A kind of one-component salt-spray resistant water-based paint and preparation method thereof

A technology of salt spray resistance and water-based paint, applied in coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve problems such as hindering the promotion and application of water-based anti-corrosion coatings, and the function of salt spray resistance is not as good as oil-based coatings, saving drying effect of time, excellent corrosion resistance, good chemical resistance

Active Publication Date: 2017-08-29
ZHANGZHOU XIN ZHAN WANG CHEM IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the particularity of water-based coatings, the salt spray resistance of current water-based anti-rust coatings is not as good as that of oil-based coatings, which is also a major obstacle to the promotion and application of water-based anti-corrosion coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The concrete steps of preparation method are as follows:

[0026] (1) Put deionized water into the mixing tank and start stirring;

[0027] (2) Maintain a stirring speed of 800rpm, add environmental protection additives into the water, and stir for 0.3-0.5 hours;

[0028] (3) Maintain a stirring speed of 800rpm, add environmental protection resin, and stir for 0.2-0.3 hours;

[0029] (4) Maintain a stirring speed of 800rpm, add anti-rust pigments, and stir for 0.5-1.0 hours;

[0030] (5) Grind after stirring evenly; control the fineness to ≤15 µm;

[0031] (6) Add special environmental protection resin, stir evenly, and adjust the viscosity.

Embodiment 1

[0033] A single-component salt-spray-resistant water-based paint, raw materials in parts by weight: 43 parts of environmental protection resin, 9 parts of special environmental protection resin, 25 parts of antirust pigment, 15 parts of deionized water, and 8 parts of environmental protection additive.

[0034] The environment-friendly resin is water-dispersed amino resin.

[0035] The special environmental protection resin is water emulsion type polyurethane modified epoxy resin.

[0036] The anti-rust pigments are zinc phosphate, iron oxide red, mica iron oxide.

[0037] The environmental protection additive is a dispersant.

[0038] The concrete steps of preparation method are as follows:

[0039] (1) Put deionized water into the mixing tank and start stirring;

[0040] (2) Maintain a stirring speed of 800rpm, add environmental protection additives into the water, and stir for 0.3 hours;

[0041] (3) Maintain a stirring speed of 800rpm, add environmental protection resi...

Embodiment 2

[0047] A single-component salt-spray-resistant water-based paint, raw materials in parts by weight: 20 parts of environmental protection resin, 5 parts of special environmental protection resin, 20 parts of antirust pigment, 13 parts of deionized water, and 2 parts of environmental protection additive.

[0048] The environmental protection resin is water-soluble epoxy resin.

[0049] The special environment-friendly resin is water-dispersed acrylic resin.

[0050] The antirust pigments are micaceous iron oxide, iron phosphate and zinc oxide.

[0051] Described environmental protection assistant is dispersant and leveling agent.

[0052] The concrete steps of preparation method are as follows:

[0053] (1) Put deionized water into the mixing tank and start stirring;

[0054] (2) Maintain a stirring speed of 800rpm, add environmental protection additives into the water, and stir for 0.5 hours;

[0055] (3) Maintain a stirring speed of 800rpm, add environmental protection res...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
adhesivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses one-component salt fog resistant water paint and a preparation method thereof. The water paint includes the following raw materials in parts by weight: 20-46 parts of EPMC, 5-18 parts of special EPMC, 20-40 parts of anti-rust pigment, 13-30 parts of deionized water, 2-10 parts of an environment-friendly additive. The product is excellent in performance: the hardness is greater than or equal to H, the adhesive force is of 0-1 level, and the salt fog resistant duration is longer than 800 hours; the paint is environment-friendly and wide in application range.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a single-component salt spray-resistant water-based paint and a preparation method thereof. Background technique [0002] When the metal is exposed to the humid atmosphere, due to the activity of its surface, it has an adsorption effect on the polar moisture in the atmosphere, forming a layer of water film. When the water film layer reaches a certain thickness, it forms the necessary chemical corrosion a. Whether it is oxygen absorption corrosion or hydrogen evolution corrosion, because the anode area and the cathode area are in contact with each other, electrons move from the anode to the cathode under the action of the corrosion electric field force, and are absorbed by the nearby reducible medium, completing the electrochemical corrosion. . And because depolarizers such as oxygen and water are relatively abundant under atmospheric conditions, metal corrosion phenomena con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D161/20C09D163/00C09D167/06C09D175/04C09D133/02C09D123/28C09D7/12C09D5/08
CPCC08L2205/03C09D5/08C09D7/61C09D161/20C09D163/00C09D167/00C08L75/04C08K13/02C08K2003/328C08K2003/2272C08L33/00C08K2003/2296C08L23/28C08L101/00
Inventor 张信露谢平展张秋虹
Owner ZHANGZHOU XIN ZHAN WANG CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap