Corrosion-resistant milling cutter

A corrosion-resistant and milling cutter technology, applied in the field of corrosion-resistant milling cutters, can solve the problems of high tool cost, weakened edge strength, reduced heat dissipation capacity, etc., and achieves high strength, improved mechanical properties, and simple manufacturing processes.

Inactive Publication Date: 2016-04-27
刘辉
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the cutting force of rough machining, semi-finishing machining and finishing machining is very different, when the rake angle and rear angle of the tool are too larg

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of corrosion-resistant milling cutter, it is characterized in that milling cutter is made of steel-bonded hard alloy, steel-bonded hard alloy raw material powder comprises hard phase and steel-based binder, and hard phase (weight) is made of tungsten boride 70 parts , 50 parts of silicon carbide, 20 parts of nickel oxide, 3 parts of cerium nitride, and 50 parts of Cr; steel-based binder (weight) consists of C0.03%, Bi1%, Sn4%, Cr0.3%, Ca0.1% , Ag0.05%, Y0.03%, Mg0.02%, Sc0.02%, the balance is composed of Fe; the weight ratio of hard phase and steel-based binder is 0.9,

[0030] Steel-bonded cemented carbide is prepared by powder mixing, pressing and sintering, heating forging, annealing, machining, quenching and tempering:

[0031] Among them, in the powder mixing process: Weigh tungsten boride, silicon carbide, nickel oxide, cerium nitride, and Cr powder and mix according to the above ratio, and carry out ball mill alloying according to the ball-to-material rati...

Embodiment 2

[0037]A kind of corrosion-resistant milling cutter, it is characterized in that milling cutter is made of steel-bonded hard alloy, steel-bonded hard alloy raw material powder comprises hard phase and steel-based binder, and hard phase (weight) is made of tungsten boride 80 parts , 60 parts of silicon carbide, 30 parts of nickel oxide, 3 parts of cerium nitride, and 50 parts of Cr; steel-based binder (weight) consists of C0.04%, Bi2%, Sn5%, Cr0.4%, Ca0.2% , Ag0.06%, Y0.04%, Mg0.03%, Sc0.03%, the balance is composed of Fe; the weight ratio of hard phase and steel-based binder is 0.9,

[0038] Steel-bonded cemented carbide is prepared by powder mixing, pressing and sintering, heating forging, annealing, machining, quenching and tempering:

[0039] Among them, in the powder mixing process: Weigh tungsten boride, silicon carbide, nickel oxide, cerium nitride, and Cr powder and mix according to the above ratio, and carry out ball mill alloying according to the ball-to-material ratio...

Embodiment 3

[0045] A corrosion-resistant milling cutter is characterized in that the milling cutter is made of steel bonded carbide, the steel bonded carbide raw material powder includes a hard phase and a steel-based binder, and the hard phase (weight) consists of 75 parts of tungsten boride , 55 parts of silicon carbide, 25 parts of nickel oxide, 3 parts of cerium nitride, and 50 parts of Cr; the steel-based binder (weight) consists of C0.035%, Bi1.5%, Sn4.5%, Cr0.35%, Ca0.15%, Ag0.055%, Y0.035%, Mg0.025%, Sc0.025%, the rest is composed of Fe; the weight ratio of hard phase and steel-based binder is 0.9,

[0046] Steel-bonded cemented carbide is prepared by powder mixing, pressing and sintering, heating forging, annealing, machining, quenching and tempering:

[0047] Among them, in the powder mixing process: Weigh tungsten boride, silicon carbide, nickel oxide, cerium nitride, and Cr powder and mix according to the above ratio, and carry out ball mill alloying according to the ball-to-m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a corrosion-resistant milling cutter. The corrosion-resistant milling cutter is characterized by being made of a steel bond hard alloy, wherein the steel bond hard alloy powder comprises a hard phase and a steel-based binder. According to the milling cutter disclosed by the invention, the hard phase consists of tungsten boride, silicon carbide, nickel oxide, cerium oxide and Cr, so that the mechanical property of the material is improved; and the components of the steel-based binder have relatively high strength, so that the strength of the steel bond hard alloy is further improved under the action of the hard phase.

Description

technical field [0001] The invention relates to a corrosion-resistant milling cutter, which belongs to the technical field of cutting tools. Background technique [0002] In metal cutting, reasonable selection of tool edge shape (helix angle, rake angle, relief angle, edge inclination angle) is an important condition for giving full play to tool processing performance. Reasonable selection of tool edge shape can improve tool life and achieve high-speed machining. Because the cutting force of rough machining, semi-finishing machining and finishing machining is very different, when the rake angle and rear angle of the tool are too large during rough machining, it will weaken the strength of the blade and reduce the heat dissipation capacity, but the service life will be reduced, so that the tool Costs remain high. Contents of the invention [0003] A corrosion-resistant milling cutter is characterized in that the milling cutter is made of steel bonded carbide, the steel bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C29/00C22C1/05C22F1/00
CPCC22C29/00C22C1/05C22F1/00C22F1/002
Inventor 刘辉
Owner 刘辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap