A kind of preparation method of coaxial cable
A coaxial cable and inner conductor technology, applied in the manufacture of coaxial cables, cable/conductor manufacturing, circuits, etc. The problem of large bending flexibility of the shaft cable, etc., can reduce the bending flexibility, the signal shielding effect is good, and the structure ratio is reasonable.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] The preparation method of a coaxial cable, the coaxial cable includes an internal conductor, the external conductor has an insulating layer, which includes the rubber layer and the foam layer.The exterior of the shielding layer has an outer sleeve. The preparation method includes the following steps:
[0021] (1) Take anaerobic copper core as an internal conductor. After the middle school is directly installed in the school, the diameter is 3mm in the pull -up mold. After cleaning with acetone and ion water, the surface is used to blow dry the surface with nitrogen.After heating and melting in the reaction kettle, spray it with a high -pressure spray gun evenly to the surface of anaerobic copper core, and the thickness of the silver layer is 0.05mm;
[0022] (2) The inner conductor is set on the inner steel core, and the fluorine rubber is heated to the melting. After the squeezing machine is fixed on the outer layer of the inner conductor by injection molding, it is made i...
Embodiment 2
[0028] Example 2: The rest are the same as the embodiment 1. The difference is that in steps (1), the diameter of the anaerobic copper core is 0.2mm, and the thickness of the silver plating layer is 0.005mm.The thickness of 0.3mm, in step (3), the ratio of polyethylene and nucleus is 2: 0.2, the mixed stirring temperature is 200 ° C, the thickness of the foam layer is 1mm, and the temperature of the three -step cooling temperature in the step (4), the three -step cooling temperature of the three -step cooling temperatureThey are 48 ° C, 35 ° C, 20 ° C, steps (6), 30WT%of aluminum hydroxide, 12WT%of magnesium hydroxide, ethylene-acetate ethylene cocoa 30WT%, linear low-density polyethylene 15WT%, ethylene-acetate-acetate-acetate-acetate-acetate-acetate-acetate-acetic acidEthylene is 10WT%, 0.8WT%of trigestylthoxyate, ethylene-based (β-methoxyyl oxygen) Silicane 1WT%, and zinc 1.2WT%.
Embodiment 3
[0029] Example 3: The rest are the same as the embodiment 1. The difference is that the diameter of the anaerobic copper core is 2mm and the thickness of the silver plating layer is 0.03mm. In step (3)2: 0.05, the mixing temperature is 250 ° C, the thickness of the foam layer is 0.5mm, and in step (4), the temperature of the three -step cooling of three steps is 50 ° C, 40 ° C, 30 ° C, and the 1 layer in step (5).As a shielding layer, in steps (6), ethylene is 5WT%.
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com