A kind of electroless silver-plating method that is used for the non-sensitization activation of nylon substrate

A technology of chemical silver plating and nylon, which is applied in the directions of dry cleaning fiber products, textiles and papermaking, fiber processing, etc., can solve the problems of difficulty in controlling the degree of water washing, environmental pollution, and cumbersomeness, and achieves low cost, low environmental pollution, and simple process methods. Effect

Inactive Publication Date: 2016-01-27
DONGHUA UNIV +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process is cumbersome, and the degree of washing is difficult to control, and the waste liquid of washing contains heavy metal ions, which is easy to cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Fabric pretreatment, wash the nylon fabric in 20g / L pretreatment solution, take it out after 30 minutes of treatment at 40°C, rinse it with tap water; irradiate the washed nylon fabric with 0.4KW ultraviolet laser 10 minutes.

[0024] (2) prepare mixed solution, containing chitosan massfraction is 1.5%, polyvinyl alcohol massfraction 3%, regulate pH with glacial acetic acid to be 3, drip cross-linking agent glyoxal under stirring state, glyoxal The mass fraction is 0.05%, and stirred for 30 minutes to obtain a chitosan derivative solution.

[0025] (3) Soak the above-mentioned pretreated nylon fabric in the chitosan derivative solution for 30 minutes, and bake at 120° C. for 30 minutes.

[0026] (4) In the silver plating reaction solution, its composition: the concentration of silver nitrate is 15g / L, the concentration of sodium hydroxide is 10g / L, the concentration of ammonia water is 110ml / L, and the concentration of glucose is 3g / L, and the fabric is immersed in...

Embodiment 2

[0028] (1) Fabric pretreatment, wash the nylon fabric in 25g / L pretreatment solution, take it out after 30 minutes of treatment at 90°C, rinse it with tap water; irradiate the washed nylon fabric with 0.5KW ultraviolet laser 15 minutes.

[0029] (2) prepare mixed solution, containing chitosan massfraction is 4%, polyvinyl alcohol massfraction 5%, regulate pH with glacial acetic acid to be 4, under stirring state dropwise drop cross-linking agent glutaraldehyde, glutaraldehyde The mass fraction is 0.1%, and stirred for 50 minutes to obtain a chitosan derivative solution.

[0030] (3) Soak the above-mentioned pretreated nylon fabric in the chitosan derivative solution for 6 minutes, and bake at 160° C. for 30 minutes.

[0031] (4) In the configuration silver plating reaction solution, its composition: silver nitrate concentration is 10g / L, and sodium hydroxide concentration is 7g / L, and ammoniacal liquor concentration is 90ml / L, and glucose concentration is 4g / L, and fabric is ...

Embodiment 3

[0033] (1) Fabric pretreatment, wash the nylon fabric in 30g / L pretreatment solution, take it out after 20 minutes of treatment at 80°C, rinse it with tap water; irradiate the washed nylon fabric with 0.6KW ultraviolet laser 30 minutes.

[0034] (2) prepare mixed solution, chitosan massfraction is 6.5%, polyvinyl alcohol massfraction 8%, regulate pH with glacial acetic acid and be 5, under stirring state dropwise drop into cross-linking agent salicylaldehyde, salicylaldehyde mass fraction The fraction is 0.3%, and stirred for 60 minutes to obtain a chitosan derivative solution.

[0035] (3) Soak the above-mentioned pretreated nylon fabric in the chitosan derivative solution for 6 minutes, and bake at 140° C. for 20 minutes.

[0036] (4) In the configuration silver plating reaction solution, its composition: silver nitrate concentration is 13g / L, and sodium hydroxide concentration is 8g / L, and ammoniacal liquor concentration is 100ml / L, and sucrose concentration is 4g / L, fabri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a sensitization-free and activation-free chemical silvering method for a polyamide base body. The method comprises the following steps: (1) soaking a polyamide fabric in a pretreatment solution, washing, taking out and cleanly rinsing to obtain the washed polyamide fabric, and performing ultraviolet laser radiation to obtain the treated polyamide fabric; (2) preparing chitosan and polyvinyl alcohol mixing solution, adjusting the pH value by using glacial acetic acid, and dropwise adding a cross-linking agent under a stirring state to obtain a chitosan derivative solution; (3) soaking the treated polyamide fabric obtained in the step (1) in the chitosan derivative solution, and baking to obtain the polyamide fabric modified by chitosan derivatives; and (4) soaking the modified polyamide fabric in a silvering reaction solution, chemically plating, performing vibrating reaction in a vibrating dyeing machine, and then taking out, washing and drying to obtain the polyamide base body. The preparation method is simple and convenient, production conditions and requirements are simple, and according to the method, sensitization-free and activation-free effects are achieved, the production cost is low and the environmental pollution is low.

Description

technical field [0001] The invention belongs to the field of preparation of silver-plated fabrics, in particular to an electroless silver-plating method for sensitization-free activation of nylon substrates. Background technique [0002] At present, the electroless plating substrate has been gradually extended to the non-metallic field. First, an oxide film is formed on the non-metallic surface through sensitization, and then after activation, a redox reaction occurs on the non-metallic surface, so that the non-metallic surface can be formed on the non-metallic surface. Catalytically active noble metal particles. This process is cumbersome, and the degree of washing is difficult to control, and the waste liquid of washing contains heavy metal ions, which is easy to cause environmental pollution. [0003] Therefore, it is necessary to develop a new chemical plating process free of sensitization and activation, which can simplify the production process and reduce costs on the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M10/00D06M15/333D06M15/03D06M11/83D06L1/12C23C18/44C23C18/20D06M101/34
Inventor 刘保江吴文周德慧余秋婷赵强强金雅雯张俊胡春艳高品朱智甲
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com