A kind of environment-friendly adhesive for construction and preparation method thereof

A kind of adhesive, environment-friendly technology, applied in the direction of adhesive type, cellulose adhesive, polymer adhesive additive, etc., can solve pollution and other problems, achieve long storage time, high safety, and production process simple effect

Active Publication Date: 2017-01-18
江苏海云花新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, 801 glue contains unreacted formaldehyde, and formaldehyde is the main cause of indoor environmental pollution. Because it contains more formaldehyde, it has been included in the list of eliminated building materials by the Ministry of Housing and Urban-Rural Development. It is currently used in home decoration. forbidden to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly adhesive for construction and preparation method thereof
  • A kind of environment-friendly adhesive for construction and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Add 650kg of tap water into the stirred reactor, heat up to 45°C, add 30kg of polyvinyl alcohol, heat while stirring, control the temperature in the kettle at 90-95°C, and keep stirring for 0.5 hours to completely dissolve the polyvinyl alcohol .

[0038] After the polyvinyl alcohol is completely dissolved, cool the temperature in the kettle to 65°C, add 1.2 kg of hydrochloric acid solution with a mass percentage of 30%, and the dropping time is controlled within 15 minutes, then add 3 kg of polyacrylamide and 0.6 kg of sodium polyacrylate respectively, 4kg hydroxypropyl methylcellulose, heat preservation and stirring for 0.5 hours.

[0039] After the heat preservation is over, cool the material temperature in the kettle to 50°C, then add 0.1kg sodium bisulfite, 0.06kg ammonium persulfate, and 3kg urea respectively, and after stirring for 1 hour, slowly add 7.5kg of 5% sodium hydroxide solution , adjust the pH to 7.2, then continue to cool the temperature of the materi...

Embodiment 2

[0041] Add 700kg of tap water into the stirred reactor, heat up to 50°C, add 32kg of polyvinyl alcohol, heat while stirring, control the temperature in the kettle at 90-95°C, keep stirring for 0.5 hours to dissolve the polyvinyl alcohol .

[0042] After the polyvinyl alcohol is completely dissolved, cool the temperature in the kettle to 68°C, add 1.5 kg of hydrochloric acid solution with a mass percentage of 30%, and the dropping time is controlled within 15 minutes, then add 4 kg of polyacrylamide and 0.8 kg of sodium polyacrylate respectively, 5kg hydroxypropyl methylcellulose, heat preservation and stirring for 0.5 hours.

[0043] After the heat preservation is over, cool the temperature of the material in the kettle to 52°C, then add 0.13kg of sodium bisulfite, 0.08kg of ammonium persulfate, and 4kg of urea respectively. After stirring for 1 hour, slowly add 9.5kg of 5% sodium hydroxide solution , adjust the pH to 7.6, then continue to cool the temperature of the material...

Embodiment 3

[0045] Add 750kg of tap water into the stirred reactor, heat up to 48°C, add 36kg of polyvinyl alcohol, heat while stirring, control the temperature in the kettle at 90-95°C, and keep stirring for 0.5 hours to dissolve all the polyvinyl alcohol .

[0046] After the polyvinyl alcohol is completely dissolved, cool the temperature in the kettle to 70°C, add 1.8 kg of hydrochloric acid solution with a mass percentage of 30%, and the dropping time is controlled within 15 minutes, then add 5 kg of polyacrylamide, 1 kg of sodium polyacrylate, and 6 kg of sodium polyacrylate respectively. Hydroxypropyl methylcellulose, heat preservation and stirring for 0.5 hours.

[0047] After the heat preservation is over, cool the temperature of the material in the kettle to 55°C, then add 0.15kg of sodium bisulfite, 0.1kg of ammonium persulfate, and 6kg of urea, and after stirring for 1 hour, slowly add 11.2kg of 5% sodium hydroxide solution , adjust the pH to 7.8, then continue to cool the temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a building adhesive. The adhesive is prepared from raw materials in parts by weight as follows: 28-36 parts of polyvinyl alcohol, 1-2 parts of a hydrochloric acid solution, 3-5 parts of polyacrylamide, 0.5-1 part of sodium polyacrylate, 3-6 parts of hydroxypropyl methyl cellulose, 0.1-0.15 parts of sodium hydrogen sulfite, 0.06-0.1 parts of ammonium persulfate, 2-6 parts of urea, 5-15 parts of a sodium hydroxide solution, 0.5-0.8 parts of sodium dodecyl benzene sulfonate, 0.3-0.6 parts of dodecyl dimethyl benzyl ammonium bromide and 600-800 parts of water. The building adhesive is prepared through condensation and amination reactions; meanwhile, a dispersing agent and a mildew preventive are added; the building adhesive is green, environment-friendly, formaldehyde-free, colorless, odorless, good in consistence, high in bonding strength, long in storage time and good in water-retaining property, cannot coagulate at the low temperature, can be mixed with white cement, talcum powder, gypsum powder and the like and is easy to construct, and powder falling and rolling are not caused.

Description

technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to an environment-friendly construction adhesive and a preparation method thereof. Background technique [0002] In the field of building decoration materials, building adhesives are a very important basic material. It is mainly used for tile bonding, cement-based adhesives, putty adhesive materials for interior and exterior walls, wallpaper and wallpaper adhesives, base materials for general architectural coatings, etc. Most of the wall adhesives with good quality in the domestic market are imported products at present, and their prices are expensive. Most of the domestically produced products use a single adhesive, and there are gaps in its water solubility, stability, and environmental protection. Especially, environmental protection has become the focus of people's attention. The commonly used 801 glue is made by polycondensation reaction of polyvinyl alcohol and f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J129/04C09J101/28C09J133/26C09J11/08C09J11/06C09J11/04
Inventor 蒋锡琴
Owner 江苏海云花新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com