Technical formula of black chemical oxidation of stainless steel
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of chemical oxidation and process formula, which is applied in the field of black chemical oxidation of stainless steel, can solve problems such as difficulty in satisfying neutral salt spray test, difficulty in color control, and easy volatilization of the solution, and achieves fast film forming speed, thick film layer, and environmental protection. The effect of less pollution
Inactive Publication Date: 2015-02-18
GUIZHOU HANGRUI AVIATION PRECISION PARTS MFG
View PDF4 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0010] The present invention aims to solve the problems in the prior art that the temperature of the bath solution is high, the solution is volatile, the color control is diffic
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] Stainless steel black chemical oxidation process formula:
[0023] Sodium hydroxide (g / L) 450
[0024] Sodium chloride (g / L) 8
[0025] Sodium thiosulfate (g / L) 45
[0026] Sodium thiocyanate (g / L) 90
[0027] Potassium permanganate (g / L) 2
[0028] Ammonium molybdate (g / L) 5
[0029] Temperature (°C) 90
[0030] Time (min) 3.
Embodiment 2
[0032] Stainless steel black chemical oxidation process formula:
[0033] Sodium hydroxide (g / L) 500
[0034] Sodium chloride (g / L) 12
[0035] Sodium thiosulfate (g / L) 50
[0036] Sodium thiocyanate (g / L) 100
[0037] Potassium permanganate (g / L) 3
[0038] Ammonium molybdate (g / L) 6
[0039] Temperature (°C) 100
[0040] Time (min) 4.
Embodiment 3
[0042] Stainless steel black chemical oxidation process formula:
[0043] Sodium hydroxide (g / L) 550
[0044] Sodium chloride (g / L) 15
[0045] Sodium thiosulfate (g / L) 55
[0046] Sodium thiocyanate (g / L) 110
[0047] Potassium permanganate (g / L) 5
[0048] Ammonium molybdate (g / L) 8
[0049] Temperature (°C) 110
[0050] Time (min) 2.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a technical formula of black chemical oxidation of a stainless steel. The technical formula comprises the following components in terms of g/L: 450-550 of sodium hydroxide, 8-15 of sodium chloride, 45-55 of sodium thiosulfate, 90-110 of sodium thiocyanate, 2-5 of potassium permanganate and 5-8 of ammonium molybdate. The technical formula has the advantages of wide temperature range, high film-forming speed and short oxidation time, wide color, good film layer property and high efficiency, the color is easily controlled and the film does not fade; after potassium permanganate and ammonium molybdate are added, the film layer is thick and has good brightness and the neutral salt spray test in 96 hours can be ensured; and since no pollutants such as chromic anhydride are added, the less environmental pollution is caused.
Description
technical field [0001] The invention relates to a technological formula for black chemical oxidation of stainless steel, mainly aimed at the black chemical oxidation of stainless steel. Background technique [0002] Stainless steel is widely used in aviation, aerospace, shipbuilding, electronics and other industries due to its excellent properties such as corrosion resistance, wear resistance, high mechanical strength, hardness and easy processing. Stainless steel fasteners used in aviation, electronics and other industries need to be black oxidized in order to extinction, increase corrosion resistance and aesthetics; stainless steel oxidation methods include electrolytic oxidation and chemical oxidation, etc., due to stainless steel fastening There are many specifications, small sizes, large quantities, and high requirements. Electrolytic anodizing is not suitable for batch processing of fasteners, and the oxidation process is unstable and difficult to control. Therefore, c...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): C23C22/62
CPCC23C22/62
Inventor 吴育照王治刚
Owner GUIZHOU HANGRUI AVIATION PRECISION PARTS MFG
Login to view more 
Login to view more