Metal bonding powder coating with mirror-like silver effect as well as preparation method and application thereof

A powder coating, mirror silver technology, applied in powder coatings, anti-corrosion coatings, anti-fouling/underwater coatings, etc., can solve the problems of ink pollution, pigments, fineness, etc., and achieve excellent decorative performance, high gloss, and excellent adhesion. Effect

Pending Publication Date: 2015-09-02
山东朗法博粉末涂装科技有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The pollution problem of ink lies in the pigments. These pigments have very small particles and strong adsorption capacity. They contain heavy metal elements such as lead, chromium, cadmium, and mercury, all of which have certain toxicity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal bonding powder coating with mirror-like silver effect as well as preparation method and application thereof
  • Metal bonding powder coating with mirror-like silver effect as well as preparation method and application thereof
  • Metal bonding powder coating with mirror-like silver effect as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The base powder of the metal bonding powder coating with mirror silver effect is made of the following raw materials in mass percentage:

[0027]

[0028]

[0029] The above raw materials are mixed evenly, melted and extruded by an extruder, tableted, air-cooled, milled, and sieved to obtain a base powder of a metal bonding powder coating with a mirror-like silver effect.

[0030] Add aluminum powder according to 0.7% of the total mass of the base powder, and perform bonding at a temperature of 60°C, and set the bonding time to 12 minutes.

[0031] The metal bonding powder coating with mirror silver effect prepared in this example was heated in an electric blast drying oven, the curing temperature was 200° C., and the curing time was 10 minutes.

[0032] The performance test results of the obtained coating film after curing are shown in Table 1:

[0033] Table 1 The performance test result of embodiment 1 coating film

[0034]

Embodiment 2

[0036] The base powder of the metal bonding powder coating with mirror silver effect is made of the following raw materials in mass percentage:

[0037]

[0038] The base powder was prepared according to the steps described in Example 1, except that the aluminum powder was added to the base powder according to 0.75% of the total mass of the base powder, the bonding temperature was 62° C., and the bonding time was set to 10 minutes.

[0039] The curing temperature is 190° C., and the curing time is 13 minutes.

[0040] The performance test results of the obtained coating film after curing are shown in Table 2:

[0041] The performance test result of table 2 embodiment 2 coating film

[0042]

Embodiment 3

[0044] The base powder of the metal bonding powder coating with mirror silver effect is made of the following raw materials in mass percentage:

[0045]

[0046] The base powder was prepared according to the steps described in Example 1, except that the aluminum powder was added to the base powder according to 0.7% of the total mass of the base powder, the bonding temperature was 58° C., and the bonding time was set to 15 minutes.

[0047] The curing temperature is 180° C., and the curing time is 15 minutes.

[0048] The performance test results of the obtained coating film after curing are shown in Table 3:

[0049] Table 3 The performance test result of embodiment 3 coating film

[0050]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of powder coating and particularly relates to a metal bonding powder coating with a mirror-like silver effect as well as a preparation method and application thereof. The powder coating is prepared by binding base powder and aluminum powder, wherein the base powder is prepared from the following raw materials in percentage by weight: 82 to 85 percent of polyester resin, 12.5 to 15 percent of curing agent, 0.8 to 1 part of leveling agent, 0.3 to 0.5 percent of benzoin, 0.8 to 1 percent of sensitizer and 0.3 to 0.5 percent of antioxidant. The preparation method of the metal bonding powder coating comprises the following steps of uniformly mixing raw materials, performing melt extrusion by an extruder, and performing tabletting, air cooling, grinding and sieving to obtain the base powder; binding the aluminum powder and the base powder. The powder coating disclosed by the invention has the characteristics of good corrosion resistance, good wear resistance, excellent decorating performance, good environment friendliness and no toxicity; the preparation method has the advantages of less investment, low cost, safe production and operation and in accordance with the requirements of large precise product manufacturers at home and abroad; a coating film of the coating has the advantages of high glossiness, high anti-pollution capacity, good greenness, good environmental protection and wide application field.

Description

technical field [0001] The invention belongs to the field of powder coatings, and in particular relates to a metal bonding powder coating with a mirror silver effect, a preparation method and an application thereof. Background technique [0002] The metal powder coating film has a metallic luster, a gorgeous multi-color effect and outstanding protection functions. It is mainly used in indoor and outdoor metal furniture, lamps, handicrafts, range hoods, baby carriages, sports equipment and other industries. According to the appearance gloss effect of the coating film, the flat metal powder coatings can be divided into high gloss, flash (colorful, different colors with corners), and metallic effect. Among them, flash and metal effect products have been promoted and applied to the surface coating of high-end cars, providing colorful appearance decoration for high-end industrial products such as automobiles, home appliances, and instruments. [0003] Silver mirrors are widely u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/06C09D5/03C09D5/10C09D5/16C09D7/12
Inventor 张剑肖建刚刘鹏邢方圆
Owner 山东朗法博粉末涂装科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com