Method for preparing high-activity aluminum oxide powder using aluminum ash

A kind of aluminum oxide powder, high activity technology, applied in the direction of alumina/hydroxide, etc., can solve the problems of high energy consumption, low recovery rate of aluminum ash, large powder particles, etc., to solve the problem of environmental pollution and realize sustainable Sustained utilization and uniform particle size distribution

Inactive Publication Date: 2016-07-06
CHANGZHOU DAAO NEW MATERIAL TECH CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to solve the disadvantages of low recovery rate of aluminum ash treatment, high energy consumption, environmental pollution, and the aluminum oxide powder produced by the current method has large particles, wide particle size distribution and easy agglomeration , provides a kind of aluminum ash as raw material, water floats to remove slag, adds sulfuric acid solution and diisopropanolamine to remove insoluble matter in aluminum ash, and then removes dissolved potassium hydroxide under the action of carbon disulfide and titanium dioxide For other metal impurities, add polyethylene glycol and ammonia water and stir to obtain a jelly, then wash, dry, calcinate, and pulverize to obtain a high-activity alumina powder.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] First put the aluminum ash into the container, add water to it to submerge the aluminum ash by 5cm, then use the agitator to stir it at a speed of 300r / min for 20min, then let it stand until no sediment sinks, and remove the impurities floating on the water surface , and then filter it under reduced pressure, rinse the filtrate with absolute ethanol for 3 times, then put the filtered aluminum ash in an oven to dry; then put the above-mentioned 200g of dried aluminum ash into a 1L container, pour Add a sulfuric acid solution with a mass fraction of 40%, stir until the solid is no longer dissolved, stop adding the sulfuric acid solution, then filter, collect the filtrate, add diisopropanolamine with 5% aluminum ash mass, and heat the 1L container to 60°C and keep warm for 50min; after the above keep warm, stop heating, add potassium hydroxide solution with a mass fraction of 20% to it, adjust the pH to 12.0, then move the 1L container to an ice bath, and set the temperatur...

example 2

[0019]First, put the aluminum ash into the container, add water to it to submerge the aluminum ash by 6cm, then use the agitator to stir it at 400r / min for 23min, then let it stand until no sediment sinks, and remove the impurities floating on the water surface , and then filter it under reduced pressure, rinse the filtrate with absolute ethanol for 4 times, then put the filtered aluminum ash in an oven to dry; then put the above-mentioned 250g of dried aluminum ash into a 1L container, pour Add a sulfuric acid solution with a mass fraction of 40%, stir until the solid is no longer dissolved, stop adding the sulfuric acid solution, then filter, collect the filtrate, add diisopropanolamine with an aluminum ash mass of 7%, and heat the 1L container to 63°C and keep warm for 60min; after the above keep warm, stop heating, add potassium hydroxide solution with a mass fraction of 20% to it, adjust the pH to 12.5, then move the 1L container to an ice bath, and set the temperature to ...

example 3

[0021] First put the aluminum ash into the container, add water to it to submerge the aluminum ash by 7cm, then use the agitator to stir it at a speed of 500r / min for 25min, then let it stand until no sediment sinks, and take out the impurities floating on the water surface , and then filter it under reduced pressure, rinse the filtrate with absolute ethanol for 5 times, then put the filtered aluminum ash in an oven to dry; then put the above-mentioned 300g of dried aluminum ash into a 1L container, Add a sulfuric acid solution with a mass fraction of 40%, stir until the solid is no longer dissolved, stop adding the sulfuric acid solution, then filter, collect the filtrate, add diisopropanolamine with an aluminum ash mass of 8%, and heat the 1L container to 65°C and keep warm for 70min; after the above keep warm, stop heating, add potassium hydroxide solution with a mass fraction of 20% to it, adjust the pH to 13.0, then move the 1L container to an ice bath, and set the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing high-activity alumina powder by using aluminum ash, which belongs to the field of alumina powder preparation. The invention uses aluminum ash as raw material, removes slag by floating in water, adds sulfuric acid solution and diisopropanolamine to remove insoluble matter in aluminum ash, and then removes other metal impurities dissolved in potassium hydroxide under the action of carbon disulfide and titanium dioxide , by adding polyethylene glycol and ammonia water and stirring to obtain a jelly, which is washed, dried, calcined, and pulverized to obtain a high-activity alumina powder. The beneficial effects of the present invention are: the present invention makes full use of aluminum ash to prepare high-activity alumina powder, which not only solves the problem of environmental pollution, but also realizes the sustainable utilization of resources; the obtained alumina powder has small particles and uniform particle size distribution. It is not easy to agglomerate, and its activity is more than 18% higher than that of alumina powder prepared by other methods.

Description

technical field [0001] The invention relates to a method for preparing high-activity alumina powder by using aluminum ash, which belongs to the field of alumina powder preparation. Background technique [0002] Alumina powder has excellent physical, chemical, optical, mechanical and thermal properties, and has been widely used in many fields such as chemical industry, electronics, machinery, special ceramics, etc. Its important role in lighting and peninsula industry is also becoming more and more prominent. At present, there are many methods for preparing ultrafine alumina, which are mainly divided into solid-phase method, gas-phase method, liquid-phase method and organic alcohol salt hydrolysis method according to the reaction principle. However, each method has its own limitations. For example, the solid-phase method has complex processes, expensive alkoxides, it is difficult to prepare small particles less than 100nnl, and the particle crystal form is not ideal; the gas-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01F7/02
CPCC01F7/02C01P2004/62C01P2006/11C01P2006/12
Inventor 王力威盛艳花宋国
Owner CHANGZHOU DAAO NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap