Production method for anti-radiation soybean fiber fabrics

A technology of soybean fiber and production method, applied in protective clothing, fabric surface trimming, weaving and other directions, can solve the problems of low conductivity of carbon fiber, poor fiber spinnability, rust, etc., so as not to break easily, improve production efficiency, and avoid excessive wear and tear Effect

Inactive Publication Date: 2015-04-22
SUZHOU WILDER IND & TRADE
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal fibers are not suitable for close-fitting protective clothing because they itch on human skin and will rust when exposed to sweat; carbon fibers have low electrical conductivity and poor electromagnetic radiation shielding effect; specific copper complexes can cause cancer, and nickel is confirmed Carcinogens, and the same, nickel can cause skin allergies, copper-plated, nickel-plated fiber cloth is suitable for protective clothing worn next to the body; intrinsically conductive polymer fibers and composite polymer electromagnetic shielding fibers have poor fiber spinnability question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Dye 43dtex soybean fiber to form soybean fiber color silk, parallel with 59dtex nylon-based silver-plated fiber, twist 500 twists / m, form soybean silver-plated fiber as weft, and dye 134dtex cotton fiber to form cotton fiber color Silk, and 59dtex nylon-based silver-plated fibers are paralleled and twisted at 400 twists / m to form cotton silver-plated fibers as warps.

[0025] The cotton silver-plated fiber warp is warped, heald and reeded, and the soybean silver-plated fiber weft is interwoven with a plain weave with a warp density of 290 threads / cm and a weft density of 270 threads / cm. For silver fabric, the silver-plated fabric is washed with polyoxyethylated nonionic surfactant at 60°C to remove surface stains, heated and shaped at 120°C to obtain radiation-proof soybean fiber fabric.

[0026] The shielding effectiveness of radiation-proof soybean fiber fabrics measured by UV-1000F textile ultraviolet protection factor tester is 47, and the antibacterial rate of Esch...

Embodiment 2

[0028] Dye 56dtex soybean fiber to form soybean fiber color yarn, parallel with 76dtex polyester-based silver-plated fiber, twist 600 twists / m to form soybean silver-plated fiber as weft, and dye 150dtex cotton fiber to form cotton fiber color Silk, and 76dtex polyester-based silver-plated fibers are paralleled, twisted at 700 twists / m to form cotton silver-plated fibers as warps.

[0029] The cotton silver-plated fiber warp is warped, heald and reeded, and the soybean silver-plated fiber weft is interwoven with a plain weave with a warp density of 290 threads / cm and a weft density of 270 threads / cm. For silver fabric, the silver-plated fabric is cleaned at 80°C with a polyoxyethylene-based nonionic surfactant to remove surface stains, heated and set at 120°C to obtain a radiation-proof soybean fiber fabric.

[0030] The shielding effectiveness of radiation-proof soybean fiber fabrics measured by UV-1000F textile ultraviolet protection factor tester is 53%, and the antibacteri...

Embodiment 3

[0032] Dye 49dtex soybean fiber to form soybean fiber colored yarn, parallel with 65dtex polyester-based silver-plated fiber, twist 550 twists / m to form soybean silver-plated fiber as weft, and dye 140dtex cotton fiber to form cotton fiber color Silk, and 65dtex polyester-based silver-plated fibers are paralleled and twisted at 600 twists / m to form cotton silver-plated fibers as warps.

[0033] The cotton silver-plated fiber warp is warped, heald and reeded, and the soybean silver-plated fiber weft is interwoven with a plain weave with a warp density of 290 threads / cm and a weft density of 270 threads / cm. For silver fabrics, the silver-plated fabrics are washed with polyoxyethylated nonionic surfactant at 70°C to remove surface stains, heated and set at 120°C to obtain radiation-resistant soybean fiber fabrics.

[0034] The shielding effectiveness of radiation-proof soybean fiber fabrics measured by UV-1000F textile ultraviolet protection factor tester is 48, and the antibacte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method for anti-radiation soybean fiber fabrics. Soybean fibers, cotton fibers and silver-plated fibers are used as raw materials to be woven into anti-radiation soybean fiber fabrics through plain weave. The production method comprises the steps of dyeing the soybean fibers and the cotton fibers respectively, mixing and twisting the soybean fibers and the silver-plated fibers into wefts, using the cotton fibers and the silver-plated fibers as warps, and weaving the wefts and the warps through the plain weave into the anti-radiation soybean fiber fabrics. According to the production method, the soybean fiber fabrics are produced through a yarn dyeing method, the process route is short, after treatment is absent, oxidation and corrosion of silver-plated fibers during chemical agent heat treatment can be prevented, and the soybean fiber fabrics are good in anti-radiation and anti-bacterial performances and comfortable to wear next to the skin.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, in particular to a method for producing radiation-proof soybean fiber fabrics. Background technique: [0002] With the rapid development of high technology, various technological products have come out successively, which not only improve people's quality of life, but also bring electromagnetic radiation. Electromagnetic radiation has become the fourth pollution source after air pollution, water pollution and noise pollution, so the protection of electromagnetic radiation is urgent. [0003] There are two main methods for the production of radiation protection clothing: one is to use fibers with radiation protection function as raw materials to make protective clothing fabrics, and the other is to carry out radiation protection finishing on the fabrics. However, the radiation-proof fabric after finishing has limited color due to the influence of the coating, and the coating between th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D03D13/00A41D31/00D06C7/02D03D15/217D03D15/233D03D15/47D03D15/50D03D15/54
CPCA41D31/00D03D13/00D03D15/00D06C7/02D10B2201/02
Inventor 刘玲
Owner SUZHOU WILDER IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More