Alkyd resin fireproof paint

A kind of technology of alkyd resin and fireproof coating, applied in fireproof coating, polyester coating, coating, etc., can solve the problems of high price, poor flame retardancy, limited application, etc., and achieve good fire resistance, water resistance and alkali resistance Good, strong adhesive effect

Inactive Publication Date: 2015-07-08
田福东
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the alkyd resin fire retardant coatings currently on the market have poor flame retar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkyd resin fireproof paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The alkyd resin fireproof coating of the present invention comprises the following components in parts by weight: 30 parts of medium oil alkyd resin, 5 parts of antimony trioxide, 1 part of carboxymethyl cellulose, 6 parts of glycerol, 4 parts of pentaerythritol 1 part, 1 part of acrylate, 8 parts of sodium dodecylbenzenesulfonate, 5 parts of calcium carbonate, 1 part of high-carbon alcohol fatty acid ester complex, 50 parts of deionized water.

Embodiment 2

[0024] The alkyd resin fireproof coating of the present invention comprises the following components in parts by weight: 40 parts of medium-oil alkyd resin, 10 parts of ammonium polyphosphate, 5 parts of carboxymethyl cellulose, 2 parts of glycerol, and 2 parts of pentaerythritol , 4 parts of polydimethylsiloxane, 2 parts of stearic acid, 10 parts of talcum powder, 3 parts of polyoxyethylene polyoxypropylene pentaerythritol ether, 30 parts of deionized water.

Embodiment 3

[0026] The alkyd resin fireproof coating of the present invention comprises the following components in parts by weight: 35 parts of medium oil alkyd resin, 7 parts of melamine, 3 parts of carboxymethyl cellulose, 4 parts of glycerol, 3 parts of pentaerythritol, poly 3 parts of methyl phenyl siloxane, 6 parts of fatty acid glyceride, 8 parts of barium sulfate, 2 parts of polyoxyethylene polyoxypropanolamine ether, 40 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Alkyd resin fireproof paint is disclosed. The alkyd resin fireproof paint comprises following components by weight: 30-40 parts of medium oil alkyd resin, 5-10 parts of a halogen-free fire retardant, 1-5 parts of carboxymethyl cellulose, 2-6 parts of glycerol, 2-4 parts of pentaerythritol, 1-4 parts of a levelling agent, 2-8 parts of a dispersant, 5-10 parts of a filler, 1-3 parts of a defoaming agent and 30-50 parts of deionized water. The alkyd resin fireproof paint is good in fireproof performance, halogen-free, high in adhesion force, good in water resistance, good in alkali resistance, and suitable for the fields of painting of furniture, electric products, electronics, and the like.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an alkyd resin fireproof coating. Background technique [0002] On February 13, 2003, the Official Journal of the European Union published the "Waste Electrical and Electronic (WEEE)" Directive (2002 / 96EC) and the "Restriction of the Use of Certain Hazardous Substances in Electrical and Electronic Equipment" (ROHS) Directive (2002 / 95 / EC) . Among them, the ROHS directive requires that electrical and electronic products put on the EU market after July 1, 2006 must not contain harmful substances such as lead, mercury, cadmium, hexavalent chromium, polybrominated biphenyls and polybrominated diphenyl ethers. Therefore, the research and development of halogen-free flame-retardant materials that do not contain harmful substances specified in the directive is currently a hot spot at home and abroad. [0003] Alkyd resin is a resin formed by the reaction of fatty acid, dibasic acid and polyol. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/08C09D5/18C09D7/12
CPCC09D167/08C08L2201/02C08L2201/22C08L2205/035C09D5/18C09D7/61C09D7/63C09D7/65C08L1/286C08K13/02C08K3/2279C08K5/053C08K2003/265C08L83/04C08L71/02C08K2003/323C08K5/09C08K3/34C08K5/34922C08K2003/3045C08K5/521C08K3/36
Inventor 田福东
Owner 田福东
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap