Decorative plate finishing paper and production method thereof

A decorative board and decorative paper technology, which is applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, paper, papermaking, etc., can solve the problems of being unable to degrade naturally, and achieve the goals of promoting rapid development, saving wood, and saving wood Effect

Active Publication Date: 2015-06-10
SHANDONG LUNAN NEW MATERIALS
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyolefin (Oxy) film is plastic and cannot be degraded naturally

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Fiber ratio: 80% by weight of wood pulp, 32% of long-fiber coniferous wood pulp, 48% of short-fiber hardwood pulp, 15% of functional fiber polyester, fiber fineness of 2D, length of 5mm, and additive 5 %, of which polyacrylamide 1%, polyamide epichlorohydrin 4%.

[0062] In-machine coating: coating liquid concentration 6%, polyvinyl alcohol 20%, dispersant 3%, water repellant 2%, titanium dioxide 5%, calcium powder 10%, latex 60%. The amount used for coating accounts for 5% of the total weight of the aforementioned three main raw materials.

[0063] In-machine impregnation: impregnation formula, melamine modified urea-formaldehyde glue 30%, modified glycerin 1%, modified starch 5%, polyvinyl alcohol 5%, penetrant JF-C 2%, polybutadiene resin 57%. The impregnation amount is 10%.

[0064] Paper weight 150g / m 2 , Thickness 0.9mm, tensile strength 5.2kn / m, tearing degree 3800mn longitudinally, transverse 4600mn, bursting strength 520kpa.

[0065] The base paper also nee...

Embodiment 2

[0073] Fiber ratio: 78% by weight of wood pulp, 38% of long-fiber softwood pulp, 40% of short-fiber hardwood pulp, 7% of polyester, and 9% of nylon. The fineness of the two fibers is 5D, and the length is 10mm. Add The solid content of additives is 6%, including 2% polyacrylamide and 4% polyamide epichlorohydrin.

[0074] In-machine coating: coating liquid concentration 10%, polyvinyl alcohol 25%, dispersant 3%, water repellant 2%, titanium dioxide 10%, calcium powder 20%, latex 40%. The amount used for coating accounts for 8% of the total weight of the aforementioned three main raw materials.

[0075] In-machine impregnation: impregnation formula, melamine modified urea-formaldehyde glue 25%, modified glycerin 1%, modified starch 5%, polyvinyl alcohol 5%, penetrant JF-C 2%, polybutadiene resin 62%. The impregnation amount is 8%.

[0076] Paper weight 320g / m 2 , thickness 2.4mm, tensile strength 6.5kn / m, tearing degree 5200mn longitudinally, transverse 5700mn, bursting stre...

Embodiment 3

[0085] Fiber ratio: 78% by weight of wood pulp, 30% of long-fiber coniferous wood pulp, 48% of short-fiber hardwood pulp, 9% of functional fibers polyester and 5% of vinylon, the fineness of both fibers is 3D, The length is 5mm, and 8% of additives are added, including 3% of polyacrylamide and 5% of polyamide epichlorohydrin.

[0086] In-machine coating: coating liquid concentration 8%, polyvinyl alcohol 20%, dispersant 3%, water repellant 2%, titanium dioxide 5%, calcium powder 10%, latex 60%. The amount used for coating accounts for 7% of the total weight of the aforementioned three main raw materials.

[0087] In-machine impregnation: impregnation formula, melamine modified urea-formaldehyde glue 35%, modified glycerin 1%, modified starch 5%, polyvinyl alcohol 5%, penetrant JF-C 2%, polybutadiene resin 52%. The impregnation amount is 12%.

[0088] Paper basis weight 220g / m 2 , Thickness 1.3mm, tensile strength 6kn / m, tearing degree 5000mn longitudinally, transverse 5200m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention aims to replace wood veneer and technical wood by using a piece of novel decorative plate finishing paper for artificial plate veneering. A piece of base paper which is 150-350g / m<2> is adopted, the upper layer of the base paper is printed with simulated natural and precious trees which are infrequent day by day, other artistic patterns can be also innovated and printed, and a vivid effect can be achieved after lamination. Due to adoption of chemical fiber in the decorative plate finishing base paper, the paper strength can be improved, and the paper is soft and tough. The decorative plate finishing paper is mainly applicable to veneering of artificial plates such as fiber boards and chipboards, and can replace veneering materials such as wood veneer and technical wood, and the finishing paper can have flame retardancy after being coated with a flame retardant adhesive.

Description

technical field [0001] The invention belongs to the technical field of special paper for veneering wood-based panels, and in particular relates to a novel decorative panel veneer paper and a production method thereof. Background technique [0002] Domestic traditional wood-based panel decorative panel materials include veneer, technical wood, impregnated decorative base paper, polyolefin (Oxy) film, etc. veneer, also known as veneer, is a thin wood veneer with the characteristics of precious tree species. Or veneer materials, the common species of veneer used for furniture veneer are ash, oak, catalpa, elm, southwest birch, more precious cherry wood, black walnut, red oak and more high-end such as White shadow wood, teak, rosewood, rosewood, rosewood, etc. Technological wood is also called artificial veneer. It is a sliced ​​veneer made of rotary-cut veneer of general tree species imitating the color tone of natural wood or precious tree species, and then glued into wood ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H13/24D21H13/26D21H13/20D21H13/22D21H19/38D21H19/60D21H21/06D21H17/51D21H19/44
Inventor 刘长冬佟瑞丰孙强
Owner SHANDONG LUNAN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com