A kind of water-resistant type SBS foam sole material and preparation method thereof

A shoe sole material and water-resistant technology, which is applied in the direction of shoe soles, footwear, clothing, etc., can solve problems such as unsatisfactory water resistance, shortened lifespan, and performance degradation, so as to reduce performance degradation, improve water resistance, and improve compatibility. Effect

Inactive Publication Date: 2019-01-11
SUZHOU JINGRO TECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this material are: the water resistance is not ideal, and the material will be troubled by hydrolysis in a rainy and humid environment, and the performance decline is obvious, resulting in a shortened life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-resistant type SBS foam sole material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A water-resistant SBS foaming shoe sole material, made of the following components in parts by weight: 36 parts of SBS, 1.5 parts of AC foaming agent, 14 parts of naphthenic oil, 1.5 parts of magnesium stearate, 2 parts of DCP, rare earth Stabilizer 1.8 parts, triphenyl phosphite 0.3 parts, antioxidant GM 0.6 parts, boron carbide fiber 15 parts, PPSS 8.5 parts, SBS-g-MAH 6 parts.

[0027] The steps of its preparation method are as follows:

[0028] (1) Extract boron carbide fibers with ethanol for 40 hours to remove surface impurities, wash with deionized water after extraction, add nitric acid after drying and stir at 90°C for 3 hours, take it out and wash with deionized water to obtain Oxidized boron carbide fibers;

[0029] (2) Add the oxidized boron carbide fiber obtained in step (1) into a rare earth solution with a mass fraction of 0.4%, take it out after soaking at room temperature for 5 hours, and place it in a vacuum drying oven at 90°C to dry to constant weig...

Embodiment 2

[0032] A water-resistant SBS foaming shoe sole material, made of the following components by weight: 50 parts of SBS, 1.8 parts of AC foaming agent, 11 parts of naphthenic oil, 2.5 parts of calcium stearate, 1.5 parts of DCP, rare earth Stabilizer 1.4 parts, triphenyl phosphite 0.4 parts, antioxidant GM 0.8 parts, boron carbide fiber 14 parts, PPSS 8 parts, SBS-g-MAH 10 parts.

[0033] Its preparation method is the same as Example 1.

Embodiment 3

[0035] A kind of water-resistant type SBS foaming sole material, by weight, is made of the following components: 58 parts of SBS, 1.4 parts of AC foaming agent, 15 parts of naphthenic oil, 2 parts of calcium stearate, 1.8 parts of DCP, Rare earth stabilizer 2 parts, triphenyl phosphite 0.4 part, antioxidant GM 1 part, boron carbide fiber 14.5 parts, PPSS 10 parts, SBS-g-MAH 7 parts.

[0036] Its preparation method is the same as Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a waterproof SBS foaming sole material.The waterproof SBS foaming sole material is prepared from, by weight, 36-58 parts of SBS, 1-2 parts of foamer, 10-15 parts of softening oil, 1-3 parts of mold release agent, 1-2 parts of cross-linking agent, 1-2 parts of thermal stabilizer, 0.2-0.4 part of light stabilizer, 0.5-1 part of antioxidant, 14-18 parts of boron carbide fiber, 8-12 parts of PPSS and 5-10 parts of compatilizer.The invention further provides a preparation method of the foaming sole material.The waterproof SBS foaming sole material has high waterproofness and long service life.

Description

Technical field: [0001] The invention relates to a shoe sole material, in particular to a water-resistant SBS foamed shoe sole material and a preparation method thereof. Background technique: [0002] SBS is a thermoplastic elastomer prepared by anionic polymerization of styrene and butadiene with alkyllithium as a catalyst. Compared with other thermoplastic elastomers, SBS has the characteristics of high strength, softness, and small permanent deformation. Rubber elasticity, suitable for adhesives and sealing materials for hot-melt processing, in the shoe industry, polymer modification, asphalt modification, waterproof coatings, liquid sealing materials, wires, cables, automotive parts, medical equipment parts, household appliances, It has a wide range of applications in office automation and adhesives, and has broad prospects for development and utilization. At present, my country's SBS products are mainly used in shoemaking, asphalt modification, polymer modification and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K13/06C08L53/02C08L81/06C08K9/02C08K7/04C08K5/098C08K5/526A43B13/04C08J9/10
CPCA43B13/04C08J9/103C08J2203/04C08J2353/02C08J2481/06C08L53/02C08L2201/08C08L2203/14C08L2205/035C08L81/06C08K13/06C08K9/02C08K7/04C08K5/098C08K5/526
Inventor 黄超
Owner SUZHOU JINGRO TECH