Method for preparing low-temperature-resisting waterproof mortar

A technology of waterproof mortar and low temperature resistance, applied in the field of building materials, can solve the problem of low temperature resistance of waterproof mortar and achieve the effect of improving cold resistance

Inactive Publication Date: 2015-04-22
利水工程咨询有限公司 +16
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the invention is to solve the problem of low temperature resistance of waterproof mortar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Step 1. Preparation of cationic prefabricated body: take 20Kg of fatty acid magnesium, heat to 160°C, then add 5Kg of polyimide particles, 10Kg of quartz sand, and 15Kg of diatomaceous earth, stir evenly, and obtain modified powder after cooling; Then add 3Kg of cationic surfactant polyethyleneimine and 30Kg of glycerin, heat up and mix in a mixer, cool to room temperature, and obtain a cationic preform, the temperature for heating up and mixing is 80°C, and the time for heating up and mixing is 20 minutes;

[0022] The 2nd step, the preparation of anionic prefabricated body: get polymethyl acrylate latex powder 20Kg, anionic surfactant polyammonium methacrylate 4Kg, epoxy resin 4Kg, o-hydroxybenzoic acid phenyl ester 4Kg, glass fiber 10Kg, ethyl acetate 15Kg, heating and mixing, after cooling, an anion preform is obtained, the temperature of heating and mixing is 40°C, and the time of heating and mixing is 20 minutes;

[0023] Step 3: Mix the cation preform and the ani...

Embodiment 2

[0027] Step 1. Preparation of cationic prefabricated body: Take 30Kg of magnesium fatty acid, heat to 180°C, then add 10Kg of polyimide particles, 20Kg of quartz sand, and 20Kg of diatomaceous earth, stir evenly, and obtain a modified powder after cooling; Then add 5Kg of cationic surfactant polyethyleneimine and 40Kg of glycerin, heat up and mix in a mixer, cool to room temperature, and obtain a cationic preform, the temperature for heating up and mixing is 110°C, and the time for heating up and mixing is 30 minutes;

[0028] The 2nd step, the preparation of anionic prefabricated body: get polymethyl acrylate latex powder 30Kg, anionic surfactant polyammonium methacrylate 7Kg, epoxy resin 8Kg, phenyl o-hydroxybenzoate 7Kg, glass fiber 20Kg, ethyl acetate 30Kg, heating and mixing, after cooling, an anion preform is obtained, the temperature of heating and mixing is 50°C, and the time of heating and mixing is 30 minutes;

[0029] Step 3: Mix the cation preform and the anion pre...

Embodiment 3

[0033] Step 1. Preparation of cationic preform: Take 25Kg of fatty acid magnesium, heat it to 170°C, then add 7Kg of polyimide particles, 18Kg of quartz sand, and 18Kg of diatomaceous earth, stir evenly, and obtain a modified powder after cooling; Then add 4Kg of cationic surfactant polyethyleneimine and 35Kg of glycerin, heat up and mix in a mixer, cool to room temperature, and obtain a cationic preform, the temperature for heating up and mixing is 90°C, and the time for heating up and mixing is 25 minutes;

[0034] The 2nd step, the preparation of anionic prefabricated body: get polymethyl acrylate latex powder 25Kg, anionic surfactant polyammonium methacrylate 5Kg, epoxy resin 6Kg, o-hydroxybenzoic acid phenyl ester 6Kg, glass fiber 15Kg, ethyl acetate 20Kg, heating and mixing, after cooling, an anion preform is obtained, the temperature of heating and mixing is 45°C, and the time of heating and mixing is 25 minutes;

[0035] Step 3: Mix the cation preform and the anion pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing low-temperature-resisting waterproof mortar. The method comprises the following steps: heating fatty acid magnesium, adding polyimide grains, quartz sand and kieselguhr, unfiromly stirring, and cooling, thereby obtaining modified powder; adding a cationic surfactant and glycerol, heating and mixing in a mixing machine, and cooling to room temperature, thereby obtaining a cationic prefabricated body; heating and mixing polymethyl acrylate latex powder, an anionic surfactant, epoxy resin, o-hydroxybenzoic acid phenyl ester, inorganic fibers and ethyl acetate, and cooling, thereby obtaining an anionic prefabricated body; mixing the cationic prefabricated body and the anionic prefabricated body, drying and carrying out ball milling, thereby obtaining a mixture; and mixing the mixture with water, coal ash, gypsum and cement, thereby obtaining the waterproof mortar. As the inorganic fiber and the inorganic grains are respectively modified by using anions and cations, the inorganic fiber and the inorganic grains can be easily wrapped by each other, and the cold resistance of the mortar with the inorganic fiber and the inorganic grains is improved.

Description

technical field [0001] The invention relates to a preparation method of low-temperature-resistant waterproof mortar, which belongs to the technical field of building materials. Background technique [0002] Waterproof mortar has good weather resistance, durability, impermeability, compactness, high adhesion and strong waterproof and anti-corrosion effect. It can resist the corrosion of soda ash production medium, urea, ammonium nitrate, seawater hydrochloric acid and acid-base salt. It is mixed with ordinary sand cement and special cement to make cement mortar. By mixing the cement mortar, casting or spraying, and manually applying it, a strong waterproof and anti-corrosion mortar layer is formed on the concrete and the surface. It is a rigid, tough, waterproof and anti-corrosion material. Mixing with cement and sand can modify the mortar, which can be used for the treatment of building walls and ground and the waterproof layer of underground engineering. There are thre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B24/28C04B111/27
Inventor 胡运冲
Owner 利水工程咨询有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka