A manufacturing method and mixing system technology, applied in the direction of mixing methods, mixers, fluid mixers, etc., can solve the problems of coating voids, difficulty, poor dispersion and solubility, etc., to reduce the mixing of air bubbles and simplify degassing Process effect

Inactive Publication Date: 2015-02-25
NIHON SPINDLE MFG CO LTD +1
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, although solid components such as positive electrode active materials or negative electrode active materials, conductive materials, and binders, and solvents such as water are put into such as Figure 9 The dispersion and mixing of solid components (including the dissolution of soluble solid components) are carried out in the batch multi-shaft mixer shown to obtain the above slurry. However, when carbon used as a conductive substance, especially the aspect ratio In the case of fibrous toner with a large (length/diameter), or a substance with poor di

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dispersing mixer system used in producing slurry containing carbon and producing method of slurry containing carbon
  • Dispersing mixer system used in producing slurry containing carbon and producing method of slurry containing carbon
  • Dispersing mixer system used in producing slurry containing carbon and producing method of slurry containing carbon

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0192] [Example 1]

[0193] (High rate discharge test)

[0194] Table 1 shows that LiFePO was used as the slurry material used in the production of electrodes for non-aqueous electrolyte secondary batteries, that is, a material that adsorbs and releases alkali metal ions. 4 (91wt%), carbon (carbon black (2wt%), carbon (carbon nanotubes) (2wt%) with an aspect ratio of 10 to 1000 fibrous carbon powder and an average fiber diameter of 1 to 500 nm) and water-based binder (CMC (carboxymethyl cellulose) (5 wt%)) (solid content ratio: 31 wt%), using water as the solvent R, and using the dispersion mixing system 100 equipped with the dispersion mixing pump Y to produce a slurry.

[0195] In addition, Figure 10(a) and Figure 10(b) show electron micrographs of the electrode surface and electrode cross section coated with carbon-containing paste (Figure 10(a) is based on a conventional batch-type multi-axis mixer Figure 10(b) is a photo of the method of manufacturing carbon-containing paste ba...

Example Embodiment

[0203] [Example 2]

[0204] (High rate discharge test)

[0205] Table 2 shows that LiFePO was used as the slurry material used in the production of electrodes for non-aqueous electrolyte secondary batteries, that is, a material that adsorbs and releases alkali metal ions. 4 (89wt%), carbon (carbon black (1.5wt%), fibrous carbon powder with an aspect ratio of 10 to 500, carbon nanotubes with an average fiber diameter of 150nm (1.5wt%), activated carbon (3wt%) ) And an aqueous binder (acrylate (5 wt%)) (solid content ratio: 37 wt%), water was used as the solvent R, and the dispersion mixing system 100 equipped with the dispersion mixing pump Y described above was used to produce a slurry.

[0206] The test electrode (positive electrode) coated the obtained slurry on an aluminum foil with a thickness of 20 μm and dried, then the aluminum foil and the coating film were adhered and bonded by a roll press, and then heated (in a reduced pressure state, 150 ℃ for more than 12 hours) to obta...

Example Embodiment

[0224] [Example 3]

[0225] Table 3 shows that as the slurry material used in the production of the electrode for the non-aqueous electrolyte secondary battery, that is, the material that adsorbs and releases alkali metal ions, LiMn is used 0.33 Ni 0.33 Co 0.33 O 2 (91wt%), carbon (carbon black (2wt%), fibrous carbon powder with an aspect ratio of 10 to 500, carbon (carbon nanotubes) (2wt%) with an average fiber diameter of 150nm) and water-based binder (acrylic acid) Ester (5wt%)) (solid content ratio: 32wt%), water was used as the solvent R, and the dispersion mixing system 100 equipped with the dispersion mixing pump Y described above was used to produce a slurry.

[0226] [table 3]

[0227]

[0228] The test electrode (positive electrode) coated the obtained slurry on an aluminum foil with a thickness of 20 μm and dried, then the aluminum foil and the coating film were adhered and bonded by a roll press, and then heated (in a reduced pressure state, 150 ℃ for more than 12 hours)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average fiber diameteraaaaaaaaaa
Capacity densityaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a dispersing mixer system equipped with a dispersing mixer pump used in producing slurry containing carbon and producing method of slurry containing carbon. The dispersing mixer system is provided with the following dispersing mixer pump that: a rotator of a rotation wing is eccentrically arranged in a cylindrical housing body, and by rotating and driving the rotator, solid ingredient and solvent are absorbed to a first guide-in chamber formed in the cylindrical housing body via a first supplying part; by using the rotation wing to stir, the solid ingredient and the solvent are spitted out from a spitting chamber via a discharging chamber; liquid spitted from the spitting part is circulated to a second supplying part via a circulation flow path; the liquid is absorbed to a second guide-in chamber formed by being separated from the first guide-in chamber via a separator plate from the second supplying part towards the interior of the cylindrical housing body; the liquid is allowed to pass a throttle flow path formed on a stator, after being stirred by the rotation wing, and is spitted out from the spitting part from the discharging chamber; and then the liquid spitted out from the spitting part is circulated to the a second supplying part via the circulation flow path.

Description

[0001] This application claims priority based on Japanese Patent Application No. 2013-167307 filed on August 12, 2013. The entire content of this application is incorporated in this specification by reference. technical field [0002] The present invention relates to a kind of dispersion mixing system and the manufacturing method of carbonaceous slurry that are equipped with the dispersing mixing pump that is used to manufacture carbonaceous slurry, particularly relate to a kind of equipment that is used in the manufacture of the electrode that contains in non-aqueous electrolyte secondary battery. A dispersive mixing system of a dispersive mixing pump for a carbon slurry used in the invention and a method for manufacturing a carbon-containing slurry. Background technique [0003] In the past, as non-aqueous electrolyte secondary batteries, lithium-ion secondary batteries have been widely used in various electronic devices such as personal computers and mobile devices. Howev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01F13/10B01F15/02B01F3/12H01M4/62H01M10/05B01F25/60
CPCY02E60/10H01M4/139H01M10/0525
Inventor 别惣俊二浅见圭一
Owner NIHON SPINDLE MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap