Preparation process for magnetic chlorinated rubber

A chlorinated rubber and production process technology, applied in the field of rubber materials, can solve the problems of rare magnetic chlorinated rubber and large demand, and achieve the effects of improving chlorination efficiency, saving energy and reducing power costs

Inactive Publication Date: 2015-09-09
ANHUI TONGFENG RUBBER & PLASTIC IND
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With its unique flexibility and plasticity, magnetic rubber is widely used in machinery, electronics, medical treatment, mining, cutting-edge science, and even daily necessities. It fills the fields that rigid magnets cannot set foot in, and its demand is increasing. Production of magnetic chlorinated rubber is currently rare

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of manufacture technology of magnetic chlorinated rubber, comprises the steps:

[0021] 1) Raw material preparation: add 200 parts of natural rubber, 20 parts of surfactant and 80 parts of 20% hydrochloric acid aqueous solution to the chlorinator, so that the pH value of the solution in the chlorinator reaches 4, and an ultraviolet lamp is installed outside the chlorinator irradiation;

[0022] 2) Rubber mastication: Stir and feed chlorine gas into the reaction vessel at a temperature of 60°C;

[0023] 3) Magnetic orientation mixing: add stearic acid, vulcanization accelerator, zinc oxide, anti-aging agent, black carbon and strontium ferrite magnetic powder into the reaction vessel;

[0024] 4) Rubber molding and magnetization: After mixing evenly, add sulfur and accelerator to the open mill, thinly pass out the sheet, put the mixed rubber in a magnetizer, take it out after magnetization for a certain period of time, and place it at room temperature for 24 h, c...

Embodiment 2

[0027] A kind of manufacture technology of magnetic chlorinated rubber, comprises the steps:

[0028] 1) Raw material preparation: Add 220 parts of natural rubber, 30 parts of surfactant and 90 parts of 20% hydrochloric acid aqueous solution to the chlorinator, so that the pH value of the solution in the chlorinator reaches 4, and an ultraviolet lamp is installed outside the chlorinator irradiation;

[0029] 2) Rubber mastication: Stir and feed chlorine gas into the reaction vessel at a temperature of 70°C;

[0030] 3) Magnetic orientation mixing: add stearic acid, vulcanization accelerator, zinc oxide, anti-aging agent, black carbon and strontium ferrite magnetic powder into the reaction vessel;

[0031] 4) Rubber molding and magnetization: After mixing evenly, add sulfur and accelerator to the open mill, thinly pass out the sheet, put the mixed rubber in a magnetizer, take it out after magnetization for a certain period of time, and place it at room temperature for 24 h, c...

Embodiment 3

[0034] A kind of manufacture technology of magnetic chlorinated rubber, comprises the steps:

[0035] 1) Raw material preparation: add 240 parts of natural rubber, 40 parts of surfactant and 100 parts of 20% hydrochloric acid aqueous solution to the chlorinator, so that the pH value of the solution in the chlorinator reaches 4, and an ultraviolet lamp is installed outside the chlorinator irradiation;

[0036] 2) Rubber mastication: Stir and feed chlorine gas into the reaction vessel at a temperature of 80°C;

[0037] 3) Magnetic orientation mixing: add stearic acid, vulcanization accelerator, zinc oxide, anti-aging agent, black carbon and strontium ferrite magnetic powder into the reaction vessel;

[0038] 4) Rubber molding and magnetization: After mixing evenly, add sulfur and accelerator to the open mill, thinly pass out the sheet, put the mixed rubber in a magnetizer, take it out after magnetization for a certain period of time, and place it at room temperature for 24 h, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process for magnetic chlorinated rubber, relating to the technical field of rubber processing. The process comprises the following steps of 1) raw material preparation; 2) sizing material plastication; 3) magnetic oriented mixing; 4) sizing material molding and magnetizing; and 5) sizing material vulcanization. The magnetic chlorinated rubber prepared by using the preparation process has good fire resistance, high strength, excellent mechanical property and good abrasive resistance, can be adapted to rubbing for a long time, can not be damaged, and has high magnetic property and good elasticity; an environment-friendly fire retardant is added in the mixing process, so that the flame retardant property is further improved; plenty of energy sources can be saved in the production process, and the preparation process is simple and is easy to master.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a manufacturing process of magnetic chlorinated rubber. Background technique [0002] Rubber is an irreplaceable high-elastic polymer material. With the increasing shortage of petroleum resources, the research on green rubber products made of renewable resources has become a current research hotspot. Natural rubber is a highly elastic material collected from natural plants and processed. It is a natural polymer compound with polyisoprene as the main component. Because of its excellent comprehensive performance and processing performance, it is Widely used in industrial production and scientific research. In order to further improve the physical and mechanical properties of natural rubber and reduce its industrial cost, various composite rubber products have appeared one after another. [0003] Chlorinated rubber is an important rubber derivative in industry. It is wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L15/02C08K13/02C08K5/09C08K3/04C08K3/22C08K3/06C08C19/14B29C35/02
Inventor 项宗武
Owner ANHUI TONGFENG RUBBER & PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com