Tile paint

A technology for ceramic tiles and quartz sand, applied in the field of tile paint, can solve the problems of poor leveling performance, easy peeling, and large amount of emulsion, and achieve the effects of strong adhesion, no aging, and good ductility.

Inactive Publication Date: 2015-02-25
赵明贵
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the advancement of science and technology and the improvement of people's living standards, people have higher and higher requirements for coatings. Traditional resin coatings and coatings with solvents as diluents are becoming less and less popular, while energy-saving and pollution-free environmental protection paints are more and more popular. People favor the acrylic water latex paint developed in the 1960s because of its reduced environmental pollution, no fire hazard, fast curing of the paint film, simple construction methods, excellent gloss retention, many varieties of designs and colors, and good decorative effects. characteristics, so the field of application is becoming more and more common. It mainly consists of emulsions, pigments and additives. The various acrylic water-emulsion paints currently produced have the following defects because of their ingredients and other aspects. The leveling performance is poor, and a large number of holes will be left after the film is painted, which will affect the smoothness of the painted surface, resulting in poor anti-fouling ability, and the second is that the amount of emulsion is large, resulting in high overall cost
The third is that the existing latex paint is attached to the bottom surface of the putty and is easy to peel off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Embodiment 1, a kind of tile paint, it is made up of following components by weight: 200 parts of quartz sand, 20 parts of deionized water, 80 parts of styrene-acrylic emulsion, 0.2 part of hydroxyethyl cellulose HEC, 4 parts of titanium dioxide , 0.8 parts of thickener, 5 parts of ethylene glycol, 0.2 parts of silicone defoamer, 6 parts of alcohol ester twelve, 0.8 parts of benzoic acid preservative.

Embodiment 2

[0008] Embodiment 2, a kind of tile paint, it is made up of following components by weight: 250 parts of quartz sand, 60 parts of deionized water, 90 parts of styrene-acrylic emulsion, 0.6 part of hydroxyethyl cellulose HEC, 12 parts of titanium dioxide , 1.4 parts of thickener, 10 parts of ethylene glycol, 0.6 parts of silicone defoamer, 10 parts of alcohol ester twelve, 1.2 parts of benzoic acid preservative.

Embodiment 3

[0009] Embodiment 3, a kind of ceramic tile paint, it is made up of the following components by weight: 300 parts of quartz sand, 100 parts of deionized water, 100 parts of styrene-acrylic emulsion, 1 part of hydroxyethyl cellulose HEC, 20 parts of titanium dioxide, 2 parts of thickener, 15 parts of ethylene glycol, 1 part of silicone defoamer, 15 parts of alcohol ester twelve, 1.5 parts of benzoic acid preservative.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of chemical materials, and specifically relates to a tile paint. The tile paint is composed of the following components in parts by weight: 200 to 300 parts of quartz sand, 20 to 100 parts of deionized water, 80 to 100 parts of styrene-acrylic emulsion, 0.2 to 1 part of hydroxyethyl cellulose HEC, 4 to 20 parts of titanium dioxide, 0.8 to 2 parts of thickening agent, 5 to 15 parts of glycol, 0.2 to 1 part of organic silicon defoaming agent, 6 to 15 parts of alcohol ester-12, and 0.8 to 1.5 parts of benzoic acid antiseptic. The invention aims to provide a tile paint with an ideal performance.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to a tile paint. Background technique [0002] Wall bricks are a popular building decoration material at the end of the last century, but with the increase of the service life, problems gradually appear, such as the consumption of non-renewable resources such as soil and coal in the production process, the cost is relatively high, and the weight is relatively large. The load-bearing capacity of the insulation material is high, which increases the cost of the insulation system. When it falls off, there is a big safety hazard, it is not easy to maintain, and it affects the appearance. In order to avoid the occurrence of the above problems without giving up the aesthetic effect of wall tiles, the paint industry has begun to develop new products, eager to achieve the same decorative aesthetic effect as wall tiles on the premise of reducing costs and having no potential safety...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/04
CPCC04B26/285
Inventor 赵明贵
Owner 赵明贵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products