Method for preparing silicon oxide nanofiber

A nanofiber and silicon oxide technology, applied in the field of nanomaterials, can solve the problems of many nanowire products, poor flexibility, high synthesis temperature, etc., and achieve good product reproducibility, convenient and efficient preparation method, and high purity Effect

Inactive Publication Date: 2016-05-25
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high synthesis temperature, there are often more defects in the nanowire product and poor flexibility.
So far, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing silicon oxide nanofiber
  • Method for preparing silicon oxide nanofiber
  • Method for preparing silicon oxide nanofiber

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] Weigh 3.75 grams of SiO with a mass fraction of 30% 2 Silica sol (alkaline), add 37.5 ml of distilled water. After stirring and ultrasonically dispersed uniformly, 15.14 grams of Fe (NO 3 ) 3 .9H 2 O (ferric nitrate nonahydrate) was added to the silica sol aqueous solution and stirred for 15 minutes until the ferric nitrate was completely dissolved.

[0032] Subsequently, the above solution was slowly added dropwise to a flask containing 60 ml of ethylenediamine liquid, and magnetic stirring (500 rpm) was performed during the dropwise addition. After the dropwise addition of the solution was completed, the emulsion was stirred for 15 hours to fully mix the system to obtain a mixed solution.

[0033] The above mixed solution was transferred into a 150-milliliter polytetrafluoroethylene-lined stainless steel reaction kettle, and after being sealed, it was left to stand in an oven at 180 degrees Celsius for 4 days to conduct a hydrothermal reaction....

Example Embodiment

[0040] Example 2

[0041] Weigh 3.75 g of 30% alkaline SiO 2 Silica sol, add 37.5 ml of distilled water. After stirring and ultrasonically dispersed uniformly, weigh 6.36 grams of AgNO 3 (Silver nitrate) was added to the silica sol aqueous solution and stirred for 20 minutes until the silver nitrate was completely dissolved.

[0042] Subsequently, the above solution was slowly added dropwise to a flask containing 60 ml of ethylenediamine liquid, and magnetic stirring (500 rpm) was performed during the dropwise addition. After the dropwise addition of the solution was completed, the emulsion was stirred for 12 hours to fully mix the system to obtain a mixed solution.

[0043] The above mixed solution was transferred into a 150-milliliter polytetrafluoroethylene-lined stainless steel reaction kettle, and after being sealed, it was left standing in an oven at 170 degrees Celsius for 4 days.

[0044] After the reaction was completed, the autoclave was taken out and cooled to r...

Example Embodiment

[0047] Example 3

[0048] Weigh 15 grams of 30% alkaline SiO 2 Silica sol, add 150 ml of distilled water. After stirring and ultrasonically dispersed uniformly, 30 grams of Fe (NO 3 ) 3 .9H 2 O (ferric nitrate nonahydrate) was added to the silica sol aqueous solution and stirred for 30 minutes until the silver nitrate was completely dissolved.

[0049] Subsequently, the above solution was slowly added dropwise to a flask containing 240 ml of ethylenediamine liquid, and magnetic stirring (500 rpm) was performed during the dropwise addition. After the dropwise addition of the solution was completed, the emulsion was stirred for 15 hours to fully mix the system to obtain a mixed solution.

[0050] The above mixed solution was transferred into a 1 liter 1Cr18Ni9Ti specification high temperature and high pressure stainless steel reaction kettle, the pressure in the kettle was maintained at 2MPa, and the reaction was carried out at a temperature of 170 degrees Celsius for 3 day...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing silicon oxide nanofiber. The method comprises the following steps of mixing silica sol with a nitrate solution, performing ultrasonic dispersion on the solution, adding ethylenediamine after the dissolution of the nitrate solution, and stirring uniformly to obtain a mixed solution; putting the mixed solution into a stainless steel reaction kettle with a polytetrafluoroethylene liner, standing the reaction kettle in a high-temperature baking oven after the closing of the reaction kettle, and performing a hydrothermal reaction; taking out the reaction kettle and cooling the reaction kettle to room temperature after the completion of the reaction, collecting precipitates in the reaction kettle, and washing the precipitates to obtain a silicon oxide nanofiber crude product; adding the silicon oxide nanofiber crude product into a hydrochloric acid solution, stirring in a thermostatic water bath, removing impurity components from the silicon oxide nanofiber crude product, and performing centrifugal separation to obtain a silicon oxide nanofiber finished product. The method disclosed by the invention has the advantages that not only can the high energy consumption in a nanofiber preparation process through a traditional chemical vapor deposition and thermal evaporation technology be avoided, but also the production is easily expanded by utilization of a hydrothermal synthesis technology.

Description

technical field [0001] The invention belongs to the technical field of nanometer materials, and in particular relates to a method for preparing bendable silicon oxide nanofibers with high flexibility and flame retardant properties. Background technique [0002] In the automation and intelligence process of oil and gas storage and transportation and oil field development, the development of fiber optic sensors has become a hot spot in the current dynamic monitoring work. However, optical fibers have poor mechanical properties. The core part is high refractive index silica glass fiber, the mechanical strength is only about 0.2GPa, and it is fragile. Due to transportation problems and human negligence of installation operators, most optical fibers cannot be used normally at the initial stage of installation. Therefore, it greatly limits the large-scale promotion of this technology in oil field enterprises. While ensuring mechanical strength, developing a silica fiber materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B33/12B82Y30/00B82Y40/00
CPCC01B33/12B82Y30/00B82Y40/00C01P2002/72C01P2004/03C01P2004/04C01P2004/16C01P2004/61
Inventor 赵宇鑫张卫华陶彬单晓雯甄永乾贾光
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap