Flame-retardant chloroprene rubber

A chloroprene rubber and natural rubber technology, applied in the field of flame retardant chloroprene rubber, can solve the problems of toxic hydrogen halide gas and secondary hazards, and achieve the effect of good comprehensive performance

Inactive Publication Date: 2014-06-25
ANHUI JIAMU RUBBLE & PLASTIC IND
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the flame retardant formulations of chloroprene rubber in China usually use halogen-containing flame retardants such as chlorine-containing flame retardants. Although the use of such flame retardants can satisfy a good flame-retardant effect, once a fire occurs, a large amount of toxic Corrosive hydrogen halide gas, causing secondary hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of flame-retardant neoprene rubber, neoprene rubber is made up of the following raw material components by weight: 100 parts of neoprene rubber, 12 parts of natural rubber, 3 parts of anti-aging agent RD, 0.25 parts of thiuram accelerator, 0.7 parts of zinc oxide , 6.5 parts of magnesium chloride, 4.5 parts of stearic acid, 48 parts of carbon black, 3 parts of dioctyl phthalate, 8 parts of antimony trioxide, and 5 parts of zinc borate.

Embodiment 2

[0014] A kind of flame-retardant chloroprene rubber, described chloroprene rubber is made up of the raw material component of following parts by weight: 100 parts of chloroprene rubber, 15 parts of natural rubber, 5 parts of anti-aging agent RD, 0.35 parts of thiuram accelerator, zinc oxide 1 part, 8 parts of magnesium chloride, 6 parts of stearic acid, 51 parts of carbon black, 4 parts of naphthenic oil, 10 parts of antimony trioxide, and 7 parts of zinc borate.

Embodiment 3

[0016] A kind of flame-retardant chloroprene rubber, described chloroprene rubber is made up of the raw material component of following parts by weight: 100 parts of chloroprene rubber, 10 parts of natural rubber, 1.5 parts of antioxidant RD, 0.2 part of thiuram accelerator, 0.4 parts of zinc oxide, 5 parts of magnesium chloride, 3 parts of stearic acid, 45 parts of carbon black, 2 parts of dibutyl sebacate, 5 parts of antimony trioxide, and 3 parts of zinc borate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a flame-retardant chloroprene rubber and belongs to the technical field of rubber. The chloroprene rubber disclosed by the invention is prepared from the following raw material constituents in parts by weight: 100 parts of chloroprene rubber, 10-15 parts of natural rubber, 1-5 parts of anti-aging agent RD, 0.2-0.35 parts of thiuram accelerants, 0.4-1 parts of zinc oxide, 5-8 parts of magnesium chloride, 3-6 parts of stearic acid, 45-52 parts of carbon black, 2-4 parts of softening agent, 5-10 parts of antimonous oxide and 3-7 parts of zinc borate. The flame-retardant chloroprene rubber disclosed by the invention has the excellent performances of chloroprene rubber and natural rubber due to a small amount of added natural rubber, thus improving the defects of single rubber; the flame-retardant chloroprene rubber disclosed by the invention is good in comprehensive performances, heat-resistant and flame-retardant due to antimonous oxide and zinc borate which are used as flame retardants.

Description

technical field [0001] The invention belongs to the technical field of rubber, in particular to flame-retardant chloroprene rubber. Background technique [0002] Chloroprene rubber is made of chloroprene as the main raw material through homopolymerization or copolymerization of a small amount of other monomers. Such as rubber products with high tensile strength, excellent heat resistance, light resistance, aging resistance, and oil resistance are better than natural rubber, styrene-butadiene rubber, and butadiene rubber. It has strong flame resistance and excellent flame retardancy resistance, high chemical stability and good water resistance. The disadvantage of chloroprene rubber is that it has poor electrical insulation performance and cold resistance, and the raw rubber is unstable during storage. Neoprene is widely used, such as making conveyor belts and transmission belts, covering materials for wires and cables, making oil-resistant hoses, gaskets, and chemical-res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L7/00C08K13/02C08K3/04C08K3/22C08K5/09C08K3/38C08K5/3437
Inventor 叶春会王泽平
Owner ANHUI JIAMU RUBBLE & PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com