Spinning finish for asphalt carbon fiber

A pitch carbon fiber and spinning technology, which is applied in carbon fiber, fiber treatment, textiles and papermaking, etc., can solve problems such as melting and merging, and achieve the effects of avoiding defects, good toughness, and good antistatic properties

Inactive Publication Date: 2015-03-25
SICHUAN CHUANGYUE CARBON MATERIAL
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the technical problem that the existing pitch-based carbon fiber spinning oil will

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] An oil for pitch carbon fiber spinning in this embodiment is composed of graphite powder with a particle size of 0.001 μm-2 μm, polyether modified silicone oil, amino modified silicone oil, epoxy modified silicone oil, alkyl alcohol amide, The raw materials of alkyl dimethyl hydroxyethyl quaternary ammonium salt, cohesive agent, octanol polyether, amine ether fiber splitting agent and deionized water are made by ultrasonic mixing for 0.5 h. The mass percentage of the above raw materials is: the particle size is 0.001μm-2μm graphite powder 5%, polyether modified silicone oil 0.5%, amino modified silicone oil 1.5%, epoxy modified silicone oil 1%, alkyl alcohol amide 0.05%, alkyl dimethyl hydroxyethyl quaternary ammonium Salt 0.05% and octanol 0.02%, the rest is deionized water.

[0016] The modified ammonia mass fraction of the amino-modified silicone oil is 0.001-0.05% calculated by end-blocking ammonia-NH2; the modified amount of the epoxy-modified silico...

Example Embodiment

[0017] Example 2

[0018] An oiling agent for pitch carbon fiber spinning in this embodiment is composed of graphene, amino modified silicone oil, epoxy modified silicone oil, alkyl alcohol amide, alkyl dimethyl hydroxyethyl quaternary ammonium salt, and cohesive agent The raw materials of octanol polyether, amine ether fiber splitting agent and deionized water are made by ultrasonic mixing for 3 hours. The mass percentages of the above raw materials are: graphene 45%, amino modified silicone oil 3.5%, epoxy modified silicone oil 2.5 %, 2% of alkyl alcohol amide, 1% of alkyl dimethyl hydroxyethyl quaternary ammonium salt, 0.3% of cohesive agent, 2% of octanol polyether and 0.2% of amine ether fiber splitting agent, and the rest is deionized water. The particle size of the graphene is 0.001 μm-2 μm.

[0019] The modified ammonia mass fraction of the amino-modified silicone oil is 0.001-0.05% calculated by end-blocking ammonia-NH2; the modified amount of the epoxy-modified silicone ...

Example Embodiment

[0020] Example 3

[0021] An oiling agent for pitch carbon fiber spinning in this embodiment is composed of graphite powder with a particle size of 0.001 μm-2 μm, polyether modified silicone oil, amino modified silicone oil, epoxy modified silicone oil, and fatty alcohol polyoxyethylene. The raw materials of ether, alkyl dimethyl hydroxyethyl quaternary ammonium salt, cohesive agent, octanol polyether, amine ether fiber splitting agent and deionized water are made by ultrasonic mixing for 1 hour. The mass percentage of the above raw materials is: particle size 0.001μm-2μm graphite powder 20%, polyether modified silicone oil 2%, amino modified silicone oil 2%, epoxy modified silicone oil 1%, fatty alcohol polyoxyethylene ether 1%, alkyl dimethyl glycol 1% base quaternary ammonium salt, 0.2% cohesive agent, 1% octanol polyether and 0.1% amine ether fiber splitting agent, and the rest is deionized water.

[0022] The modified ammonia mass fraction of the amino-modified silicone oil i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of spinning auxiliary for an asphalt-based carbon fiber precursor fiber, and particularly relates to a spinning finish for an asphalt carbon fiber, and the spinning finish is mainly used for solving the problems that the existing spinning finish for asphalt-based carbon fiber can be molten when used for spinning a large bundle of asphalt-based carbon fibers. According to the technical scheme, the spinning finish for asphalt carbon fiber is prepared by performing ultrasonic mixing on the following raw materials in percentage by weight for 0.5h-3h: 5%-45% of carbon powder, 3%-6% of silicone oil, 0.1%-3% of antistatic agent, 0-0.3% of cohesive agent, 0.02%-2% of wetting agent, 0-0.2% of fiber splitting agent and the balance of deionized water. The spinning finish has the following advantages that the melting phenomenon in a process of spinning a large bundle of asphalt-based carbon fibers cannot exist, the friction and wear of fiber surface and a roller during production can be prevented, and the spinning finish has good antistatic property and toughness effect.

Description

technical field [0001] The invention belongs to the technical field of auxiliary agents for spinning pitch-based carbon fiber precursor fibers, and in particular relates to an oil agent for spinning pitch carbon fibers. Background technique [0002] Oil agent is an important auxiliary agent for the production of high-performance raw silk and carbon fiber. The manufacture of carbon fiber (especially the manufacture of high-performance carbon fiber) has strict requirements on spinning oil agent: such as excellent high temperature resistance to ensure High-temperature pre-oxidation and early carbonization can not only bundle but also prevent the adhesion of the precursor; excellent antistatic performance, to endow the precursor with good bundle and processability, and ensure the smooth progress of the spinning and pre-oxidation process; excellent Excellent lubricity and anti-adhesive isolation, in order to prevent monofilament adhesion in the initial stage of spinning, pre-oxid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M11/74D06M15/643D06M15/65D06M15/647D06M15/53D06M13/463D06M13/224D06M101/40
Inventor 白峰康秀珍伍孝
Owner SICHUAN CHUANGYUE CARBON MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap