Composite insulating material for coal mine cable

A composite insulation and cable technology, used in rubber insulators, organic insulators, plastic/resin/wax insulators, etc., can solve the problems of thermal oxygen aging, ozone aging resistance, low volume resistivity, and poor pressure resistance. , to achieve the effect of good water vapor resistance, high dielectric strength and good heat resistance

Inactive Publication Date: 2016-02-10
山东太平洋橡缆股份有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it can also be used as the main material of insulating materials. Using polyolefin elastomer (POE) alone as the main material of insulating materials has poor electrical propert

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: according to the raw materials involved in the active ingredients of the composite insulating material formula for coal mine cables and the proportioning by weight, get EPDM rubber, 50 parts, polyolefin elastomer, 50 parts, calcined kaolin, 60 parts, Zinc oxide, 6 parts, coupling agent A-172, 1.5 parts, paraffin wax, 2.5 parts, antioxidant, 4 parts, paraffin oil, 7 parts, polyethylene wax, 0.8 parts, stearic acid, 0.6 parts, vulcanizing agent, 4 parts. After mixing the obtained EPDM rubber and polyolefin elastomer, enter the internal mixer for mastication, masticate for 2-3 minutes, add zinc oxide, anti-aging agent, coupling agent, paraffin wax, stearic acid, polyethylene Wax is mixed, then calcined kaolin is added for mixing, then paraffin oil (added after the filler and reinforcing agent is fed) is added for mixing, and finally vulcanizing agent is added for mixing, and then enters the open mill to form a compound for coal mine cables. Insulation Materi...

Embodiment 2

[0023] Embodiment 2: according to the raw materials involved in the active ingredient of the composite insulation material formula for coal mine cables and the proportioning by weight, get EPDM rubber, 55 parts, polyolefin elastomer, 45 parts, calcined kaolin, 70 parts, Zinc oxide, 7 parts, coupling agent A-172, 2.2 parts, paraffin wax, 3.0 parts, antioxidant, 6 parts, paraffin oil, 8 parts, polyethylene wax, 0.6 parts, stearic acid, 0.8 parts, vulcanizing agent, 5.5 servings. After mixing the obtained EPDM rubber and polyolefin elastomer, enter the internal mixer for mastication, masticate for 2-3 minutes, add zinc oxide, anti-aging agent, coupling agent, paraffin wax, stearic acid, polyethylene Wax is mixed, then calcined kaolin is added for mixing, then paraffin oil (added after the filler and reinforcing agent is fed) is added for mixing, and finally vulcanizing agent is added for mixing, and then enters the open mill to form a compound for coal mine cables. Insulation Ma...

Embodiment 3

[0024] Embodiment 3: according to the raw materials involved in the active ingredient of the composite insulating material formula for coal mine cables and the proportioning by weight, get EPDM rubber, 45 parts, polyolefin elastomer, 55 parts, calcined kaolin, 65 parts, Zinc oxide, 8.5 parts, coupling agent A-172, 2.5 parts, paraffin wax, 3.8 parts, antioxidant, 8 parts, paraffin oil, 10 parts, polyethylene wax, 0.8 parts, stearic acid, 1 part, vulcanizing agent, 7.5 servings. After mixing the obtained EPDM rubber and polyolefin elastomer, enter the internal mixer for mastication, masticate for 2-3 minutes, add zinc oxide, anti-aging agent, coupling agent, paraffin wax, stearic acid, polyethylene Wax is mixed, then calcined kaolin is added for mixing, then paraffin oil (added after the filler and reinforcing agent is fed) is added for mixing, and finally vulcanizing agent is added for mixing, and then enters the open mill to form a compound for coal mine cables. Insulation Ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite insulating material for a coal mine cable. The composite insulating material is characterized by being prepared from, by weight, 40-60 parts of EPDM rubber, 40-60 parts of polyolefin elastomer, 60-90 parts of calcined kaolin, 5-10 parts of zinc oxide, 1-3 parts of coupling agent A-172, 2-4 parts of paraffin, 3-10 parts of anti-aging agent, 6-12 parts of paraffin oil, 0.5-1 part of polyethylene wax, 0.5-1 part of stearic acid and 2-10 parts of vulcanizing agents. The composite insulating material for the coal mine cable has the advantages of being good in ozone aging resistant performance and thermal oxygen aging resistant performance, high in elasticity, small in permanent deformation, high in tensile strength, good in calendering performance, low in cost and the like.

Description

technical field [0001] The invention relates to a cable insulating material, which belongs to the technical field of chemical industry, in particular to a composite insulating material for coal mine cables. Background technique [0002] At present, the insulating materials used in domestic coal mine cables are all made of EPDM rubber or polyolefin elastomer (POE) as the single main material. EPDM rubber is used as the main material of coal mine cable insulation, its performance characteristics: (1) high cost performance, raw rubber density is only 0.86 ~ 0.90kg / m 3 , is the commonly used rubber with the lightest raw rubber density; and it can be filled in large quantities to reduce the cost of the rubber compound. (2) Excellent aging resistance, weather resistance, ozone resistance, sunlight resistance, thermal oxygen resistance, water resistance, water vapor resistance, ultraviolet resistance, radiation resistance and other aging properties. (3) Excellent chemical resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L23/00C08L91/06C08L23/06C08K13/06C08K3/34C08K3/22C08K5/09C08K5/5425H01B3/28H01B3/44
CPCC08L23/00C08L23/16C08L2201/08C08L2203/202C08L2205/025C08L2205/035H01B3/28H01B3/441C08L91/06C08L23/06C08K13/06C08K3/346C08K2003/2296C08K5/09C08K5/5425
Inventor 李德强张云龙王义军高静童向坡
Owner 山东太平洋橡缆股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap