Antistatic high-luster polypropylene composite material and preparation method thereof

A composite material, polypropylene technology, applied in the field of polymer material modification, can solve the problems of large filling amount, glossiness, shrinkage rate not considered, glossiness mechanical properties not considered, etc., to improve antistatic performance, improve comprehensive Performance and cost-effective, high gloss improved effect

Inactive Publication Date: 2015-01-14
HEFEI GENIUS NEW MATERIALS
View PDF10 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Chinese patent CN101463163B discloses the preparation of a permanent antistatic polypropylene material, but only emphasizes the antistatic effect of polypropylene, and does not consider the gloss, shrinkage, etc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic high-luster polypropylene composite material and preparation method thereof
  • Antistatic high-luster polypropylene composite material and preparation method thereof
  • Antistatic high-luster polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) Preparation of modified filler:

[0045]Put 100 parts of barium sulfate in the high-speed mixer, start the high-speed mixer, and slowly add 2 parts of coupling agent AC-311 through the small hole of the high-speed mixer. The rotation speed of the high-speed mixer is 120 rpm, the temperature of the high-speed mixer is 40° C., the mixing time is 10 minutes, and the coupling agent addition time is 5 minutes.

[0046] (2) Preparation of antistatic, high-gloss polypropylene composite materials:

[0047] 100 parts of polypropylene, 50 parts of acrylonitrile-butadiene-styrene copolymer, 6 parts of polyether block polyamide, 2 parts of glycerol monostearamide, 1 part of ethoxylated amine, 2 parts of PP-g-MAH , 2 parts of ABS-g-MAH, 10 parts of modified fillers, 0.2 parts of anti-1010, 0.4 parts of anti-1076, 0.4 parts of anti-168, 0.3 parts of silicone powder, and 0.2 parts of EBS were added to the high-speed mixer and mixed for 5 minutes, mixed The speed is 120 rpm, and ...

Embodiment 2

[0079] (1) Preparation of modified filler:

[0080] Put 100 parts of barium sulfate in the high-speed mixer, start the high-speed mixer, and slowly add 4 parts of coupling agent AC-311 through the small hole of the top cover of the high-speed mixer. The rotation speed of the high-speed mixer is 200 rpm, the temperature of the high-speed mixer is 60° C., the mixing time is 15 minutes, and the coupling agent addition time is controlled at 10 minutes.

[0081] (2) Preparation of antistatic, high-gloss polypropylene composite materials:

[0082] 100 parts of polypropylene, 100 parts of acrylonitrile-butadiene-styrene copolymer, 27 parts of polyether block polyamide, 2 parts of glycerol monostearamide, 1 part of ethoxylated amine, 5 parts of PP-g-MAH , 5 parts of ABS-g-MAH, 20 parts of modified fillers, 0.4 parts of anti-1010, 0.8 parts of anti-1076, 0.8 parts of anti-168, 0.6 parts of silicone powder, and 0.4 parts of EBS were added to the high-speed mixer and mixed for 10 minute...

Embodiment 3

[0084] (1) Preparation of modified filler:

[0085] Put 100 parts of barium sulfate in the high-speed mixer, start the high-speed mixer, and then slowly add 3 parts of coupling agent AC-311 through the small hole of the top cover of the high-speed mixer. The rotation speed of the high-speed mixer is 180 rpm, the temperature of the high-speed mixer is 50° C., the mixing time is 12 minutes, and the coupling agent addition time is controlled at 8 minutes.

[0086] (2) Preparation of antistatic, high-gloss polypropylene composite materials:

[0087] 100 parts of polypropylene, 80 parts of acrylonitrile-butadiene-styrene copolymer, 15 parts of polyether block polyamide, 10 parts of glycerol monostearamide, 5 parts of ethoxylated amine, 4 parts of PP-g-MAH , 4 parts of ABS-g-MAH, 16 parts of modified fillers, 0.3 parts of anti-1010, 0.6 parts of anti-1076, 0.8 parts of anti-168, 0.5 parts of silicone powder, and 0.3 parts of EBS were added to the high-speed mixer and mixed for 12 min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Screw diameteraaaaaaaaaa
Screw diameteraaaaaaaaaa
Screw diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an antistatic high-luster polypropylene composite material and a preparation method thereof. The composite material is prepared by using 100 parts of polypropylene, 50-100 parts of acrylonitrile-butadiene-styrene copolymer, 9-30 parts of an antistatic agent, 4-10 parts of a compatilizer, 10-20 parts of a modification filler, 1-2 parts of an antioxidant and 0.5-1 part of a processing assistant, wherein the antistatic agent is composed of a permanent high-molecular antistatic agent and a low-molecular antistatic agent; and the compatilizer is a polypropylene grafted maleic anhydride and acrylonitrile-butadiene-styrene copolymer grafted maleic anhydride mixture. The preparation method improves the antistatic performance, the comprehensive performances and the cost performance of the polypropylene composite material, so the composite material has the characteristics of permanent antistatic performance, high luster and workability, and can be widely used in the field of electronic apparatuses, the field of household electrical appliances, the fields of aviation and aerospace, the national defense field and the like.

Description

[0001] technical field [0002] The invention relates to the field of polymer material modification, in particular to the preparation and method of an antistatic and high-gloss polypropylene composite material. [0003] Background technique [0004] Plastics are used more and more widely, and polypropylene (PP) as a general-purpose plastic has attracted more and more attention, and its application range has also been greatly expanded. However, in some fields due to the high shrinkage rate of polypropylene (1.4~1.6%), large surface resistivity (10 16 ~10 18 Ω), poor gloss and other shortcomings, making pure polypropylene not widely used. With the development of science and technology, a single plastic can no longer meet the needs of social development in some fields. In recent years, plastic alloys and their modifications have been widely used, and the modified polypropylene has a wide range of applications. At present, the method of reducing the shrinkage of polypropyle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L55/02C08L51/06C08L51/00C08L77/00C08K13/06C08K9/04C08K3/30C08K5/20C08K5/17B29C47/92B29C48/92
CPCC08L23/12B29C48/92B29C2948/92704C08K2201/003C08K2201/014C08K2201/017C08L2201/04C08L2205/025C08L2205/035C08L2205/08C08L55/02C08L51/06C08L77/00C08L83/04C08K13/06C08K9/04C08K2003/3045C08K5/17C08K5/20C08K5/1345C08K5/526
Inventor 杨桂生俞飞
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap