Inorganic combined coating and method for producing radiator by applying same

A technology of inorganic pigments and coatings, which is applied in the direction of surface coating liquid devices, coatings, pretreatment surfaces, etc., and can solve problems such as the generation of oxide layers, loss of function, and low thermal conductivity of radiators

Inactive Publication Date: 2014-05-14
广东雷特斯建材科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Bare metal body: ①Formulation: aluminum ingots, alloy mixed ingots, copper materials, iron materials, etc. are melted at high temperature, and various shapes of fins / pipes are cast or die-cast to increase the heat dissipation area to dissipate heat; ②Process: Metal ingot melting → pouring mold → forming; ③ Existing problems: easy to oxidize, bare metal profiles will produce an oxide layer when exposed to air or water vapor in the air, causing heat dissipation failure of the product, rapid aging or loss of function of the product ; Not resistant to acid and alkali, the current air pollution is relatively serious, acidic, automobile exhaust, industrial pollution, oil pollution, etc., bare metal profiles are oxidized, acidified, and alkalized at any time, resulting in product heat dissipation failure and rapid product aging or go to function
[0005] Electrochemical or spray-coated heat-dissipating profiles of silicone protective layer: ①Formulation: metal ingots for casting are melted at high temperature, die-casting, organic coating; ②Process: metal ingot melting→casting mold→forming→oil removal→spraying→drying→product ; ③ Existing problems: poor heat dissipation, silicone is a poor conductor of heat, coating silicone on the radiator, the purpose is to prevent metal parts from being air, acidified, alkalized or oxidized, but the metal substrate of the radiator is all coated Covering will reduce the thermal conductivity of the entire radiator, causing the product to fail in heat dissipation, causing rapid aging or loss of function of the product; it is not weather-resistant, silicone coating and electrification are greatly affected by the environment, and the thermal expansion coefficient of the coating is relatively large. Cold shrinkage, easy to crack, and eventually cause heat dissipation failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Take 40Kg of water-based alumina dispersion, 4Kg of iron oxide dispersion, 8Kg of zirconia dispersion, 8Kg of titanium dioxide, 6Kg of inorganic pigment, 4Kg of carbon black, and 20Kg of filler to form component A; take 10Kg of silica as an inorganic film-forming accelerator for the B component. Among them, the inorganic pigments are selected according to the color of the radiator design. For example, black radiators use one of iron oxide black, cobalt oxide black, manganese cobalt black, ceramic black, and copper chromium black, or choose a variety of them to match, red Choose one of iron oxide red and ceramic red, or use two kinds of ratios. As in this embodiment, a black LED radiator is made, and the inorganic pigments are made of 20% each of iron oxide black, cobalt oxide black, manganese cobalt black, ceramic black, and copper chromium black.

[0031] Follow the steps below to make the LED heat sink:

[0032] 1) Aluminum is selected as the base material of the LE...

Embodiment 2

[0040] Take 35Kg of water-based alumina dispersion, 4Kg of iron oxide dispersion, 6Kg of zirconia dispersion, 6Kg of titanium dioxide, 8Kg of inorganic pigment, 6Kg of carbon black, and 22Kg of filler to form component A; take 13Kg of silica as an inorganic film-forming accelerator for the B component. Among them, the inorganic pigments are selected according to the color of the radiator design. For example, black radiators use one of iron oxide black, cobalt oxide black, manganese cobalt black, ceramic black, and copper chromium black, or choose a variety of them to match, red Choose one of iron oxide red and ceramic red, or use two kinds of ratios. Make the red heating radiator as in this embodiment, the inorganic pigment is made of each 50% of iron oxide red and ceramic red.

[0041] Follow the steps below to make the radiator fins:

[0042] 1) Selected as the base material of the heat sink. If it is a substrate workpiece with grease and rust, it is required that the sur...

Embodiment 3

[0051] Take 45Kg of water-based alumina dispersion, 7Kg of iron oxide dispersion, 9Kg of zirconia dispersion, 8Kg of titanium dioxide, 4Kg of inorganic pigment, 2Kg of carbon black, and 18Kg of filler to form component A; take 7Kg of silica as an inorganic film-forming accelerator for the B component. Among them, the inorganic pigments are selected according to the color of the radiator design. For example, black radiators use one of iron oxide black, cobalt oxide black, manganese cobalt black, ceramic black, and copper chromium black, or choose a variety of them to match, red Choose one of iron oxide red and ceramic red, or use two kinds of ratios. Make black car radiator as present embodiment, inorganic pigment selects cobalt oxide black for use. Follow these steps to make a car radiator:

[0052] 1) Copper is selected as the base material of the heat sink. If it is a substrate workpiece with grease and rust, it is required that the surface of the workpiece should be a cl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an inorganic combined coating and a method for producing a radiator by applying the same. The formula of the inorganic combined coating comprises A component including a water-based alumina dispersoid, a ferric oxide dispersoid, zirconium oxide dispersoid, titanium dioxide, inorganic pigment, carbon black and filler, and B component taking silica as an inorganic film forming accelerator; the method for producing the radiator by applying the inorganic combined coating comprises the steps of: performing oil removal and dust removal and sand blasting treatment to the surface of a base material workpiece; preparing, filtering and curing the coating; coating; sintering. The inorganic combined coating is advanced in formula, the radiator produced by applying the inorganic combined coating has the advantages of being good in radiation property, acid-proof and base-proof and oxidization-resistant, good in weather resistance, environment-friendly and the like, and is simple in technique, and energy-saving in production process.

Description

technical field [0001] The invention relates to a formula of heat-dissipating paint and a method for making a heat sink by using the same. Background technique [0002] Because of its good heat dissipation performance, many radiators are made of metal materials such as aluminum, copper, iron or alloys, such as: automobile radiators, air-conditioning radiators are made of aluminum or copper materials, heating radiators, infrared ray Furnace pipes are made of stainless steel, various military guns / barrels are made of various alloys for heat dissipation, induction cooker radiators and LED radiators are made of aluminum materials, some of the various heating plates are made of aluminum materials, and some are made of iron. [0003] However, most of the current radiators are made of bare metal body, electrochemical or sprayed protective layer profiles: [0004] Bare metal body: ①Formulation: aluminum ingots, alloy mixed ingots, copper materials, iron materials, etc. are melted a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/12B05D3/00B05D3/02B05D1/12B05D7/14B05D7/24
Inventor 韩勇敢钟志敏李綦
Owner 广东雷特斯建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products