Oxygen carrier for chemical cycle dry gas reforming and its preparation method and application

A dry gas reforming and oxygen carrier technology, which is applied in chemical instruments and methods, inorganic chemistry, bulk chemical production, etc., can solve the problems of low cycle reactivity, reduced reactivity, high reaction temperature, etc., and achieve low cost, The effect of promoting the formation and improving the catalytic activity

Active Publication Date: 2017-10-31
NORTHWEST UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But Fe 2 o 3 Oxygen-like carrier and carrier Al 2 o 3 or SiO 2 Easy to form spinel or silicate structure resulting in reduced reactivity
In short, the currently developed oxygen carriers have shortcomings such as low oxygen loading rate, low cycle reactivity, and inability to withstand high reaction temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oxygen carrier for chemical cycle dry gas reforming and its preparation method and application
  • Oxygen carrier for chemical cycle dry gas reforming and its preparation method and application
  • Oxygen carrier for chemical cycle dry gas reforming and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Preparation of hexaaluminate (LaFe 3 Al 9 o 19 ) oxygen carrier. Proceed as follows:

[0044] 2.54 grams of lanthanum nitrate (La(NO 3 ) 2 ), 7.1 grams of iron nitrate (Fe(NO 3 ) 3 9H 2 O) and 19.78 grams of aluminum nitrate (Al(NO 3 ) 3 9H 2 O) were respectively dissolved in deionized water at 60° C. to form lanthanum nitrate solution, iron nitrate solution, and aluminum nitrate solution each at 1 mol / L. After mixing the lanthanum nitrate solution and the ferric nitrate solution evenly, use 0.1mol / L nitric acid to adjust the pH value to 1, then add the aluminum nitrate solution, after mixing evenly, a mixed solution is obtained, and quickly add the mixed solution to excess saturated ammonium carbonate In the solution, stir rapidly (stirring speed is 250r / min) at 60°C for 6 hours, filter to obtain precipitate, dry the precipitate at 120°C for 12 hours, then roast the precipitate, and then cool down to room temperature naturally. Wherein, the amount of ammoni...

Embodiment 2

[0049] Preparation of Ba 1-x La x FeAl 11 o 19 (x=0-1, step size is 0.2) hexaaluminate oxygen carrier, labeled B 1-x L x F (LF when x=1, BF when x=0), the Ba(NO 3 ) 2 , La(NO 3 ) 3 ·6H 2 O, Fe(NO 3 ) 3 9H 2 O and Al(NO 3 ) 3 9H 2 O was dissolved in deionized water at 60°C to form 1 mol / L Ba(NO 3 ) 2 solution, La(NO 3 ) 3 solution, Fe(NO 3 ) 3 solution, Al(NO 3 ) 3 solution. Ba(NO 3 ) 2 solution, La(NO 3 ) 3 solution, Fe(NO 3 ) 3 After the solution is mixed evenly, use 2mol / L nitric acid to adjust the pH value to 1, then add aluminum nitrate solution, after mixing evenly, a mixed solution is obtained, and the mixed solution is quickly added to an excess of 1mol / L saturated ammonium carbonate solution. After stirring vigorously at 60°C for 6 hours, filter the precipitate, wash the precipitate with deionized water for 3-5 times and dry at 120°C for 12 hours; grind, then transfer to a muffle furnace and bake at 500°C for 4 hours , and then baked at 12...

Embodiment 3

[0055] Preparation of LaFe x Al 12-x o 19 (x = 0-4, step size 1) hexaaluminate oxygen carrier, labeled LF x (When x=0, LFxA=LA). The molar ratio is 1:x:(12-x) La(NO 3 ) 3 ·6H 2 O, Fe(NO 3 ) 3 9H 2 O and Al(NO 3 ) 3 9H 2 O was respectively dissolved in deionized water at 60°C to form a 1mol / L solution. Mix lanthanum nitrate solution and ferric nitrate solution evenly, use 1mol / L nitric acid to adjust PH=1, then add aluminum nitrate solution, after mixing evenly, quickly add to excess saturated ammonium carbonate solution, at 60°C 400r / Stir vigorously for 6 hours; filter and separate, wash with deionized water for 3-5 times, and then dry at 120°C for 12 hours; mill, transfer to a muffle furnace and bake at 500°C for 4 hours, then heat up to 1100°C for 4 hours, Let it cool down to room temperature naturally. Wherein, the amount of ammonium carbonate in the saturated ammonium carbonate solution is 1.6 times of the required molar amount of ammonium carbonate when lan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

An oxygen carrier for dry gas reforming in chemical circulation and its preparation method and application, the oxygen carrier is a composite metal oxide with a hexaaluminate structure, the general formula is AMxAl12‑xO19, wherein A is rare earth metal lanthanum and / or barium, M is transition metal iron, 0<x<5. The temperature of the oxygen carrier in the fuel reactor is 750-1000 DEG C, the temperature in the oxidation reactor is 750-1000 DEG C, and the reaction pressure is normal pressure. The preparation process is: using ferric nitrate, aluminum nitrate, lanthanum nitrate and / or barium nitrate as precursors, preparing nitrate solution, adding ammonium carbonate as precipitant for co-precipitation, and then suction filtration, washing, drying and roasting. have to. The oxygen carrier has high oxygen loading rate and reactivity, and has the advantages of excellent impact resistance mechanical properties, high temperature stability, environmental friendliness, low cost and easy preparation.

Description

technical field [0001] The invention belongs to the technical field of catalysts in the field of chemical cycle dry gas reforming, and in particular relates to an oxygen carrier for chemical cycle dry gas reforming and its preparation method and application. Background technique [0002] At present and for a long time to come, the world's energy consumption structure will still be dominated by fossil energy such as coal, oil, and natural gas. Coal, oil, and natural gas as carbon-containing energy sources (C n h m O), whose utilization ends in CO 2 generation, while CO 2 As a major greenhouse gas, it has had a serious impact on global warming and environmental degradation. During the traditional direct combustion of fossil fuels, due to the N in the air 2 dilution, the CO in the flue gas produced 2 Only 10% to 14%, CO 2 The separation cost is higher. Combining new energy conversion principles with CO 2 The organic combination of enrichment process is undoubtedly a ve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/78B01J23/83C01B3/40
CPCY02P20/52
Inventor 朱燕燕马晓迅刘伟伟刘莹刘泽民
Owner NORTHWEST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com