High-fluidity clay green molding sand used for steel casting and preparation method thereof

A high fluidity, steel casting technology, applied in casting molding equipment, casting molds, cores, etc., can solve problems such as poor fluidity and affecting the quality of steel castings, increase heat resistance, and ensure comprehensive performance and quality Stability, effect of improving surface quality

Inactive Publication Date: 2016-05-11
安徽创奇乐智能游乐设备有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the continuous development of casting technology, the performance requirements for molding sand are getting higher and higher. At present, the molding sand used for steel castings in the market has the disadvantage of poor fluidity, which affects the quality of steel castings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high fluidity clay green sand for steel castings, made of the following raw materials in weight (kg): zircon sand 35, chromium slag 26, petroleum coke powder 14, rectorite 23, waste molasses 7, vermiculite 20 , pearl clay 41, white jade 12, spinel 8, superfine aluminum silicate 9, tricalcium phosphate 8, improver 360;

[0014] The preparation method of the modifier is as follows: a. Take the following raw materials by weight (kg): polyvinylpyrrolidone 15, polyvinyl alcohol 13, sodium tripolyphosphate 5, corn starch 16, guar gum 13, acrylic acid 34, acrylic acid Amide 31, soybean oil 7, Span 801.5, ammonium persulfate 0.15, sodium bisulfite 0.06; b. Mix cornstarch and guar gum evenly, add water equivalent to 2.5 times the amount of the mixture, and heat in a water bath to 80°C. Stir for 30 minutes, cool down to 55°C, add soybean oil and Span 80, stir for 15 minutes, and set aside; c. Mix polyvinylpyrrolidone, polyvinyl alcohol, and sodium tripolyphosphate evenly, and a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wet compressive strengthaaaaaaaaaa
strengthaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-fluidity clay green molding sand used for a steel casting and a preparation method thereof. The high-fluidity clay green molding sand is made from, by weight, 25-40 parts of zircon sand, 18-32 parts of chromite residues, 11-19 parts of petrol coke powder, 14-26 parts of rectorite, 5-10 parts of waste molasses, 15-25 parts of vermiculite, 33-47 parts of nacrite, 9-18 parts of white onxy, 5-10 parts of spinel, 7-11 parts of ultra-fine aluminum silicate, 5-10 parts of tricalcium phosphate and 320-380 parts of improver. According to the high-fluidity clay green molding sand used for the steel casting and the preparation method thereof, the zircon sand and the nacrite are adopted as the main ingredients, and the chromite residues, the petrol coke powder, the rectorite, the white onxy, the spinel and other raw materials are added, so that the prepared clay green molding sand is made to have excellent fluidity; sand grains can easily move towards one another under the action of external force or gravity; the high-fluidity clay green molding sand further has good plasticity, gas permeability, collapsibility and heat stability.

Description

technical field [0001] The invention relates to high fluidity clay green molding sand for steel castings and a preparation method thereof, belonging to the technical field of molding sand. Background technique [0002] Sand casting is the most common casting method, and molding sand is the most important molding material in the current molding process. Molding sand is generally made by mixing molding materials such as raw sand for casting, molding sand binder and auxiliary additives in a certain proportion. Castings produced with sand molds account for more than 80% of the total casting production. The quality of molding sand directly affects the appearance quality of castings and casting defects such as sand holes, pores, and sand inclusions. With the continuous development of casting technology, the performance requirements for molding sand are getting higher and higher. Currently, the molding sand used for steel castings in the market has the disadvantage of poor fluidi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/02B22C1/00
CPCB22C1/02B22C1/00
Inventor 张庆
Owner 安徽创奇乐智能游乐设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products