Glass-fiber-reinforced PET/ABS composite material and preparation method thereof

A composite material and glass fiber technology, which is applied in the field of glass fiber reinforced PET/ABS composite material and its preparation, can solve the problems of poor compatibilizer and low glow wire temperature, achieve excellent comprehensive performance, and increase the glow wire temperature value , good compatibility effect

Inactive Publication Date: 2015-03-18
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, blending PET and ABS can produce PET / ABS materials with excellent performance, but the compatibilizer of PET and ABS is not good, and the glow wire temperature (GWIT) value of PET / ABS composite system is not high. Well suited for demanding electrical environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A glass fiber-reinforced PET / ABS composite material, whose components are proportioned by mass percentage: 20% PET, 48% ABS, 25% alkali-free glass fiber whose surface has been treated with a silane coupling agent, maleic anhydride grafted Acrylonitrile-styrene copolymer (AS-g-MAH) 5%, EVA wax 1%, compound of polybasic hindered phenol antioxidant 1076 and phosphite antioxidant 168 0.6%, 2-hydroxy-4 - Methylbenzophenone 0.4%. Wherein, the PET is polyethylene terephthalate, and its relative density is 1.35~1.38 g / cm 3 , a melting point of 255° C. to 260° C., and an intrinsic viscosity of 0.9 to 1.1 dL / g; the ABS is an acrylonitrile-butadiene-styrene terpolymer.

[0021] Preparation method: (1) Dry PET at 120°C-130°C for 4-6 hours, control the moisture content below 0.03%, and wait for use; (2) Dry ABS at 80°C-90°C for 2-4 hours, Stand-by; (3) Weigh each component according to the weight ratio, and then add it to a high-speed mixer and mix it thoroughly for 5-15 minutes t...

Embodiment 2

[0023] A glass fiber-reinforced PET / ABS composite material, the components of which are: 37% PET, 37% ABS, 15% alkali-free glass fiber whose surface has been treated with a silane coupling agent, maleic anhydride grafted Styrene-ethylene-butadiene copolymer (SEBS-g-MAH) 8%, TAS-2A 1.5%, multi-component hindered phenol antioxidant 1076 and phosphite antioxidant 168 compound 1%, 2 -Hydroxy-4-methylbenzophenone 0.5%. Wherein, the PET is polyethylene terephthalate, and its relative density is 1.35~1.38 g / cm 3 , a melting point of 255° C. to 260° C., and an intrinsic viscosity of 0.9 to 1.1 dL / g; the ABS is an acrylonitrile-butadiene-styrene terpolymer.

[0024] Preparation method: (1) Dry PET at 120°C-130°C for 4-6 hours, control the moisture content below 0.03%, and wait for use; (2) Dry ABS at 80°C-90°C for 2-4 hours, Stand-by; (3) Weigh each component according to the weight ratio, and then add it to a high-speed mixer and mix it thoroughly for 5-15 minutes to make it evenly ...

Embodiment 3

[0026] A glass fiber-reinforced PET / ABS composite material, the components of which are: 50% PET, 24% ABS, 20% alkali-free glass fiber whose surface has been treated with a silane coupling agent, methyl methacrylate -Compound of 4% glycidyl methacrylate-propylene ethyl ester terpolymer (MGE), 1% ethylene bis stearamide, multi-component hindered phenol antioxidant 1076 and phosphite antioxidant 168 0.8 %, 2-hydroxy-4-methylbenzophenone 0.2%. Wherein, the PET is polyethylene terephthalate, and its relative density is 1.35~1.38 g / cm 3 , a melting point of 255° C. to 260° C., and an intrinsic viscosity of 0.9 to 1.1 dL / g; the ABS is an acrylonitrile-butadiene-styrene terpolymer.

[0027] Preparation method: (1) Dry PET at 120°C-130°C for 4-6 hours, control the moisture content below 0.03%, and wait for use; (2) Dry ABS at 80°C-90°C for 2-4 hours, Stand-by; (3) Weigh each component according to the weight ratio, and then add it to a high-speed mixer and mix it thoroughly for 5-15...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass-fiber-reinforced PET / ABS composite material and a preparation method thereof. The glass-fiber-reinforced PET / ABS composite material comprises the following components in percentage by mass: 20%-50% of PET, 20%-50% of ABS, 15%-30% of glass fiber, 3%-8% of a compatibilizer, 0.5%-2% of a lubricant, 0.1%-1% of an antioxidant and 0.1-1% of a light stabilizer. The PET / ABS composite material prepared by the preparation method has the beneficial effects of good compatibility, strong aging resistance, good processing flowability, high notched impact strength, good elongation at break and heat resistance and excellent comprehensive properties, particularly excellent mechanical properties; by adding the glass fiber, the strength of the material is not only further increased and the temperature value of the glow wire of the material is also significantly increased.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a glass fiber reinforced PET / ABS composite material and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) was widely used in the 1960s due to its low price and excellent wear resistance, heat resistance, chemical resistance, electrical insulation, molding dimensional stability and high mechanical strength. S is widely used as an engineering plastic. However, PET has disadvantages such as slow crystallization speed, difficult molding process, high mold temperature, long molding cycle, poor impact strength, and high water absorption, which limit its application. ABS (acrylonitrile-butadiene-styrene copolymer) is currently the plastic with the largest output and the most widely used, and the price is relatively cheap. ABS not only has the mechanical properties of toughness, hardness, and rigid phase balance, but also has good siz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L55/02C08K13/06C08K9/06C08K7/14C08J5/08B29B9/06
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap