Fireproof high-strength plastic floor material and preparation method thereof

A plastic floor, high-strength technology, applied in the field of polymer materials, can solve the problems of easy sag, limited pressure on the surface of the plastic floor, not fire resistance, etc., to achieve the effect of improving service life and customer satisfaction

Active Publication Date: 2016-05-25
郑州峰泰纳米材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with ordinary floors, although plastic flooring has the advantages of green recyclability, light weight, corrosion resistance, mildew resistance, insect resistance, and simple construction, there are still serious defects in plastic flooring: it is not fire-resistant and is easily damaged. Cigarette butts are scalded; secondly, the pressure that the surface of the plastic floor can withstand is limited, and it is easy to produce depressions. In addition, the plastic floor is not resistant to friction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The fireproof high-strength plastic floor material of this embodiment comprises the following components by weight: 50 parts of chlorohydrin rubber, 21 parts of silicone resin, 6 parts of zirconia ceramic micropowder, 8 parts of urea aldehyde melamine resin, 4 parts of zinc powder, magnesium silicate 3 parts, 3 parts of sepiolite powder, 2 parts of antimony trioxide, 3 parts of propylene oxide propyl ether, 2 parts of phenyl petroleum sulfonate, 4 parts of dicumyl di-tert-butyl peroxide, phthalate 4 parts of dioctyl diformate, 3 parts of terpene resin, 1 part of coupling agent and 1 part of anti-aging agent.

[0021] Wherein, the coupling agent is aminoethylaminopropyltrimethoxysilane.

[0022] The anti-aging agent is anti-aging agent 4010.

[0023] The preparation method of the fireproof high-strength plastic floor material of the present embodiment adopts the following preparation steps:

[0024] S1: Weigh each component by weight;

[0025] S2: adding zinc powder, ...

Embodiment 2

[0029] The fireproof high-strength plastic floor material of this embodiment comprises the following components by weight: 70 parts of chlorohydrin rubber, 33 parts of silicone resin, 13 parts of zirconia ceramic micropowder, 17 parts of urea melamine resin, 9 parts of zinc powder, magnesium silicate 10 parts, 8 parts of sepiolite powder, 6 parts of antimony trioxide, 9 parts of propylene oxide propyl ether, 7 parts of phenyl petroleum sulfonate, 10 parts of dicumyl di-tert-butyl peroxide, phthalate 11 parts of dioctyl diformate, 8 parts of terpene resin, 4 parts of coupling agent and 5 parts of anti-aging agent.

[0030] Wherein, the coupling agent is isopropyl 4-aminobenzenesulfonyl bis(dodecylphenylsulfonyl) titanate.

[0031] The anti-aging agent is anti-aging agent MB.

[0032] The preparation method of the fireproof high-strength plastic floor material of the present embodiment adopts the following preparation steps:

[0033] S1: Weigh each component by weight;

[003...

Embodiment 3

[0038] The fire-resistant high-strength plastic floor material of this embodiment comprises the following components by weight: 60 parts of chlorohydrin rubber, 27 parts of silicone resin, 10 parts of zirconia ceramic micropowder, 12 parts of urea aldehyde melamine resin, 6 parts of zinc powder, magnesium silicate 7 parts, 5 parts of sepiolite powder, 4 parts of antimony trioxide, 6 parts of propylene oxide propyl ether, 4 parts of phenyl petroleum sulfonate, 7 parts of dicumyl di-tert-butyl peroxide, o-phthalic acid 7 parts of dioctyl diformate, 5 parts of terpene resin, 2 parts of coupling agent and 3 parts of anti-aging agent.

[0039] Wherein, the coupling agent is aminoethylaminopropyltrimethoxysilane.

[0040] The anti-aging agent is anti-aging agent 1010.

[0041] The preparation method of the fireproof high-strength plastic floor material of the present embodiment adopts the following preparation steps:

[0042] S1: Weigh each component by weight;

[0043] S2: Add z...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fireproof high-strength plastic floor material. The fireproof high-strength plastic floor material comprises, by weight, 50-70 parts of chlorohydrine rubber, 21-33 parts of silicon resin, 6-13 parts of ultrafine zirconia ceramic powder, 8-17 parts of urea formaldehyde melamine resin, 4-9 parts of zinc powder, 3-10 parts of magnesium silicate, 3-8 parts of sea-foam stone powder, 2-6 parts of antimony trioxide, 3-9 parts of triglycidyl propyl ether, 2-7 parts of phenyl petroleum sulfonate, 4-10 parts of di(tert-butylperoxyisopropyl)benzene, 4-11 parts of dioctyl phthalate, 3-8 parts of terpene resin, 1-4 parts of coupling agent and 1-5 parts of anti-aging agent. The invention further discloses a preparation method of the fireproof high-strength plastic floor material. The prepared fireproof high-strength plastic floor material has the advantages that a hardness value ranges from 51 to 58, abradability is 21.5-25.31/cm<2>, flame retardant rating is I, and various performance indexes meet practical application requirements, so that the service life of the plastic floor material can be prolonged and customer satisfaction can be improved.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a fireproof high-strength plastic floor material and a preparation method thereof. Background technique [0002] Plastic flooring is a relatively new flooring material in the world's building materials industry. Plastic flooring has many styles and simple and quick construction. Nowadays, plastic flooring has been more and more widely used in daily life, such as in shopping malls, airports, hospitals, factories and other occasions, and the amount of use is increasing day by day. However, compared with ordinary floors, although plastic flooring has the advantages of green recyclability, light weight, corrosion resistance, mildew resistance, insect resistance, and simple construction, there are still serious defects in plastic flooring: it is not fire-resistant and is easily damaged. Cigarette butts are scalded; secondly, the pressure that the surface of the plastic floo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/03C08L83/04C08L61/28C08L45/00C08K13/02C08K3/22C08K3/34C08K3/08C08K5/12
CPCC08L71/03C08L2201/02C08L2205/035C08L83/04C08L61/28C08L45/00C08K13/02C08K2003/2244C08K3/34C08K2003/0893C08K5/12C08K3/2279
Inventor 彭孝茹
Owner 郑州峰泰纳米材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap