Halogen-free flame-retardant TPVC ( polyvinyl chloride elastomer) material and preparation method therefor
A technology of PVC resin and flame retardant, which is applied in the field of polymer composite materials and its preparation, can solve the problems of harm to human body, increase of flammability of TPVC material, decrease of mechanical properties of TPVC material, etc., and achieve good environmental protection and synergistic flame retardant Good resistance, the effect of improving cold resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example
[0025] (Example 1)
[0026] The halogen-free flame retardant TPVC material of this embodiment is made of the following components by weight:
[0027] 100kg of SG-3 type PVC resin.
[0028] 30 kg of dioctyl terephthalate (DOTP), 4.5 kg of epoxy fatty acid methyl ester, 22.5 kg of diphenyl monoisooctyl phosphate (DPOP), and 3 kg of chlorinated paraffin were used as plasticizers.
[0029] 6kg of calcium zinc composite stabilizer.
[0030] 1 kg of calcium stearate, 1.1 kg of stearic acid and 1 kg of polyethylene wax as lubricants.
[0031] 50kg of active magnesium hydroxide, 6kg of microcapsule red phosphorus, 4kg of antimony trioxide and 5kg of zinc borate as halogen-free flame retardants.
[0032] The preparation method of the above-mentioned halogen-free flame-retardant TPVC material has the following steps:
[0033] ①Weigh SG-3 type PVC resin, dioctyl terephthalate, epoxy fatty acid methyl ester, diphenyl-isooctyl phosphate, chlorinated paraffin, calcium-zinc composite sta...
Example
[0038] (Example 2 to Example 6)
[0039] The preparation method of each embodiment is the same as that of embodiment 1, and the difference lies in the formula of halogen-free flame retardant TPVC material, as shown in Table 1 for details.
[0040] Table 1
[0041]
Example
[0042] (application example)
[0043] The halogen-free flame retardant TPVC materials prepared in Examples 1 to 6 were molded and sampled, and the mechanical properties and flame retardant properties of the standard samples were tested according to national standards. The test results are shown in Table 2.
[0044] Table 2
[0045] Test performance Performance standard test Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Tensile strength / MPa >10.0 GB / T1043-2006 12.8 13.1 12.1 12.5 12.6 12.5 Elongation at break / % >250 GB / T1043-2006 280 300 286 278 270 285 Thermal aging (80℃, 168h) tensile strength >10.0
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap