Modified high chlorinated polyethylene antirust coating and preparation method thereof

A technology for chlorinated polyethylene and anti-rust coatings, applied in anti-corrosion coatings, fire-retardant coatings, coatings and other directions, can solve the problems of poor acid and alkali resistance and salt water resistance, long drying time, etc., and achieves a simple and easy preparation method. The effect of running, short drying time, good salt water resistance

Inactive Publication Date: 2014-04-30
SUZHOU CITY BANGCHENG ELECTRICITY TECH
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, heavy-duty anti-corrosion coatings have good acid and alkali resistance, and the paint film is thicke

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0011] Example 1

[0012] The modified high chlorinated polyethylene anti-rust coating includes the following raw materials in parts by mass: 72 parts of high chlorinated polyethylene resin, 10 parts of polyvinyl chloride resin, 5 parts of zinc borate, 8 parts of tributyl citrate, 0.6 parts of polyvinyl acetate, 0.1 parts of triphenyl phosphite, 8 parts of iron oxide red, 8 parts of mica powder, 30 parts of toluene, 15 parts of ethyl acetate.

[0013] The preparation method of this embodiment: according to the mass ratio, add high chlorinated polyethylene resin and polyvinyl chloride resin to toluene, stir evenly, add ethyl acetate, zinc borate, tributyl citrate, polyvinyl acetate, and ethylene After mixing triphenyl phosphate, iron oxide red and mica powder, the modified high chlorinated polyethylene flame-retardant anti-rust paint is obtained.

[0014] The finished product was tested for performance, and the test results are shown in Table 1.

Example Embodiment

[0015] Example 2

[0016] The modified high chlorinated polyethylene anti-rust coating includes the following raw materials in parts by mass: 78 parts of high chlorinated polyethylene resin, 12 parts of polyvinyl chloride resin, 7 parts of zinc borate, 10 parts of tributyl citrate, 1.2 parts of polyvinyl acetate, 0.5 parts of epoxidized soybean oil, 10 parts of iron oxide red, 14 parts of mica powder, 40 parts of toluene, and 18 parts of ethyl acetate.

[0017] The preparation method of this embodiment is the same as that of embodiment 1, wherein the stabilizer is epoxy soybean oil. The finished product was tested for performance, and the test results are shown in Table 1.

Example Embodiment

[0018] Example 3

[0019] The modified high chlorinated polyethylene anti-rust coating includes the following raw materials in parts by mass: 76 parts of high chlorinated polyethylene resin, 11 parts of polyvinyl chloride resin, 6 parts of zinc borate, 9 parts of tributyl citrate, 0.8 parts of polyvinyl acetate, 0.4 parts of xylitol, 9 parts of iron oxide red, 12 parts of mica powder, 35 parts of toluene, and 16 parts of ethyl acetate.

[0020] The preparation method of this embodiment is the same as that of embodiment 1, wherein the stabilizer is xylitol, and the performance of the finished product is tested. The test results are shown in Table 1.

[0021] The finished products prepared in Examples 1-3 were tested for performance, and the results are shown in Table 1:

[0022] Table 1 Performance test data

[0023] performance Example 1 Example 2 Example 3 Surface dry, h303030 Hard work, h 10109

[0024] It can be seen from the above table that the drying time of the coating of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides modified high chlorinated polyethylene antirust coating and a preparation method thereof. The modified high chlorinated polyethylene antirust coating comprises the following raw materials in parts by mass: 72-78 parts of high chlorinated polyethylene resin, 10-12 parts of polyvinyl chloride resin, 5-7 parts of zinc borate, 8-10 parts of tributyl citrate, 0.6-1.2 parts of polyvinyl acetate, 0.1-0.5 part of a stabilizer, 8-10 parts of iron oxide red, 8-14 parts of mica powder, 30-40 parts of toluene and 15-18 parts of ethyl acetate. The modified high chlorinated polyethylene antirust coating has good resistance to acid and base and salt water resistance, is relatively short in drying time, convenient to coat and free of limitation of seasons and can be cured at a low temperature; the preparation method provided by the invention is simple and practicable and is suitable for large-scale popularization and application.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a modified high-chlorinated polyethylene antirust coating and a preparation method thereof. Background technique [0002] In a relatively harsh environment, heavy-duty anti-corrosion coatings are particularly important, which can protect the device from rapid corrosion, thereby prolonging the life of the device. Generally, heavy-duty anti-corrosion coatings have good acid and alkali resistance, and the paint film is relatively thick, but there are still shortcomings such as poor acid and alkali resistance and salt water resistance, and long drying time. [0003] To sum up, how to overcome the deficiencies of the prior art has become an urgent problem to be solved in the field of coatings. Contents of the invention [0004] The purpose of the invention is to overcome the deficiencies in the prior art and propose a modified highly chlorinated polyethylene antirust coating and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D123/28C09D127/06C09D131/04C09D5/08C09D5/18C09D7/12
Inventor 陈汉刚
Owner SUZHOU CITY BANGCHENG ELECTRICITY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap