Water-resistant white latex

A white latex and emulsifier technology, applied in the field of white latex, can solve the problems of high toxicity of vinyl acetate, unable to meet strict requirements, poor environmental protection performance, etc., and achieve the effect of excellent curing time, meeting strict requirements and improving environmental performance.

Inactive Publication Date: 2015-05-20
海安县紫石涂料有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vinyl acetate used in this glue is highly toxic and not environmentally friendly
[0007] Chinese invention patent application 201410004735.1 (public date: April 16, 2014) discloses a water-resistant white latex. The glue includes: polyvinyl alcohol PVA, vinyl acetate VAC, acrylic acid AA, acrylamide AM, ammonium persulfate , anionic emulsifier A-102, alkyl polyoxyethylene ether LCN-287 nonionic emulsifier; corn starch, transparent powder, plasticizer, diethylene glycol dibenzoate DEDB, preservative KSG-201, hydroxide Sodium, and methanol; but this glue still uses toxic vinyl acetate, which has poor environmental performance
[0008] At the same time, the related glue disclosed in the prior art has poor comprehensive performance in terms of use effect and cannot meet the stringent demands of the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-resistant white latex

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment relates to a water-resistant latex and a preparation method thereof; the water-resistant latex is composed of the following components in parts by weight:

[0034] Polyvinyl acetate 700,

[0035] Vinyl acetate 300,

[0036] polyvinyl alcohol 120,

[0037] Dibutyl phthalate 60,

[0038] Diethylene glycol dibenzoate 20,

[0039] Octanol 10,

[0040] Isopropanol 30,

[0041] Allyl methacrylate 10,

[0042] Ethylene glycol dimethacrylate 5,

[0043] Toluene diisocyanate 3,

[0044] Sodium bicarbonate 35,

[0045] water 1400,

[0046] Emulsifier 40, the emulsifier is sodium oleate (i.e. sodium octadecenoate);

[0047] Composite initiator 5,

[0048] Methylolacrylamide 20,

[0049] waxy cornstarch 10,

[0050] sodium hypochlorite 2,

[0051] The composite initiator is composed of the following components in weight ratio: potassium persulfate, ammonium persulfate, sodium bisulfite, sodium persulfate, and kaolin in a weight ratio of 3:1:2:1:1.

[...

Embodiment 2

[0059] This embodiment relates to a kind of whitening-resistant latex. The preparation method of whitening-resistant latex refers to Example 1. The whitening-resistant latex is composed of the following components by weight:

[0060] Polyvinyl acetate 1050,

[0061] Vinyl acetate 350,

[0062] polyvinyl alcohol 145,

[0063] Dibutyl phthalate 100,

[0064] Diethylene glycol dibenzoate 40,

[0065] Octanol 15,

[0066] Isopropanol 45,

[0067] Allyl methacrylate 25,

[0068] Ethylene glycol dimethacrylate 10,

[0069] Toluene diisocyanate 7,

[0070] Sodium bicarbonate 50,

[0071] water 1500,

[0072] Emulsifier 50, the emulsifier is sodium dodecylbenzenesulfonate;

[0073] Composite initiator 9,

[0074] Methylolacrylamide 32,

[0075] waxy cornstarch 15,

[0076] Sodium hypochlorite 7,

[0077] The composite initiator is composed of the following components in weight ratio: potassium persulfate, ammonium persulfate, sodium bisulfite, sodium persulfate, and kaolin...

Embodiment 3

[0079] This embodiment relates to a kind of water whitening latex. The preparation method of water whitening latex refers to Example 1. Water whitening latex is composed of the following components by weight:

[0080] Polyvinyl acetate 800,

[0081] Vinyl acetate 315,

[0082] Polyvinyl alcohol 125,

[0083] Dibutyl phthalate 80,

[0084] Diethylene glycol dibenzoate 25,

[0085] Octanol 12,

[0086] Isopropanol 35,

[0087] Allyl methacrylate 15,

[0088] Ethylene glycol dimethacrylate 7,

[0089] Toluene diisocyanate 4,

[0090] Sodium bicarbonate 39,

[0091] water 1450,

[0092] Emulsifier 45, the emulsifier is sodium dodecylbenzenesulfonate;

[0093] Composite initiator 6,

[0094] Methylolacrylamide 25,

[0095] waxy cornstarch 12,

[0096] Sodium hypochlorite 4,

[0097] The composite initiator is composed of components in the following weight ratios: potassium persulfate, ammonium persulfate, sodium bisulfite, sodium persulfate, and kaolin in a weight rat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-resistant white latex which is composed of the following components in parts by weight: 700-1050 parts of polyvinyl acetate, 300-350 parts of vinyl acetate, 120-145 parts of polyvinyl alcohol, 60-100 parts of dibutyl phthalate, 20-40 parts of diethylene glycol dibenzoate, 10-15 parts of octanol, 30-45 parts of isopropanol, 10-25 parts of allyl methacrylate, 5-10 parts of glycol bis methacrylate, 3-7 parts of toluene diisocyanate, 35-50 parts of sodium bicarbonate, 1400-1500 parts of water, 40-50 parts of emulsifier 5-9 parts of composite initiator, 20-32 parts of hydroxymethyl acrylamide, 10-15 parts of waxy corn starch and 2-7 parts of sodium hypochlorite. The water-resistant white latex does not need formaldehyde or any other solvent, and has the advantages of environment friendliness, high heat stability, short primary drying time, excellent water resistance, excellent binding strength, excellent curing time, excellent comprehensive properties and the like.

Description

technical field [0001] The invention relates to the technical field of white latex, in particular to a water-resistant white latex. Background technique [0002] At present, the threshold industry of doors and windows is relatively low, and the competition in the industry is relatively chaotic. In order to improve product quality and market competitiveness, continuous improvement is required. High-grade energy-saving wooden doors and windows widely used in building exterior windows include: pure wood doors and windows, aluminum-clad wood doors and windows, and wood-aluminum composite doors and windows. The wood-aluminum composite doors and windows are more suitable for the rainy, high temperature and humid climate conditions in the south because the outer side is made of heat-insulating aluminum alloy profiles and the inner side is made of wood decorative profiles. At present, the structure of wood-aluminum composite doors and windows processed and produced in the domestic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09J4/02C09J11/06C09J11/08
Inventor 董德明
Owner 海安县紫石涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More