Violet ceramic pigment and preparation method thereof

A technology of ceramic pigment and violet, applied in the field of ceramic pigment, can solve problems such as poor stability and limited application scope, and achieve the effects of easy industrial production, simple production process and good stability

Inactive Publication Date: 2016-03-16
赖清甜
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is a shortcoming in the above patents, that is, the stability is not good under high temperature conditions, which limits its application range, and high temperature ceramics have irreplaceable unique effects in terms of material density and so on.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of violet ceramic pigment, the parts by weight of each component are:

[0023] 2 parts of tin dioxide, 0.3 parts of chromium oxide green, 0.5 parts of silicon dioxide, 10 parts of zinc oxide, 10 parts of citric acid, 1 part of chrome tin amethyst seed, 0.1 part of sodium fluorosilicate.

[0024] Its preparation method comprises the following steps:

[0025] Mix and stir the raw materials evenly to obtain a uniform mixture, then grind it thoroughly for 4 hours; calcinate the mixture at 500°C for 8 hours; after calcining, add the powder into pure water that is 20 times its weight, stir for 30 minutes, and then filter out the water , drying; the dried solid is ground by a ball mill and passed through a 350-mesh sieve to obtain a violet ceramic colorant.

Embodiment 2

[0027] A kind of violet ceramic pigment, the parts by weight of each component are:

[0028] 4 parts of tin dioxide, 0.5 parts of chromium oxide green, 0.65 parts of silicon dioxide, 15 parts of zinc oxide, 15 parts of citric acid, 3 parts of chromium tin amethyst seed, 0.25 parts of sodium fluorosilicate.

[0029] Its preparation method comprises the following steps:

[0030] Mix and stir the raw materials evenly to obtain a uniform mixture, then grind it thoroughly for 6 hours; calcinate the mixture at 550°C for 10 hours; after calcining, add the powder to 25 times its weight in pure water, stir for 60 minutes, and filter out the water , drying; the dried solid is ground by a ball mill and passed through a 400-mesh sieve to obtain a violet ceramic colorant.

Embodiment 3

[0032] A kind of violet ceramic pigment, the parts by weight of each component are:

[0033] 3 parts of tin dioxide, 0.5 parts of chromium oxide green, 65 parts of silicon dioxide, 15 parts of zinc oxide, 20 parts of citric acid, 3 parts of chrome tin amethyst seed, 0.5 part of sodium fluorosilicate.

[0034] Its preparation method comprises the following steps:

[0035] Mix and stir the raw materials evenly to obtain a uniform mixture, then grind it thoroughly for 5 hours; calcinate the mixture at 525°C for 9 hours; after calcining, add the powder into pure water whose weight is 22.5 times, stir for 45 minutes, and filter out the water , drying; the dried solid is ground by a ball mill and passed through a 375-mesh sieve to obtain a violet ceramic colorant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to violet ceramic pigment and a preparation method thereof, and belongs to the technical field of ceramic pigment preparation. The violet ceramic pigment comprises the following raw materials by weight: 1 to 5 parts of stannic oxide, 0.2 to 0.5 part of chromium oxide green, 0.5 to 0.8 part of silicon dioxide, 10 to 20 parts of zinc oxide, 10 to 20 parts of citric acid, 1 to 5 parts of chrome-tin amethyst, and 0.1 to 0.5 part of sodium fluorosilicate. The preparation method comprises the following steps: mixing the raw materials uniformly, stirring to obtain a uniform mixture, and carrying out sufficient grinding for 4 to 6 hours; calcining the mixture powder at 500 to 550 DEG C for 8 to 10 hours; adding the calcined powder into purified water which is 20 to 25 times of the calcined powder in weight, stirring 30 to 60 minutes, filtering to remove water, and drying; grinding the dried solid with a ball mill, and sieving with a 350 to 400-mesh screen, so as to obtain the violet ceramic pigment. The violet ceramic pigment is narrow in particle size distribution, stable in color generation, low in color difference variation, and high in stability under a high-temperature condition; moreover, the preparation process is simple, the equipment requirement is low, and industrial production is easy to realize.

Description

technical field [0001] The invention relates to a ceramic color material, in particular to a violet ceramic color material and a preparation method thereof, belonging to the technical field of ceramic color material preparation. Background technique [0002] Ceramics are various products made of natural clay and various natural minerals as the main raw materials through crushing, kneading, molding and calcination. Painted pottery, also known as ceramic painting, is an art in my country's long-standing "national quintessence" - ceramic art. Painted pottery is beautifully made, mainly clay pottery, the color is painted before firing, and the texture is fine, so it is not only a practical vessel, but also has high artistic value. [0003] Ceramic pigments, also known as pigments or color materials, are powdery decorative materials for colored ceramics formulated with color bases and fluxes or additives. Pigment = color base + flux, the color base is the chromogenic substance ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/85
Inventor 赖清甜
Owner 赖清甜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com