Fabric back lining heat insulation coating

A heat insulation and coating technology for backing, applied in textiles and papermaking, biochemical fiber treatment, fiber treatment, etc., can solve the problems of poor water resistance, short service life, acid and alkali resistance, etc., and achieve sag resistance and storage stability Good performance and long service life

Inactive Publication Date: 2016-04-27
SUZHOU YUXI NEW MATERIAL TECH
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention aims at the technical problems of the existing fabric backing coatings with poor mildew resistance, short service life, acid and alkali resistance, poor flame retardant effect and poor water resistance, and provides a fabric backing thermal insulation coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Weigh 100 parts of deionized water, 30 parts of styrene-acrylic emulsion, 2 parts of talcum powder, 8 parts of light calcium carbonate, 4 parts of ammonia water, 30 parts of polyvinyl chloride, 3 parts of zinc oxide, N-benzene 1 part of base-1-naphthylamine, 5 parts of soft soap, 0.4 part of rubber scarlet, 1.5 parts of ammonium sulfate, 20 parts of calcium bicarbonate, 2 parts of sodium polyacrylate, and 1 part of zinc dimethyl dithiocarbamate.

[0019] Put ammonia water, active agent, foaming agent, coagulant and deionized water into the reaction kettle equipped with stirrer, thermometer and reflux condenser, rotate at 50r / min, and stir for 10min. Then add thickener, styrene-acrylic emulsion, light calcium carbonate and polyvinyl chloride, remove the air in the reactor, heat up to 65°C while stirring, and keep it warm for 1h; add the remaining raw materials, heat up to 80°C and stir evenly, then cool. Grind on a sand mill to a fineness of 10 μm, and filter to obtain t...

Embodiment 2

[0022] Weigh 100 parts of deionized water, 50 parts of styrene-acrylic emulsion, 8 parts of talcum powder, 12 parts of light calcium carbonate, 8 parts of ammonia water, 50 parts of polyvinyl chloride, 7 parts of zinc oxide, N-benzene 5 parts of base-1-naphthylamine, 25 parts of soft soap, 0.8 parts of rubber scarlet, 3.5 parts of ammonium sulfate, 40 parts of calcium bicarbonate, 8 parts of sodium polyacrylate, and 5 parts of zinc dimethyl dithiocarbamate.

[0023] Put ammonia water, active agent, foaming agent, coagulant and deionized water into the reaction kettle equipped with stirrer, thermometer and reflux condenser, rotate at 50r / min, and stir for 30min. Then add thickener, styrene-acrylic emulsion, light calcium carbonate and polyvinyl chloride, remove the air in the reactor, heat up to 75°C while stirring, and keep warm for 3h; add the remaining raw materials, heat up to 90°C and stir evenly, then cool down. Grind on a sand mill to a fineness of 20 μm, and filter to o...

Embodiment 3

[0026] Weigh 100 parts of deionized water, 35 parts of styrene-acrylic emulsion, 3 parts of talcum powder, 9 parts of light calcium carbonate, 5 parts of ammonia water, 35 parts of polyvinyl chloride, 4 parts of zinc oxide, N-benzene 2 parts of base-1-naphthylamine, 10 parts of soft soap, 0.5 parts of rubber scarlet, 2 parts of ammonium sulfate, 25 parts of calcium bicarbonate, 4 parts of sodium polyacrylate, and 2 parts of zinc dimethyl dithiocarbamate.

[0027] Put ammonia water, active agent, foaming agent, coagulant and deionized water into the reaction kettle equipped with stirrer, thermometer and reflux condenser, rotate at 50r / min, and stir for 10min. Then add thickener, styrene-acrylic emulsion, light calcium carbonate and polyvinyl chloride, remove the air in the reactor, heat up to 65°C while stirring, and keep it warm for 1h; add the remaining raw materials, heat up to 80°C and stir evenly, then cool. Grind on a sand mill to a fineness of 10 μm, and filter to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tack-free timeaaaaaaaaaa
flame retardantaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fabric back lining heat insulation coating. Raw materials of the fabric back lining heat insulation coating comprise deionized water, a styrene acrylic emulsion, talcum powder, light calcium carbonate, ammonia water, polyvinyl chloride, an activator, an antioxidant, a foaming agent, a coloring agent, a coagulating agent, a filler, a thickener and zinc dimethyldithiocarbamate. The surface drying time of the above product is 10-30min, and the hard drying time of the product is 50-90min; the fire resistance time is 30-60s, and the fire resistance weight loss is 2-4g; the adhesion is 98-100%, the impact strength is 60-70cm, the levelability is extremely good, and a coating film can resist saturated calcium hydrate immersion for 10-20d; the coating film does not shed or mildew after being immersed in water for 20-30d; the gloss is 96-100%, the flexibility is 1-5mm, and the service life of the coating film is long; and the sagging resistance and the storage stability of the product are good.

Description

technical field [0001] The present application relates to a paint, in particular to a fabric-backed thermal insulation paint. Background technique [0002] Most of the existing heat-insulating coating products are used on the surface of concrete or metal structures to achieve heat-insulating effect. The flexibility, compactness and adhesion of this type of heat-insulating coating are generally poor, so it is not suitable to be painted on textiles for heat insulation. insulation. But along with the wide application of outdoor textiles and sunshade curtains, people's requirements for the thermal insulation performance of textiles are also getting higher and higher. Therefore, it is very necessary to design a fabric-backed thermal insulation coating with high bonding strength, fast drying, high tensile strength, high elongation at break and long flame-resistant time and its preparation method to meet market demand. Contents of the invention [0003] Technical issues solved:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/60D06M11/76D06M11/79D06M13/425D06M15/233D06M15/248D06M15/263
CPCD06M15/263D06M11/60D06M11/76D06M11/79D06M13/425D06M15/233D06M15/248D06M16/00D06M2200/12D06M2200/30
Inventor 左士祥杨阳
Owner SUZHOU YUXI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com