Environment-friendly rubber sound-insulation material and preparation method thereof

A technology of sound insulation material and environmental protection rubber, applied in the direction of climate change adaptation, etc., can solve the problems of unfavorable car environmental protection, low sound insulation performance, and many materials used, and achieve the effects of excellent mechanical properties, high dielectric properties, and reduced raw material costs.

Active Publication Date: 2014-12-10
江苏金泰祥内外门业有限公司
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this material is that the sound insulation performance is low. In addition, the use of asphalt is not conducive to the environmental protection inside the car. At the same time, it uses a lot of materials and the process is cumbersome.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly rubber sound-insulation material and preparation method thereof
  • Environment-friendly rubber sound-insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The environmental protection rubber sound insulation material of the present invention, its preparation method is as follows:

[0022] (1) Preparation of composite rare earth oxides

[0023] Mix neodymium oxide, alumina and silicon oxide powders evenly, then put them into a mold and compact them into a cylinder with a diameter of 10mm and a height of 15mm, and the compaction pressure is 0.15-0.2MPa; then put the cylinder into a sintering furnace Medium sintering, the sintering temperature is 1150°C, and the sintering holding time is 1 hour; after the sintering is completed, quickly put the cylinder into the liquid nitrogen upper space in the liquid nitrogen pool at -120°C, and the cylinder is automatically broken into 1-5mm particles. Then the particles are kept warm for 10 minutes, taken out and ground to obtain a composite rare earth oxide powder with a particle size of 150-200 microns;

[0024] (2) Preparation of composite material mixture

[0025] Take 5% of compo...

Embodiment 2

[0029] The environmental protection rubber sound insulation material of the present invention, its preparation method is as follows:

[0030] (1) Preparation of composite rare earth oxides

[0031] Mix neodymium oxide, alumina and silicon oxide powders evenly, then put them into a mold and compact them into a cylinder with a diameter of 13mm and a height of 17mm, and the compaction pressure is 0.15-0.2MPa; then put the cylinder into a sintering furnace Medium sintering, the sintering temperature is 1170°C, and the sintering holding time is 1.5 hours; after the sintering is completed, quickly put the cylinder into the liquid nitrogen upper space in the liquid nitrogen pool at -140°C, and the cylinder is automatically broken into 1-5mm particles. Then the particles are kept warm for 15 minutes, taken out and ground to obtain a composite rare earth oxide powder with a particle size of 150-200 microns;

[0032] (2) Preparation of composite material mixture

[0033] Take 10% of c...

Embodiment 3

[0037] The environmental protection rubber sound insulation material of the present invention, its preparation method is as follows:

[0038] (1) Preparation of composite rare earth oxides

[0039] Mix neodymium oxide, alumina and silicon oxide powders evenly, then put them into a mold and compact them into a cylinder with a diameter of 15mm and a height of 20mm, and the compaction pressure is 0.15-0.2MPa; then put the cylinder into a sintering furnace Medium sintering, the sintering temperature is 1180°C, and the sintering holding time is 2 hours; after the sintering is completed, quickly put the cylinder into the liquid nitrogen upper space in the liquid nitrogen pool at -150°C, and the cylinder is automatically broken into 1-5mm particles. Then the particles are kept warm for 20 minutes, taken out and ground to obtain a composite rare earth oxide powder with a particle size of 150-200 microns;

[0040] (2) Preparation of composite material mixture

[0041] Take 15% of com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of functional materials, and particularly relates to an environment-friendly rubber sound-insulation material and a preparation method thereof. The material comprises the following components in percentage by weight: 1-3% of dibenzoyl peroxide, 1-3% of silicon oxide, 5-15% of recovered epoxy resin, 5-15% of composite rare-earth oxide and the balance of silicon rubber. No abundant rare materials are used in the preparation process, so the raw material cost is lowered; and the wastes are used as the raw materials, so the material preparation method is convenient in technique and simple in process. The prepared material can effectively absorb energies, can be used in the fields of transportations, architecture, military affairs and the like, has the functions of shock resistance, impact buffering, heat insulation, sound insulation and the like, and is especially suitable to be used as a saloon car damping fin.

Description

technical field [0001] The invention belongs to the field of functional materials, and in particular relates to an environment-friendly rubber sound-insulating material and a preparation method thereof. Background technique [0002] CN201310244786.7 provides lightweight asphalt damping film for automobiles and a preparation method thereof. The damping film is prepared by blending petroleum asphalt, SBS, warm-mix asphalt modifier, aromatic oil, light heat-insulating and sound-absorbing materials, and inorganic fillers. 180-200 parts of 10# asphalt resin, 0-20 parts of 30# asphalt resin, 5 parts of SBS elastomer, 5-7 parts of warm mix asphalt modifier, 90-100 parts of aromatic oil, 90 parts of attapulgite, hollow glass 10 parts of microbeads, 60-80 parts of Shuangfei powder, 90-100 parts of light calcium carbonate. Applicable to the bottom of the car body, it has the advantages of light weight, shock absorption and good heat insulation and sound absorption. The damping coef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L63/00C08K3/00C08K3/34C08K3/22C08J3/24
CPCY02A30/30
Inventor 赵浩峰王玲张太忠徐小雪雷霆潘子云宋超郑泽昌王冰曹燕子谢艳春龚国庆何晓蕾赵佳玉柯维雄陆阳平裴李娜赵圣哲
Owner 江苏金泰祥内外门业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap