Anticorrosive material for metallic equipment and preparation and construction methods thereof

A technology of anti-corrosion materials and anti-corrosion coatings, applied in the field of materials, can solve the problems of reduced salt spray resistance, coating adhesion, mechanical properties of impact resistance, equipment damage, etc., to achieve accelerated speed, small construction environment, and guaranteed construction. effect of progress

Inactive Publication Date: 2015-09-09
YUGREAT (BEIJING) INTERNATIONAL TECHNOLOGY CO LTD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The corrosion of metal equipment not only consumes precious wealth, but also destroys the normal operation of production and life
Corroded metal equipment will deteriorate in shape, color, and mechanical properties, leading to equipment damage, serious waste of resources and energy, and even serious accidents
[0003] Traditional anti-corrosion coatings are not ideal for the corrosion protection of the base metal due to the limitations of their own material properties and processes, and a considerable part of the coatings contain toxic substances such as lead or chromate, which are polluted during preparation and use. Environmental hazards, which are not compatible with the requirements of the socio-economic sustainable development strategy
At present, most of the commonly used anti-corrosion coatings are epoxy zinc-rich paints, but in the prior art, the dry film metal zinc content based on epoxy zinc-rich paints is more than 80%, and the adhesion of the coating and the mechanical impact resistance The performance will decrease with the increase of zinc content, and the salt spray resistance will also decrease, so that the coating is easily damaged by external force during the construction process, which will affect the corrosion resistance of the coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anticorrosive material for metallic equipment and preparation and construction methods thereof
  • Anticorrosive material for metallic equipment and preparation and construction methods thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] refer to figure 1 , which shows a flow chart of a method for preparing the rubber asphalt anticorrosion coating in an anticorrosion material for metal equipment according to an embodiment of the present invention, and the preparation method specifically includes:

[0049] Step 101. Preparation of vulcanized rubber-modified anionic emulsified asphalt: mixing asphalt and vulcanized rubber and emulsifying to prepare vulcanized rubber-modified anionic emulsified asphalt.

[0050] Step 102. Preparation of the antirust agent: adding one or more of zinc phosphate, modified zinc phosphate, and zinc molybdate, and wetting agent, deionized water, and surfactant in proportion to prepare an antiseptic Crude product, the crude product of the anti-rust agent is dispersed at a speed of 1000-2000r / min, the dispersion time is 1h, and then the crude product of the dispersed anti-rust agent is ground, and the grinding time is 1h to obtain the anti-rust agent .

[0051] Step 103, prepara...

Embodiment 1

[0060] When preparing rubber asphalt anticorrosion coatings for metal equipment anticorrosion materials, 63kg of asphalt and 27kg of vulcanized rubber were mixed and then emulsified to obtain 90kg of vulcanized rubber modified anionic emulsified asphalt.

[0061] Add successively 0.1kg of rosin soap and fatty acid soap, 0.1kg of wetting agent, 0.1kg of polynaphthalene sulfonic acid sodium salt, 0.1kg of deionized water and 0.1kg of zinc phosphate to mix to obtain the rust inhibitor crude product, and the The rust preventive crude product is dispersed at a speed of 1000r / min for 1 hour, and then the dispersed rust preventive crude product is ground for 1 hour to obtain a total amount of 0.5 kg of the rust preventive. .

[0062] Put 0.1kg of rosin soap and fatty acid soap, 0.1kg of dispersant, 0.1kg of sodium alkyl sulfate, 0.1kg of hindered amine light stabilizer, 0.1kg of defoamer and 0.1kg of anti-aging agent at 500r / min Mix and disperse at a rotating speed for 1 hour to pre...

Embodiment 2

[0065] When preparing rubber asphalt anticorrosion coatings for metal equipment anticorrosion materials, 63kg of asphalt and 27kg of vulcanized rubber were mixed and then emulsified to obtain 90kg of vulcanized rubber modified anionic emulsified asphalt.

[0066] Add 0.1kg of rosin soap and fatty acid soap, 0.1kg of wetting agent, 0.1kg of sodium polynaphthalene sulfonate, 0.1kg of deionized water, 0.1kg of zinc phosphate, 0.1kg of modified zinc phosphate and 0.1 kg of zinc molybdate mixed to obtain the rust preventive crude product mixed to obtain the rust preventive crude product, the rust preventive crude product was dispersed at a speed of 1000r / min for a dispersion time of 1h, and then the dispersed rust preventive The crude product of the agent was ground for 1 hour to obtain a total amount of 0.7 kg of the antirust agent.

[0067] Put 0.1kg of rosin soap and fatty acid soap, 0.1kg of dispersant, 0.1kg of sodium alkyl sulfate, 0.1kg of hindered amine light stabilizer, 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anticorrosive material for metallic equipment. The material comprises a rubber-asphalt anticorrosive coating material and an organic acid type curing agent, wherein the organic acid type curing agent consists of one or more of citric acid type curing agent, sorbic acid, amino naphthalene disulfonic acid and tartaric acid, and an anti-rusting agent is added in the rubber-asphalt anticorrosive coating material and is prepared from one or more of zinc phosphate, modified zinc phosphate and zinc molybdate, a surfactant, a wetting agent, a dispersing agent and deionized water. According to the anticorrosive material for the metallic equipment and the preparation and construction methods thereof, the anti-rusting agent is innovatively added in the anticorrosive material for the metallic equipment, so that the anticorrosive material for the metallic equipment, prepared by using the anti-rusting agent, has more excellent corrosion resistance while guaranteeing environmental friendliness; meanwhile, the weather resistance is very excellent, and the service life of the metallic equipment is greatly prolonged; the organic acid type curing agent, of which the corrosiveness to metal can be neglected, is used innovatively, and the required curing performance can be effectively guaranteed by the organic acid type curing agent.

Description

technical field [0001] The invention relates to the field of material technology, in particular to an anti-corrosion material for metal equipment, a preparation method for the anti-corrosion material for metal equipment, and a construction method for the anti-corrosion material for metal equipment. Background technique [0002] Corrosion of metal materials is a worldwide problem. The corrosion of metal equipment not only consumes precious wealth, but also destroys the normal operation of production and life. Corroded metal equipment will deteriorate in shape, color, and mechanical properties, leading to equipment damage, serious waste of resources and energy, and even serious accidents. [0003] Traditional anti-corrosion coatings are not ideal for the corrosion protection of the base metal due to the limitations of their own material properties and processes, and a considerable part of the coatings contain toxic substances such as lead or chromate, which are polluted durin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D195/00C09D121/02C09D7/12C09D5/08
Inventor 王彦秋李晓亮罗莹莹黄金星
Owner YUGREAT (BEIJING) INTERNATIONAL TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com