Anti-reflection abrasion-resistant mobile phone cover plate capable of filtering out blue light and preparation method thereof

A technology for filtering blue light and mobile phone covers, which is used in devices for coating liquids on the surface, ion implantation plating, coatings, etc.

Inactive Publication Date: 2016-05-04
OURLOOK ZHANGZHOU OPTICAL TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, mobile phone screen covers have appeared in the prior art, and mobile phone screen covers can filter part of the harmful light, but the existing mobile phone covers lack the function of anti-reflection during use. In the cold winter, people carry mobile phones from When the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-reflection abrasion-resistant mobile phone cover plate capable of filtering out blue light and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Embodiment 1, a preparation method of a wear-resistant mobile phone cover plate for filtering blue light and anti-reflection, when the substrate is formed by resin, the preparation method specifically includes the following steps:

[0069] 1) Clean the outer surface of the substrate;

[0070] 2) Coating the outer surface of the substrate;

[0071] A. Coating the first film layer:

[0072] Adjust the vacuum degree in the vacuum coating chamber to less than or equal to 5.0×10 -3 Pa, and control the temperature in the vacuum coating chamber to 50-70°C, and use an electron gun to bombard the film material of the first film layer. The film material of the first film layer evaporates and deposits on the outer surface of the substrate in the form of nano-scale molecules. The rate of evaporation of the first film layer is 2.5? / S, and the thickness after the final formation of the first film layer is 10-100nm; Wherein, the film material of the first film layer is trititanium p...

Embodiment 2

[0090] Embodiment 2, a preparation method of a wear-resistant mobile phone cover plate for filtering blue light and anti-reflection, when the substrate is formed from glass, the preparation method specifically includes the following steps:

[0091] 1) Clean the outer surface of the substrate;

[0092] 2) Coating the outer surface of the substrate;

[0093] A. Coating the first film layer:

[0094] Adjust the vacuum degree in the vacuum coating chamber to less than or equal to 5.0×10 -3 Pa, and control the temperature in the vacuum coating chamber to 200-300°C, use an electron gun to bombard the film material of the first film layer, and the film material of the first film layer evaporates and deposits on the outer surface of the substrate in the form of nano-scale molecules. The rate of evaporation of the first film layer is 2.5? / S, and the thickness after the final formation of the first film layer is 10-100nm; Wherein, the film material of the first film layer is trititani...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Adhesionaaaaaaaaaa
Adhesionaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of mobile phone cover plates, in particular to an anti-reflection abrasion-resistant mobile phone cover plate capable of filtering out blue light and a preparation method thereof. The mobile phone cover plate comprises a substrate. The outer surface of the substrate is sequentially provided with a first film layer, a second film layer, a third film layer, a fourth film layer, a fifth film layer, a sixth film layer, a seventh film layer, an eighth film layer and a ninth film layer from inside to outside. The first film layer, the third film layer and the fifth film layer are all trititanium pentoxide layers, and the thicknesses of the first film layer, the third film layer and the fifth film layer are all 10-100 nm. The second film layer, the fourth film layer and the sixth film layer are all silicon dioxide layers, and the thicknesses of the second film layer, the fourth film layer and the sixth film layer are all 50-100 nm. The seventh film layer is a metal layer, and the thickness of the seventh film layer is 5-20 nm. The eighth film layer is a high-hardness layer, and the thickness of the eighth layer is 10-50 nm. The ninth film layer is an acrylic acid layer, and the thickness of the ninth film layer is 5-15 nm. The manufacturing method includes the following steps that firstly, the substrate is cleaned; secondly, the outer surface of the substrate is coated with films; and thirdly, the inner surface of the substrate is coated with films. The mobile phone cover plate can filter out harmful blue light and dazzle light, and abrasion resistance and anti-reflection performance can be improved.

Description

technical field [0001] The invention relates to the technical field of a mobile phone cover, in particular to a wear-resistant mobile phone cover for filtering blue light and antireflection and a preparation method thereof. Background technique [0002] With the widespread use of mobile phones in modern life, and people's lives are becoming more and more inseparable from mobile phones, many people often use mobile phones as a result of uncomfortable symptoms such as sore eyes, pain, tears, and more serious symptoms. Vision loss, these uncomfortable symptoms are caused by the harmful light emitted by the eyes on the mobile phone screen for a long time. The light emitted by the mobile phone screen is the enemy of the eyes. Color contrast and saturation will increase the brightness of the light behind the phone screen, which will make the surface of the screen appear textured like a piece of glass and improve clarity. It will also reflect light like glass, but the light shines ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/30C23C14/08C23C14/10C23C14/18B05D5/06B05D7/24
CPCB05D5/06B05D7/24B05D2502/00C23C14/083C23C14/10C23C14/18C23C14/30B05D2401/20
Inventor 吴晓彤方俊勇
Owner OURLOOK ZHANGZHOU OPTICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap