Preparation method and application of water-based acrylate pressure-sensitive adhesive

A water-based acrylate and acrylate technology, applied in the field of pressure-sensitive adhesives, can solve problems such as wrinkles, small bubbles, and knife marks

Active Publication Date: 2016-01-06
HUBEI INST OF AEROSPACE CHEMOTECHNOLOGY
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] When the pressure-sensitive adhesives currently on the market are coated with transparent protective ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The water-based acrylate pressure-sensitive adhesive of the present invention is composed of component A and component B;

[0026] Component A is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0027] 33.6 parts of butyl acrylate, 0 parts of isooctyl acrylate, 2.18 parts of methyl methacrylate, 2 parts of butyl methacrylate, 0.2 parts of 2-hydroxypropyl acrylate, 1.2 parts of acrylic acid, containing two double bonds ( 0 part of meth)acrylate, 0.16 part of ammonium persulfate, 0.06 part of sodium bicarbonate, 0.4 part of nonylphenol polyoxyethylene (4) ammonium sulfate, 0.2 part of dimethylethanolamine, 60 parts of deionized water.

[0028] The concrete preparation steps of component A are:

[0029] (1) Weigh all the alkyl (meth)acrylate, 50% nonylphenol polyoxyethylene (4) ammonium sulfate, 40% ammonium persulfate and 30% deionized water, and add them to the emulsification kettle ...

Embodiment 2

[0037] The water-based acrylate pressure-sensitive adhesive of the present invention is composed of component A and component B;

[0038] Component A is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0039] 0 parts of butyl acrylate, 33.6 parts of isooctyl acrylate, 0.8 parts of methyl methacrylate, 2.6 parts of butyl methacrylate, 1.2 parts of 2-hydroxypropyl acrylate, 0.2 parts of acrylic acid, ethylene glycol dimethacrylate 0.3 parts of triethylene glycol dimethacrylate, 0.1 parts of triethylene glycol dimethacrylate, 0.4 parts of ammonium persulfate, 0.12 parts of sodium bicarbonate, 0.48 parts of sodium dodecyl diphenyl ether disulfonate, 0.2 parts of dimethylethanolamine, 60 parts of ionized water.

[0040] The concrete preparation steps of component A are:

[0041] (1) Weigh all the alkyl (meth)acrylate, 60% sodium dodecyl diphenyl ether disulfonate, 50% ammonium persulfate and 4...

Embodiment 3

[0050] The water-based acrylate pressure-sensitive adhesive of the present invention is composed of component A and component B;

[0051] Component A is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0052]17.2 parts of butyl acrylate, 27 parts of isooctyl acrylate, 4 parts of methyl methacrylate, 4 parts of butyl methacrylate, 0.8 parts of 2-hydroxypropyl acrylate, 0.8 parts of acrylic acid, 1,6-hexanediol 0.1 part of diacrylate, 0.4 part of ammonium persulfate, 0.16 part of sodium bicarbonate, 0.14 part of nonylphenol polyoxyethylene (4) ammonium sulfate, 0.2 part of sodium dodecyl diphenyl ether disulfonate, the concentration is 25% 0.2 parts of ammonia water and 45 parts of deionized water.

[0053] The concrete preparation steps of component A are:

[0054] (1) Weigh all the alkyl (meth)acrylate, 50% anionic emulsifier, 50% ammonium persulfate and 40% deionized water, put them into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a water-based acrylate pressure-sensitive adhesive, and an application of the adhesive in household appliance protective films. A component A of the pressure-sensitive adhesive is an alkyl (methyl) acrylate polymer, and a component B of the pressure-sensitive adhesive is a polyfunctional aziridine-series crosslinking agent. The component A is obtained through polymerization of butyl acrylate, isooctyl acrylate, methyl methacrylate, butyl methacrylate, 2-hydroxypropyl acrylate, acrylic acid and (methyl) acrylate containing two double bonds, wherein the polymerization is initiated by ammonium sulfate. The pressure-sensitive adhesive provided by the invention has the advantages of good leveling property, less foam, fisheye-free property in coating, and the like. When the adhesive is applied on a needed substrate to prepare a household appliance protective film, the protective film has good high-temperature resistance, good high-humidity resistance and good aging resistance. When the protective film is torn from the surface of a household appliance, no residual adhesive or spot is left.

Description

technical field [0001] The invention relates to a pressure-sensitive adhesive, which is a pressure-sensitive adhesive having the advantages of good leveling performance, less foam, small latex liquid particle size and the like. The pressure-sensitive adhesive can be used in fields that have high requirements on the appearance of the pressure-sensitive adhesive tape, such as the surface protective film of household appliances and the like. Background technique [0002] Due to its universality, low cost and other advantages, transparent protective film is used more and more widely. The high-grade transparent protective film has higher requirements on the glue, which requires the glue to have good leveling properties, less foam, and no small gel pieces. Home appliance protective film is its typical representative. [0003] With the improvement of people's living standards, various household appliances have gradually entered thousands of households, which has brought about the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J11/06C09J7/02C08F220/18C08F220/14C08F220/28
Inventor 何伟武鹏李胜华冯小平姜云刚
Owner HUBEI INST OF AEROSPACE CHEMOTECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap