcium stearate, 1-2 parts of 2,6-Di-tert-butyl-4-methylphenol, 1-2 parts of an accelerating agent CZ, 0.8-1.2 parts of sulphur and 16-20 parts of a composite filler. The rubber sheath for the automobile universal joint, provided by the invention, has the effects of vibration reduction and sound insulation, and is good in water proofing and oil resistance, strong in abrasion resistance and excellent in comprehensive performance.

Description

technical field [0001] The invention mainly relates to the field of auto parts, in particular to a rubber sheath for an auto universal joint. Background technique [0002] Neoprene has good physical and mechanical properties, oil resistance, heat resistance, flame resistance, sunlight resistance, ozone resistance, acid and alkali resistance, and chemical reagent resistance. The disadvantage is poor cold resistance and storage stability. It has high tensile strength, elongation and reversible crystallinity, and good adhesion. Aging resistance and heat resistance. Excellent oil and chemical resistance. Weather resistance and ozone aging resistance are second only to ethylene propylene rubber and butyl rubber. The heat resistance is equivalent to that of nitrile rubber, the decomposition temperature is 230-260°C, the short-term resistance is 120-150°C, and it can be used for a long time at 80-100°C. It has certain flame retardancy. Oil resistance is second only to nitr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L11/00C08K13/06C08K5/58C08K5/20C08K5/098C08K3/06C08K3/16
Inventor 韦中祥
Owner WUHU JINYING MACHINERY SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap