A release film and film layer technology, applied in the field of release film, can solve the problems of poor weather resistance of PVC film, affecting the scope of use, aging, etc., and achieve the effects of good compatibility, easy operation and strong adhesion

Inactive Publication Date: 2016-03-30
JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although PE has many advantages, the weather resistance of PVC film is poor, and it is more likely to age under the action of external environments such as light, heat, and oxygen, which affects its scope of use.
At the same time, the current release film has relatively single performance and is usually only used for isolation and filling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A PVC color-changing release film, comprising a film layer, the film layer comprises the following components in proportion by weight:

[0043] PVC: 80 copies;

[0044] PA: 10 copies;

[0045] EVA: 8 parts;

[0046] CPE resin: 8 parts;

[0047] PBT: 8 parts;

[0048] PET: 10 parts;

[0049] Polyethylene glycol monomethyl ether: 15 parts;

[0050] PTFE: 8 parts;

[0051] Polymethyl methacrylate: 8 parts;

[0052] Polyphenylene sulfide: 4 parts;

[0053] Fiberglass: 4 parts;

[0054] Organic montmorillonite: 4 parts;

[0055] Polyether ether ketone fiber: 2 parts;

[0056] Thermal red: 2 parts;

[0057] PVA: 4 parts;

[0058] Lauryl alcohol: 8 parts;

[0059] Chitosan: 2 parts;

[0060] Antioxidant 1010: 0.6 parts;

[0061] Light stabilizer 622: 0.6 parts;

[0062] Nano-TiO 2 : 0.8 parts;

[0063] PE-g-MAH: 0.6 parts;

[0064] Thickener: methyl hydroxyethyl cellulose: 0.3 parts;

[0065] Coupling agent: vinyl triperoxy tert-butylsilane: 0.8 parts.

Embodiment 2

[0067] A PVC color-changing release film, comprising a film layer, the film layer comprises the following components in proportion by weight:

[0068] PVC: 90 parts;

[0069] PA: 15 copies;

[0070] EVA: 9 parts;

[0071] CPE resin: 9 parts;

[0072] PBT: 9 parts;

[0073] PET: 11 parts;

[0074] Polyethylene glycol monomethyl ether: 18 parts;

[0075] PTFE: 9 parts;

[0076] Polymethyl methacrylate: 9 parts;

[0077] Polyphenylene sulfide: 5 parts;

[0078] Fiberglass: 5 parts;

[0079] Organic montmorillonite: 5 parts;

[0080] Polyether ether ketone fiber: 3 parts;

[0081] Thermal red: 2.5 parts;

[0082] PVA: 5 parts;

[0083] Dodecanol: 9 parts;

[0084] Chitosan: 3 parts;

[0085] Antioxidant 1010: 0.7 parts;

[0086] Light stabilizer 622: 0.7 parts;

[0087] Nano-TiO 2 : 1 copy;

[0088] PE-g-MAH: 0.7 parts;

[0089] Thickener: methyl hydroxyethyl cellulose: 0.4 parts;

[0090] Coupling agent: vinyl triperoxy tert-butylsilane: 0.9 parts.

Embodiment 3

[0092] A PVC color-changing release film, comprising a film layer, the film layer comprises the following components in proportion by weight:

[0093] PVC: 100 copies;

[0094] PA: 20 copies;

[0095] EVA: 10 parts;

[0096] CPE resin: 10 parts;

[0097] PBT: 10 parts;

[0098] PET: 12 copies;

[0099] Polyethylene glycol monomethyl ether: 20 parts;

[0100] PTFE: 10 parts;

[0101] Polymethyl methacrylate: 10 parts;

[0102] Polyphenylene sulfide: 6 parts;

[0103] Fiberglass: 6 parts;

[0104] Organic montmorillonite: 6 parts;

[0105] PEEK fiber: 4 parts;

[0106] Thermal red: 3 parts;

[0107] PVA: 6 parts;

[0108] Lauryl alcohol: 10 parts;

[0109] Chitosan: 4 parts;

[0110] Antioxidant 1010: 0.8 parts;

[0111] Light stabilizer 622: 0.8 parts;

[0112] Nano-TiO 2 : 1.2 parts;

[0113] PE-g-MAH: 0.8 parts;

[0114] Thickener: methyl hydroxyethyl cellulose: 0.5 parts;

[0115] Coupling agent: vinyl triperoxy tert-butylsilane: 1 part.

[0116] The org...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

A disclosed PVC color-variable release film comprises PVC, PA, EVA, CPE resin, PBT, PET, methoxy polyethylene glycol, PTFE, polymethyl methacrylate, polyphenylene sulfide, glass fiber, organic montmorillonite, poly(ether ether ketone) fiber, heat-sensitive red, PVA, dodecanol, chitosan, anti-oxidant 1010, light-stabilizing agent 622, nanometer TiO2, PE-g-MAH, a thickening agent and a coupling agent. The release film possesses extremely excellent waterproofness, corrosion resistance, temperature tolerance, weatherability and binding property, also can change color after being heated, and possesses heat-dissipation energy-storage effects.

Description

technical field [0001] The invention relates to a release film, in particular to a PVC discoloration release film. Background technique [0002] Release film, also known as peeling film, isolation film, separation film, barrier film, release film, film, plastic film, hole masking film, silicone oil film, silicone oil paper, anti-adhesive film, slip film, Tianna paper, release film Paper, silliconfilm, release film, release. Usually, in order to increase the release force of the plastic film, the plastic film will be treated with plasma, or coated with fluorine, or coated with silicon (silicone) release agent on the surface of the film material, such as PET, PE, OPP, etc. ;It can show extremely light and stable release force for various organic pressure-sensitive adhesives (such as hot-melt adhesives, acrylic adhesives and rubber-based pressure-sensitive adhesives). [0003] Because the release film has the advantages of isolation, filling, protection, and easy peeling, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/08C08L23/28C08L77/00C08L67/02C08L33/12C08L61/16C08K13/06C08K9/04C08K3/34C08K7/14C08K3/22
CPCC08L27/06C08K2201/011C08L2201/08C08L2203/16C08L2205/02C08L2205/025C08L2205/035C08L2205/16
Inventor 於险峰
Owner JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka