Preparation method of spherical lithium ion battery anode material vanadium borate

A technology for lithium-ion batteries and negative electrode materials, applied in battery electrodes, circuits, electrical components, etc., can solve problems such as low theoretical capacity and poor safety performance, and achieve the effects of improving tap density, facilitating processing, and enhancing bonding

Active Publication Date: 2015-08-05
CENT SOUTH UNIV
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, due to its low theoretical capacity (about 372mAh / g) and poor safety performance, commercial graphite anode materials are difficult to meet the requirements of power batteries. Therefore, it is particularly necessary to explore other alternative materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of spherical lithium ion battery anode material vanadium borate
  • Preparation method of spherical lithium ion battery anode material vanadium borate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0038] This embodiment includes the following steps:

[0039] (1) Weigh 0.04mol of vanadium pentoxide, 0.08mol of ammonium borate, and 0.18mol of oxalic acid, mix them, and dissolve them in 100mL of deionized water to obtain a mixed solution;

[0040] (2) Place the mixed solution obtained in step (1) in a constant temperature water bath at 80°C and stir for 6 hours to form a homogeneous solution;

[0041] (3) adjusting the pH value of the solution obtained in step (2) to 9;

[0042] (4) The solution treated in step (3) is dried and granulated by spray drying. The air inlet temperature of the spray drying is 200°C, the speed of the peristaltic pump is 1500 rpm, and the speed of the fan is 100 Hz to obtain vanadium borate ( VBO 3 )Precursor;

[0043] (5) Vanadium borate (VBO) obtained in step (4) 3 ) precursors were placed in a tubular sintering furnace, sintered at 500 °C for 20 h in a nitrogen atmosphere, and then naturally cooled to room temperature to obtain a spherical ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of a spherical lithium ion battery anode material vanadium borate includes following steps: (1) dissolving a vanadium source, a boron source and a reduction agent in deionized water to obtain a mixed solution according to the molar ratio of vanadium element, boron element to the reduction agent of 1:1:2-4; (2) placing the mixed solution in a 60-90 DEG C constant-temperature water-bath pot with stirring for 4-8 h to obtain a solution; (3) regulating the pH of the solution to 6-9; (4) performing granulation to obtain a vanadium borate precursor in a spray-drying manner; (5) placing the vanadium borate precursor in a tubular sintering furnace and sintering the vanadium borate precursor at 500-800 DEG C for 8-20 h under a non-reducing atmosphere. The spherical lithium ion battery anode material vanadium borate is high in specific capacity, is excellent in rate capability and is excellent in cycle performance due to the unique crystal structure and micro appearance of the material.

Description

technical field [0001] The invention relates to a preparation method of a lithium ion battery negative electrode material, in particular to a preparation method of a spherical lithium ion battery negative electrode material vanadium borate. Background technique [0002] Lithium-ion power batteries have an absolute advantage in the development of the global electric vehicle industry, and its dominant position will not be shaken in the next few decades. With the continuous development of society, it is particularly necessary to develop power batteries with high energy density. Low cost, long life and high safety, as the core elements of power batteries, are closely related to electrode materials. As a key factor determining the overall performance of lithium-ion batteries, the research on negative electrode materials has always been a hot spot in this field. At present, due to its low theoretical capacity (about 372mAh / g) and poor safety performance, commercial graphite anod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/1397
CPCY02E60/10
Inventor 张宝朱玉时郑俊超韩亚东孙楠周其杰童汇田业成
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com