Waxy cornstarch additive composition and glue, application

A waxy corn starch and glue technology, applied in the directions of adhesive additives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of poor environmental protection performance, poor comprehensive performance, and insufficient environmental protection, and achieve Excellent comprehensive performance and the effect of improving performance

Active Publication Date: 2017-04-26
江苏中丽新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vinyl acetate used in this glue is highly toxic and not environmentally friendly
[0006] Chinese invention patent application 201410004735.1 (public date: April 16, 2014) discloses an environmentally friendly white latex, the glue includes: polyvinyl alcohol PVA, vinyl acetate VAC, acrylic acid AA, acrylamide AM, persulfuric acid Ammonium, anionic emulsifier A-102, alkyl polyoxyethylene ether LCN-287 nonionic emulsifier; corn starch, transparent powder, plasticizer, diethylene glycol dibenzoate DEDB, preservative KSG-201, hydrogen Sodium oxide, and methanol; but this glue still uses toxic vinyl acetate, which has poor environmental performance
[0007] At the same time, the related glue disclosed in the prior art has poor overall performance in terms of use effect, and cannot yet meet the relevant requirements for the quality of high-grade energy-saving wooden doors and windows.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waxy cornstarch additive composition and glue, application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment relates to a kind of waxy cornstarch additive composition, described composition is added in glue, and finally described glue is made up of each component of following parts by weight:

[0037] Polyvinyl acetate 700,

[0038] Vinyl acetate 300,

[0039] polyvinyl alcohol 120,

[0040] Dibutyl phthalate 60,

[0041] Diethylene glycol dibenzoate 20,

[0042] Octanol 10,

[0043] Isopropanol 30,

[0044] Allyl methacrylate 10,

[0045] Ethylene glycol dimethacrylate 5,

[0046] Toluene diisocyanate 3,

[0047] Sodium bicarbonate 35,

[0048] water 1400,

[0049] Emulsifier 40, the emulsifier is sodium oleate (i.e. sodium octadecenoate);

[0050] Initiator 5, the initiator is ammonium persulfate;

[0051] Methylolacrylamide 20,

[0052] waxy cornstarch 10,

[0053] Sodium hypochlorite 2.

[0054] All components involved in this example can be obtained through public commercial channels. The preparation method step of glue in the present embodi...

Embodiment 2

[0061] This embodiment relates to a waxy cornstarch additive composition, which is added to the glue, and finally the glue (refer to Example 1 for the preparation method) consists of the following components in parts by weight:

[0062] Polyvinyl acetate 1050,

[0063]Vinyl acetate 350,

[0064] polyvinyl alcohol 145,

[0065] Dibutyl phthalate 100,

[0066] Diethylene glycol dibenzoate 40,

[0067] Octanol 15,

[0068] Isopropanol 45,

[0069] Allyl methacrylate 25,

[0070] Ethylene glycol dimethacrylate 10,

[0071] Toluene diisocyanate 7,

[0072] Sodium bicarbonate 50,

[0073] water 1500,

[0074] Emulsifier 50, the emulsifier is sodium dodecylbenzenesulfonate;

[0075] Initiator 10, the initiator is ammonium persulfate;

[0076] Methylolacrylamide 32,

[0077] waxy cornstarch 15,

[0078] Sodium hypochlorite7.

Embodiment 3

[0080] This embodiment relates to a waxy cornstarch additive composition, which is added to the glue, and finally the glue (refer to Example 1 for the preparation method) consists of the following components in parts by weight:

[0081] Polyvinyl acetate 800,

[0082] Vinyl acetate 315,

[0083] Polyvinyl alcohol 125,

[0084] Dibutyl phthalate 80,

[0085] Diethylene glycol dibenzoate 25,

[0086] Octanol 12,

[0087] Isopropanol 35,

[0088] Allyl methacrylate 15,

[0089] Ethylene glycol dimethacrylate 7,

[0090] Toluene diisocyanate 4,

[0091] Sodium bicarbonate 39,

[0092] water 1450,

[0093] Emulsifier 45, the emulsifier is sodium dodecylbenzenesulfonate;

[0094] Initiator 6, the initiator is potassium persulfate;

[0095] Methylolacrylamide 25,

[0096] waxy cornstarch 12,

[0097] Sodium hypochlorite4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a waxy corn starch additive composition, and a glue and application thereof. The composition comprises hydroxymethyl acrylamide, waxy corn starch and sodium hypochlorite. The invention also provides application of the waxy corn starch additive composition in preparing the glue. The waxy corn starch additive composition can obviously enhance the comprehensive properties of the glue, so that the glue has excellent heat stability, excellent primary drying time, excellent water resistance, excellent binding strength, excellent curing time, excellent comprehensive properties and the like.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a waxy cornstarch additive composition, glue and application. Background technique [0002] At present, the threshold industry of doors and windows is relatively low, and the competition in the industry is relatively chaotic. In order to improve product quality and market competitiveness, continuous improvement is required. High-grade energy-saving wooden doors and windows widely used in building exterior windows include: pure wood doors and windows, aluminum-clad wood doors and windows, and wood-aluminum composite doors and windows. The wood-aluminum composite doors and windows are more suitable for the rainy, high temperature and humid climate conditions in the south because the outer side is made of heat-insulating aluminum alloy profiles and the inner side is made of wood decorative profiles. At present, the structure of wood-aluminum composite doors and windows p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J11/08C09J11/06C09J11/04C09J4/02C09J4/06
Inventor 胡浩
Owner 江苏中丽新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com