A kind of sintered flux for submerged arc welding of x100 pipeline steel and preparation method thereof

A technology of sintering flux and submerged arc welding, applied in arc welding equipment, welding equipment, welding equipment, etc., can solve problems such as incomplete combustion, human health and environmental threats, and achieve the effect of improving low temperature impact toughness

Inactive Publication Date: 2017-10-31
上饶市荣昌焊接材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a flux for submerged arc welding of X100 pipeline steel and its preparation method, to solve the problem that the sintered flux containing halogen elements is prone to incomplete combustion during the welding process of X100 pipeline steel, and many toxic substances and acid or Corrosive gases, technical issues with potential threats to human health and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] A sintered flux for X100 pipeline steel submerged arc welding, the chemical composition of the flux includes: MgO45~50wt.%, Al 2 o 3 3~5wt.%, CaO5~8wt.%, SiO 2 5~8wt.%, MnO2~3wt.%, TiO 2 8~10wt.%, FeO3~5wt.%, ZrO 2 2~3wt.%, Na 2 O5~8wt.%, K 2 O3~4wt.%.

[0035] The sintered flux for submerged arc welding of X100 pipeline steel also includes: B 2 o 3 1.2wt.%.

[0036] The sintered flux for submerged arc welding of X100 pipeline steel also includes: a binder accounting for 5wt.% of the flux.

[0037] The sintered flux for submerged arc welding of X100 pipeline steel also includes: alloy agent: one or more of Si-Fe, Ti-Fe, Mn-Fe, adding Si-Fe alloy agent containing 60wt% silicon by weight 8 ~10wt.%, the weight of Ti-Fe alloy powder containing 45wt% titanium is 8~10wt.%, the weight of Mn-Fe containing 1wt% carbon and 60wt% manganese is 5~10wt.%.

[0038] The basicity B of the sintered flux for submerged arc welding of X100 pipeline steel Ⅱw is 1.8.

[0039] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention aims at providing sintering flux for submerged-arc welding of X100 pipeline steel and a preparation method for the sintering flux. By means of the sintering flux, the technical problem that many toxic substances and acid or corrosive gas produced due to incomplete combustion, which can easily occur during welding of the X100 pipeline steel, of the sintering flux containing halogen elements have potential threats to human health and the environment is solved. Meanwhile, the alkalinity is improved, so that the low-temperature impact toughness of weld metal is improved. Besides, the electrical conductivity during welding is enhanced, and the electrochemical corrosion resistant performance of welded joints is improved. The sintering flux comprises chemical components of, 45-55 wt.% of MgO, 3-5 wt.% of Al2O3, 5-10 wt.% of CaO, 5-8 wt.% of SiO2, 2-3 wt.% of MnO, 8-10 wt.% of TiO2, 3-5 wt.% of FeO, 2-3 wt.% of ZrO2, 5-10 wt.% of Na2O and 3-4 wt.% of K2O.

Description

technical field [0001] The invention belongs to the field of flux, and in particular relates to a sintered flux for submerged arc welding of X100 pipeline steel and a preparation method thereof. Background technique [0002] Medium-thick plates and coils used in the manufacture of oil, natural gas gathering and long-distance pipelines or coal, building material slurry pipelines, etc. are called pipeline steel (steel for pipeline). Generally, medium and thick plates are used to make thick-walled straight seam welded pipes, while coils are used to produce straight seam resistance welded pipes or submerged arc spiral welded pipes. The country has a production capacity of 700,000 t / a spiral welded pipes with a diameter within 1800mm, and has established a production line for straight seam thick-walled pipes with a diameter within 1600mm. It is only over 10 years in China that the pipeline steel that meets the pipeline engineering design requirements of the API5L standard can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/362B23K9/18B23K101/10B23K103/04
CPCB23K9/18B23K35/3602B23K35/362B23K2101/10B23K2103/04
Inventor 孙玉博
Owner 上饶市荣昌焊接材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products