Noble metal catalyst for catalytic wet oxidation and preparation method thereof

A technology for catalyzing wet oxidation and catalysts, applied in metal/metal oxide/metal hydroxide catalysts, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problem of unstable properties of amorphous alumina, sludge impurities High content and complex structure

Active Publication Date: 2018-05-29
FUSHUN HUANKE PETROCHEM TECH DEV CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method belongs to the process of physical mixing of alumina-containing species and activated carbon, and the dispersion of alumina and activated carbon is uneven; and the sludge used has high impurity content, and the obtained amorphous alumina is unstable, unrepeatable, and complex in structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Solid aluminum chloride was added to distilled water while heating and stirring until dissolved to obtain solution (a). Add an appropriate amount of distilled water to the concentrated ammonia water and dilute it into about 10wt% dilute ammonia water (b). Powdered coconut shell charcoal is impregnated with an impregnating solution containing Pt-Ce. The impregnated activated carbon is dried at 120°C for 240 minutes, roasted at 500°C for 4 hours under the protection of nitrogen, then added to glucose aqueous solution and mixed evenly. The liquid-solid volume ratio is 3 : 1, then add water and beat to obtain slurry (c). After adding (a) into the gelling tank and stirring and heating to 60°C, open the valve of the container containing (b), and control the system in the tank to drop to pH=4.0 within 10 minutes, then add (c), continue to add (b) dropwise, and control the dropwise addition of the tank system to pH=8.0 within 30 minutes. Keep the temperature at 60°C, pH=8.0, ...

Embodiment 2

[0053]Solid aluminum sulfate was added to distilled water while heating and stirring until dissolved to obtain solution (a). Add an appropriate amount of distilled water to the concentrated ammonia water and dilute it into about 10wt% dilute ammonia water (b). The powdered coconut shell charcoal is impregnated with an impregnating solution containing Rh-Ce. The impregnated activated carbon is dried at 120°C for 240 minutes, roasted at 500°C for 4 hours under the protection of nitrogen, then added to the aqueous glucose solution and mixed evenly. The liquid-solid volume ratio is 3 : 1, then add water to make a slurry to obtain activated carbon slurry (c). Take a plastic tank, add (a) into the tank, stir and heat to 60°C, open the valve of the container containing (b), control the system in the tank to drop to pH=4.0 within 10 minutes, open (c ) the valve of the container, continue to drop (b), control the dropwise addition of the system in the tank to pH=8.0 within 30 minutes,...

Embodiment 3

[0056] Solid aluminum sulfate was added to distilled water while heating and stirring until dissolved to obtain solution (a). The solid sodium metaaluminate is formulated to a concentration of 250g Al 2 o 3 / L sodium aluminate solution (b). The powdered coconut shell charcoal was impregnated with an impregnating solution containing Rh-Ce, and the impregnated activated carbon was dried at 120°C for 240 minutes, and then roasted at 500°C for 4 hours under the protection of nitrogen, then added to the sucrose aqueous solution and mixed evenly, the liquid-solid volume ratio was 3:1, then add water and beat to obtain slurry (c). The water glass is diluted in deionized water according to the ratio of 1:2 to prepare solution (d). Take a glue tank, put 2L of deionized water into it, stir and heat it to 60°C, then add the slurry (c), open the valve of the container containing (a) and (b) at the same time, control the pH of the system to 8.0, and control it for 45 minutes After drip...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a noble metal catalyst for catalyzing wet oxidation and a preparation method thereof. The catalyst includes the following core-shell structure components, the core-shell structure components are activated carbon loaded with noble metals and rare earth metals as the core, with alumina or amorphous silica aluminum as the shell, and the preparation method is alumina or amorphous silica The activated carbon slurry loaded with precious metals and rare earth metals is introduced into the aluminum gelling process, and the catalyst is obtained through aging and other steps after gelling. The catalyst has high reactivity and stability in use.

Description

technical field [0001] The invention relates to a catalytic wet oxidation catalyst and a preparation method thereof, in particular to a noble metal catalyst for catalytic wet oxidation and a preparation method thereof. Background technique [0002] With the increasingly stringent global environmental protection regulations, the control indicators for sewage discharge standards are getting higher and higher. Under this form, wastewater catalytic oxidation treatment methods have been paid more and more attention to and adopted by people, such as the catalytic wet method of high-concentration sewage Oxidation, electrolytic catalytic oxidation, photocatalytic oxidation, advanced oxidation, etc. In the process of catalytic oxidation of wastewater, in order to obtain the ideal treatment effect and keep the cost of wastewater treatment low by reducing the reaction temperature and pressure, the preparation of cheap catalysts with high active components, high strength and high stabil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/63C02F1/72
Inventor 蒋广安邓德刚单广波刘雪玲张晔李宝忠郭宏山刘忠生
Owner FUSHUN HUANKE PETROCHEM TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com