A technology of calcium carbonate filler and zinc stearate, which is applied in the field of calcium carbonate filler, can solve problems such as poor dispersion, inability to achieve filling and reinforcing effects, and insufficient compatibility of high polymers to achieve improved surface properties and good flame retardancy Fire-resistant effect, good filling and reinforcing effect

Inactive Publication Date: 2014-05-07
安徽雪城超细碳酸钙有限公司
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Calcium carbonate is an important class of functional inorganic fillers. It has the advantages of low price, abundant reserves, stable performance, easy processing, and non-toxicity. It can significantly improve the processing performance and physical properties of materials and reduce production costs. It is widely used In the fields of plastics, rubber, coatings, papermaking, etc., because c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0012] The modified calcium carbonate filler of the present embodiment is made of the following raw materials in parts by weight: calcium carbonate 200, shell powder 2, aluminum hydroxide 9, zinc stearate 3, borax 1, ammonium molybdate 2, chromium oxide 3, molybdenum Phyloline 2, triethyl citrate 25, hexamethylphosphoric triamide 2, antioxidant NBC 2, additive 5;

[0013] The above-mentioned additives are made of the following raw materials in parts by weight: methyltriethoxysilane 2, zirconium fluoride 1, nano silicon dioxide 1, basswood ash 2, crosslinking agent TAC1, ascorbic acid 1; its preparation method is to The materials are mixed, ground and dispersed evenly, and the product is obtained.

[0014] The modified calcium carbonate filler is prepared by the following method:

[0015] (1) Mix calcium carbonate, shell powder, aluminum hydroxide, borax, chromium oxide, and triethyl citrate, grind for 20 minutes, and pass through a 200-mesh sieve;

[0016] (2) Mix the materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a calcium carbonate filler, and particularly relates to a flame-retardant zinc stearate modified calcium carbonate filler. The modified calcium carbonate is prepared from the following raw materials in parts by weight: 200 parts of calcium carbonate, 1-2 parts of shell powder, 8-10 parts of aluminium hydroxide, 2-3 parts of zinc stearate, 1-2 parts of sodium borate, 2-3 parts of ammonium molybdate, 3-4 parts of chromium oxide, 1-2 parts of morpholine, 23-25 parts of triethyl citrate, 1-2 parts of hexamethylphosphoric triamide, 1-2 parts of anti-aging agent NBC and 4-5 parts of assistant. Modification treatment is carried out on calcium carbonate by adopting the raw materials such as zinc stearate, morpholine and the like; the performance indexes such as oil absorption value, viscosity, activating rate and the like of the modified calcium carbonate powder are improved, which indicates that the modified calcium carbonate filler is more easily dispersed and compatible in a medium. Compared with the material filled by unmodified calcium carbonate, the mechanical property of a polyvinyl chloride (PVC) material filled by the modified calcium carbonate filler disclosed by the invention is obviously improved, the flame-retardant and fire-resistant grades are also improved, and good toughening and reinforcing effects are achieved.

Description

technical field [0001] The invention relates to a calcium carbonate filler, in particular to a flame-retardant zinc stearate modified calcium carbonate filler. Background technique [0002] Calcium carbonate is an important class of functional inorganic fillers. It has the advantages of low price, abundant reserves, stable performance, easy processing, and non-toxicity. It can significantly improve the processing performance and physical properties of materials and reduce production costs. It is widely used In the fields of plastics, rubber, coatings, papermaking, etc., because calcium carbonate is a hydrophilic compound, there are defects such as insufficient compatibility with polymers and poor dispersion in practical applications, and satisfactory filling and reinforcing effects cannot be achieved. Therefore, Calcium carbonate needs to be modified to improve its dispersion and compatibility in various materials, so as to achieve the effect of improving product performance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/06C08K9/04C08K9/02C08K3/26C08K3/34C08K3/22C08K5/098C08K3/38C08K3/28C08K5/3432C08K5/11C08K5/5399C08K5/5419C08K3/16C08K3/36C08K5/3492
Inventor 窦念根
Owner 安徽雪城超细碳酸钙有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap