Antistatic waterborne polyurethane coating and preparation method thereof

A water-based coating and antistatic technology, applied in polyurea/polyurethane coatings, conductive coatings, coatings, etc., can solve the problems of high cost, environmental protection, and complicated methods of single carbon nanotube conductive fillers, and achieve antistatic performance reduction , small amount of addition, simple operation process

Active Publication Date: 2014-04-23
AODA KOALA PAINT HUIZHOU
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The Chinese patent application number CN201010281940.4 discloses "Preparation method of solvent-based two-component carbon nanotube polyurethane nanocomposite coating", which uses in-situ polymerization to prepare solvent-based two-component carbon Nanotube polyurethane nanocomposite coatings, but the use of organic solvents has caused corresponding environmental problems
The Chinese patent application with the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic waterborne polyurethane coating and preparation method thereof
  • Antistatic waterborne polyurethane coating and preparation method thereof
  • Antistatic waterborne polyurethane coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1:

[0017] 1. Put 1.5 parts of carbon nanotubes into concentrated H 2 SO 4 And HNO 3 In the mixed solution (volume ratio 3:1), treated for 2.5h under the action of ultrasonic vibration and mechanical stirring, and then washed with a large amount of deionized water to neutrality.

[0018] 2. Add 45 parts of aqueous hydroxyl-containing acrylic dispersion (Bayhydrol XP series 2457) into the cone mill, add 1.0 part of carbon nanotubes obtained in step 1 under medium speed grinding, 0.2 part of conductive carbon black, and 0.1 part of wetting agent , 0.03 parts defoamer, 0.2 parts leveling agent, 15 parts water, disperse for 20 minutes.

[0019] 3. Add 16 parts of hydrophilic aliphatic polyisocyanate (Bayhydur XP series 2451) and disperse for 10 minutes to obtain a waterborne polyurethane antistatic coating containing carbon nanotubes.

Example Embodiment

[0020] Example 2:

[0021] 1. Put 2.0 parts of carbon nanotubes into concentrated H 2 SO 4 And HNO 3 In the mixed solution (volume ratio of 3:1), treated with ultrasonic vibration and mechanical stirring for 4h, and then washed with a large amount of deionized water to neutrality.

[0022] 2. Add 50 parts of aqueous hydroxyl-containing acrylic dispersion (Bayhydrol XP series 2470) into the cone mill, add 2.0 parts of carbon nanotubes obtained in step 1 under medium speed grinding, 0.3 parts of conductive carbon black, and 0.15 parts of wetting agent , 0.02 parts defoamer, 0.1 parts leveling agent, 17 parts water, 25 minutes dispersion.

[0023] 3. Add 17 parts of hydrophilic aliphatic polyisocyanate (Bayhydur XP series 2547) and disperse for 10 minutes to obtain a waterborne polyurethane antistatic coating containing carbon nanotubes.

Example Embodiment

[0024] Example 3:

[0025] 1. Put 4.0 parts of carbon nanotubes into concentrated H 2 SO 4 And HNO 3 In the mixed solution (volume ratio of 3:1), under the action of ultrasonic vibration and mechanical stirring, treat for 5h, and then wash with a large amount of deionized water to neutrality.

[0026] 2. Add 48 parts of aqueous hydroxyl-containing acrylic dispersion (Bayhydrol XP series 2546) into the cone mill, add 4.0 parts of carbon nanotubes obtained in step 1 under medium speed grinding, 0.5 parts of conductive carbon black, and 0.3 parts of wetting agent , 0.05 parts defoamer, 0.5 parts leveling agent, 20 parts water, dispersed for 30 minutes.

[0027] 3. Add 20 parts of hydrophilic aliphatic polyisocyanate (Bayhydur XP series 2451) and disperse for 20 minutes to obtain a waterborne polyurethane antistatic coating containing carbon nanotubes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical fields of a polymer composite material and a preparation method thereof, and particularly relates to an antistatic waterborne polyurethane coating and a preparation method thereof. The antistatic waterborne polyurethane coating comprises the following components in parts by weight: 1.0-5.0 parts of carbon nano tube, 0.1-1.0 part of conductive carbon black, 45-55 parts of waterborne hydroxyl-containing acrylic dispersion, 15-20 parts of hydrophilic aliphatic polyisocyanate, 15-20 parts of water, 0.1-0.3 part of wetting agent, 0.01-1.0 part of defoamer, and 0.1-1.0 part of flatting agent. The waterborne polyurethane coating prepared by the method has good anti-static performance, can be applied to a few of electronic equipment and elements, and effectively prevents electrostatic aggregation.

Description

technical field [0001] The invention belongs to the technical field of a polymer composite material and a preparation method thereof, and in particular relates to an antistatic polyurethane water-based coating and a preparation method thereof. Background technique [0002] Most polymer materials are excellent electrical insulating materials, and their surface resistivity ρ s (10 14 ~10 17 Ω) and volume resistivity ρ v (10 15 ~10 18 Ω·m) is very large and has good electrical insulation properties, but in general industrial production and product applications, friction and peeling processes often occur, and a large amount of static electricity is easy to accumulate, which hinders the production process and product quality. Electrostatic hazards, such as causing distortion of precision instruments, scrapping of electronic components, fire and explosion accidents. The use of antistatic coatings can conduct the charge on the surface of polymer materials and eliminate the ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D7/12C09D5/24
Inventor 袁进松梁浩谢芳强那陈日云
Owner AODA KOALA PAINT HUIZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap