An activated emulsion for welding power lithium battery joints
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for welding power and lithium batteries, used in welding media, welding equipment, battery pack components, etc. It can solve problems such as easy and difficult welding, and achieve the effects of convenient feeding, moderate viscosity and excellent physical properties.
Active Publication Date: 2018-01-23
LICHUANG TAISHAN ELECTRONICS TECH
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But it is not an easy task to weld the joints well. Because there is a dense oxide film on the surface of aluminum, ordinary welding materials are difficult to weld, and it is also a problem that needs to be solved urgently in the production of battery joints.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0027] An activated emulsion for welding power lithium battery joints, the composition weight ratio includes: 20% paste, 80% active alloypowder,
[0028] Wherein, the composition weight proportion of described paste comprises: polyvinyl alcohol 5%, white oil 35%, active flux 60%,
[0029] The composition weight ratio of the active alloypowder includes: Si: 3%, Cu: 0.05%, Ag: 0.1%, Ga: 0.006%, Ge: 0.05%, impurities are less than 0.2%, and the balance is Al.
Embodiment 2
[0031] An activated emulsion for welding power lithium battery joints, the composition weight ratio includes: 25% paste, 75% active alloy powder,
[0032] Wherein, the composition weight ratio of the paste comprises: 10% methyl silicone oil, 35% white oil, 55% active brazing flux,
[0033] The composition weight ratio of the active alloy powder includes: Si: 20%, Zn: 0%, Cu: 0.1%, Ag: 0.1%, Ga: 0.02%, Ge: 0.1%, impurities are less than 0.2%, and the balance is Al.
Embodiment 3
[0035] An activated emulsion for welding power lithium battery joints, the composition weight ratio includes: 20% paste, 80% active alloy powder,
[0036] Wherein, the composition weight proportion of described paste comprises: polyethylene glycol 10%, propylene glycol 25%, active flux 65%,
[0037] The composition weight ratio of the active alloy powder includes: Si: 13%, Zn: 0%, Cu: 0.05%, Ag: 0.1%, Ga: 0.04%, Ge: 0.05%, impurities are less than 0.2%, and the balance is Al.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses an activated emulsion for welding power lithium battery joints. The composition weight ratio includes: 5%-50% of paste, 50%-95% of active alloypowder. Through the above method, the activated emulsion used for welding power lithium battery joints of the present invention has moderate viscosity, no tailing, convenient feeding, low welding temperature, excellent fluidity, no halides, no corrosion after welding, no residue and no moisture absorption, Welding has the advantages of excellent physical properties, remarkable thermal fatigue resistance, no oxidation, high electrical conductivity, and convenient welding use. It has broad market prospects in the popularization of activated emulsions for welding power lithium battery joints.
Description
technical field [0001] The invention relates to the field of emulsions, in particular to an activated emulsion used for welding power lithium battery joints. Background technique [0002] Earlier large buses or brand electric vehicles generally used lead-acid batteries as power sources, but lead-acid batteries have disadvantages such as low capacity density, heavy weight, single voltage, and environmental pollution that cannot be overcome. Lithium batteries are currently widely used in automotive power due to their advantages such as high terminal voltage, large specific energy, long charge and discharge life, stable discharge performance, low self-discharge rate, and no pollution to the environment. [0003] Automobile power batteries exist in the form of battery packs. In order to make these rechargeable batteries have sufficient battery capacity, the battery packs are connected by multiple lithium battery cells as the power source of the car, so the environment in which t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More