Aerated concrete dry-blended plastering mortar and preparing method thereof
A technology for air-entrained concrete and plastering mortar, applied in the field of plastering mortar, can solve the problems of low shrinkage, hollowing, cracking, etc., and achieve the effects of low shrinkage, simple process steps and broad application prospects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example 1
[0022] A dry-mixed aerated concrete plastering mortar, which is composed of the following components by mass percentage: 22% Portland cement, 15% fly ash, 7% slag powder, 0.4% starch ether, 2% diatomaceous earth , 4% sodium alginate, 0.4% hydroxypropyl methyl cellulose ether, 0.6% VAE redispersible latex powder, 0.08% polypropylene fiber, 7% performance improver, the balance is construction fine sand, slag powder in mortar The particle size is 5μm, the fineness modulus of construction sand is 1.5, the equivalent diameter of polypropylene fiber is 12μm, and the length is 10mm. The performance modifier is composed of the following mass percentage components: 2% tea saponin, 0.6% Konjac flour, 6% graphene, 12% vermiculite powder, 7% sodium gluconate, the balance is glutinous rice flour, and the particle size of vermiculite powder is 1.2mm.
[0023] The preparation method of the aerated concrete dry-mix plaster mortar is as follows:
[0024] (1) After weighing tea sa...
Example Embodiment
[0026] Example 2
[0027] A dry-mixed aerated concrete plastering mortar, consisting of the following components by mass percentage: 20% Portland cement, 10% fly ash, 5% slag powder, 0.3% starch ether, 1% diatomaceous earth , 3% sodium alginate, 0.3% hydroxypropyl methyl cellulose ether, 0.5% VAE redispersible latex powder, 0.05% polypropylene fiber, 5% performance modifier, the balance is construction fine sand, slag powder in mortar The particle size is 3μm, the fineness modulus of construction sand is 1, the polypropylene fiber equivalent diameter is 10μm, and the length is 8mm. The performance modifier is composed of the following components by mass percentage: 1% tea saponin, 0.5% Konjac flour, 5% graphene, 10% vermiculite powder, 5% sodium gluconate, the balance is glutinous rice flour, and the vermiculite powder has a particle size of 1mm.
[0028] The preparation method of the aerated concrete dry-mix plaster mortar is as follows:
[0029] (1) After weighing tea saponin, ko...
Example Embodiment
[0031] Example 3
[0032] A dry-mixed aerated concrete plaster mortar, composed of the following components by mass percentage: 30% Portland cement, 20% fly ash, 10% slag powder, 0.5% starch ether, 3% diatomaceous earth , 5% sodium alginate, 0.5% hydroxypropyl methyl cellulose ether, 1% VAE redispersible latex powder, 0.1% polypropylene fiber, 10% performance modifier, the balance is construction fine sand, slag powder in mortar The particle size is 10μm, the fineness modulus of construction sand is 2, the equivalent diameter of polypropylene fiber is 30μm, and the length is 12mm. The performance modifier is composed of the following mass percentage components: 3% tea saponin, 1% Konjac flour, 10% graphene, 20% vermiculite powder, 10% sodium gluconate, the balance is glutinous rice flour, and the particle size of vermiculite powder is 1.5mm.
[0033] The preparation method of the aerated concrete dry-mix plaster mortar is as follows:
[0034] (1) After weighing tea saponin, konjac ...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap