High-performance water-based epoxy resin automobile paint and preparation method thereof
A water-based epoxy resin and epoxy resin technology, used in epoxy resin coatings, anti-corrosion coatings, coatings, etc., can solve the problems of large dispersed phase size and poor stability, and achieve low cost, good stability, and adhesion. high effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1
[0032] The preparation method of the high-performance water-based epoxy resin automobile coating of the present invention includes the following steps:
[0033] a. Preparation of emulsifier X
[0034] Add 10 parts by weight of epoxy resin E20 and 50 parts of polyol PEG6000 into a four-necked flask equipped with a stirrer, condenser and thermometer. After heating up to the two completely melted, add the catalyst boron trifluoride dropwise 0.5 part of ether complex, react at 100°C for 3h, add 60 parts of deionized water to obtain light yellow transparent epoxy resin emulsifier X;
[0035] b. Preparation of component A
[0036] Add 3 parts by weight of emulsifier X (prepared in step a) and 3 parts of cosolvent propylene glycol methyl ether into 60 parts of epoxy resin E20. The temperature of the system is controlled at 50°C, and after rapid stirring for 50 minutes, add dropwise Ionized water until the viscosity of the system suddenly decreases and a uniform emulsion is...
Example Embodiment
[0041] Example 2
[0042] The preparation method of the high-performance waterborne epoxy resin automobile coating of the present invention includes the following steps:
[0043] a. Preparation of emulsifier X
[0044] Add 10 parts by weight of epoxy resin E44 and 50 parts of polyol PEG4000 into a four-necked flask equipped with a stirrer, condenser and thermometer. After heating up to the two completely melted, add the catalyst dilauric acid dropwise. 1 part of butyl tin, react at 80°C for 4 hours, add 60 parts of deionized water to obtain light yellow transparent epoxy resin emulsifier X;
[0045] b. Preparation of component A
[0046] Add 3 parts by weight of emulsifier X (prepared in step a) and 4 parts of cosolvent ethylene glycol butyl ether into 60 parts of epoxy resin E44. The temperature of the system is controlled at 50°C, and after rapid stirring for 40 minutes, dropwise Add deionized water until the viscosity of the system suddenly decreases and a uniform emulsion is forme...
Example Embodiment
[0051] Example 3
[0052] The preparation method of the high-performance water-based epoxy resin automobile coating of the present invention includes the following steps:
[0053] a. Preparation of emulsifier X
[0054] Add 10 parts by weight of epoxy resin E51 and 50 parts of polyol PPG3000 into a four-necked flask equipped with a stirrer, condenser and thermometer. After heating up to the two completely melted, add the catalyst triphenylphosphine dropwise 0.8 part, react at 90°C for 5h, add 60 parts of deionized water to obtain light yellow transparent epoxy resin emulsifier X;
[0055] b. Preparation of component A
[0056] Add 3 parts by weight of emulsifier X (prepared in step a) and 2 parts of co-solvent diethylene glycol monomethyl ether into 60 parts of epoxy resin E51. The temperature of the system is controlled at 60°C, and after rapid stirring for 30 minutes, Add deionized water dropwise until the viscosity of the system suddenly decreases and a uniform emulsion is formed, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap