Preparation process of rubber material for seal ring of automobile

A technology of rubber material and preparation process, which is applied in the field of rubber materials for automobile sealing rings, can solve the problems of not being able to meet the increasingly high requirements of automobile sealing, and achieve the improvement of rubber processing performance, good process performance and superior oxidation resistance. Effect

Inactive Publication Date: 2015-01-14
安徽宁国尚鼎橡塑制品有限公司
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Sealing ring sealing is an important form of automobile static sealing. There are 100-400 sealing rings used in automobiles. The modern automobile industry has put forward higher and higher requirements for seals. These sealing rings can seal the liquid inside the car. With the role of gas and to prevent the intrusion of external rain and dust, all kinds of rubber sealing rings used in au

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of rubber material for seal ring of automobile
  • Preparation process of rubber material for seal ring of automobile
  • Preparation process of rubber material for seal ring of automobile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] like figure 1 as shown, figure 1 It is a flow chart of the preparation process of rubber material for automobile sealing ring proposed by the present invention.

[0019] refer to figure 1 , a rubber material for automobile sealing rings, the preparation process of which is:

[0020] S1. First, 100 parts of natural rubber, 35 parts of styrene-butadiene rubber, 1.1 parts of anti-aging agent RD, 0.6 parts of anti-aging agent SP, 1.3 parts of stearic acid, 2 parts of palm wax, and 3 parts of active agent magnesium oxide will be prepared by weight. , 1 part of acid-base balance agent PEG4001, 4 parts of zinc oxide, 0.8 part of compound paraffin, 3 parts of flame retardant tetrachlorophthalic anhydride, 4 parts of alkyl phenolic resin, 3.2 parts of rubber plasticizer cashew nut shell oil The mixing machine is mixed completely to obtain the mixed rubber, and the first mixing temperature is 85°C;

[0021] S2, then mix the obtained mixed rubber with 40 parts of high cis-1,4-...

Embodiment 2

[0025] A kind of automobile sealing ring rubber material, its preparation process is:

[0026] S1. First, 100 parts of natural rubber, 50 parts of styrene-butadiene rubber, 0.7 part of antioxidant RD, 1 part of antioxidant SP, 0.8 part of stearic acid, 2.5 parts of palm wax, 1 part of active agent magnesium oxide, and 3 parts of alkali balance agent PEG4003, 2 parts of zinc oxide, 1.3 parts of compound paraffin, 1.5 parts of flame retardant tetrachlorophthalic anhydride, 5 parts of alkyl phenolic resin, and 2.5 parts of rubber plasticizer cashew nut shell oil are put into the internal mixer The mixed rubber is completely obtained by mixing, and the first mixing temperature is 93°C;

[0027] S2, then mix the obtained mixed rubber with 30 parts of high cis-1,4-polybutadiene rubber, 30 parts of carbon black N55030, 15 parts of carbon black N3301, 13 parts of nano silicon dioxide, and 967 parts of silane coupling agent , 16 parts of epoxidized soybean oil are put into open mill m...

Embodiment 3

[0031] A kind of automobile sealing ring rubber material, its preparation process is:

[0032] S1. First, 100 parts of natural rubber, 42 parts of styrene-butadiene rubber, 0.85 parts of anti-aging agent RD, 0.75 parts of anti-aging agent SP, 1.25 parts of stearic acid, 2.2 parts of palm wax, and 1.5 parts of active agent magnesium oxide will be prepared by weight. , 2.5 parts of acid-base balance agent PEG400, 2.3 parts of zinc oxide, 1.25 parts of compound paraffin, 2.5 parts of flame retardant tetrachlorophthalic anhydride, 4.5 parts of alkyl phenolic resin, 3.15 parts of rubber plasticizer cashew nut shell oil Put it into the internal mixer and mix completely to obtain the rubber compound, and the first mixing temperature is 92°C;

[0033] S2. Then mix the obtained mixed rubber with 38 parts of high cis-1,4-polybutadiene rubber, 28 parts of carbon black N55028 parts, 23 parts of carbon black N3302, 12 parts of nano-silica, and 967 parts of silane coupling agent 14 parts b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of a rubber material for a seal ring of an automobile. The preparation process comprises the following steps: placing natural rubber, styrene-butadiene rubber, an anti-aging agent RD, an anti-aging agent SP, stearic acid, carnauba wax, an active agent magnesium oxide, an acid-base balancing agent PEG400, zinc oxide, composite paraffin, a flame retardant tetrachlorophthalic anhydride, alkyl phenolic resin, a rubber plasticizer cashew nut oil into an internal mixer and completely mixing to obtain mixed rubber; then placing mixed rubber, high cis-1,4-polybutadiene rubber, carbon black N550, carbon black N330, nano-silica, a silane coupling agent SI-96 and epoxy soybean oil in parts by weight into an open mill and completely mixing; and then adding dicumyl peroxide, an accelerator TETD, and an accelerator DM and completely mixing, processing and molding the obtained material, sending to a vulcanizing machine for vulcanizing to obtain the rubber material for the seal ring of the automobile. The product prepared from the rubber material disclosed by the invention has the advantages of heat resistance, aging resistance, good weather resistance, high hardness, good tear resistance performance, low cost, good processing performance.

Description

technical field [0001] The invention relates to the technical field of rubber materials for automobile sealing rings, in particular to a preparation process of rubber materials for automobile sealing rings. Background technique [0002] Sealing ring sealing is an important form of automobile static sealing. There are 100-400 sealing rings used in automobiles. The modern automobile industry has put forward higher and higher requirements for seals. These sealing rings can seal the liquid inside the car. With the role of gas and to prevent the intrusion of external rain and dust, all kinds of rubber sealing rings used in automobiles have the functions of high temperature resistance, weather resistance and aging resistance during work, and require high hardness and good tear resistance, which is very important for rubber materials and The sealing structure is a severe test; the sealing ring material prepared by using the traditional formula can no longer meet the increasingly hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L9/06C08L9/00C08K13/02C08K5/09C08K3/22C08K3/04C08K3/36C08K5/1515C08K5/14
CPCC08L7/00B29C35/02C08K2201/011C08K2201/014C08L2201/08C08L2205/025C08L2205/035
Inventor 杨存俊
Owner 安徽宁国尚鼎橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap