Treatment method for metallurgy sintering of abandoned SCR flue gas denitrification catalyst

A technology of denitrification catalyst and sintering treatment, which is applied in the field of environmental protection and iron and steel metallurgical engineering, and can solve the problems of high treatment cost, high cost of recycling heavy metals, unsuitable for mass production, etc.

Active Publication Date: 2016-08-31
ZHEJIANG UNIV
View PDF9 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The highly toxic vanadium compound is added to the regeneration solution, which will cause serious pollution during use;
[0007] 3) The cost of recycling heavy metals is too high, the benefit is not obvious, and it is not suitable for mass production;
[0008] 4) The space required for landfill is relatively large, and the processing cost is relatively high. For example, the patent application with publication number CN104926235A discloses a treatment and solidification method before the waste SCR denitrification catalyst is buried. , Portland cement, sand and water are mixed and fully stirred into concrete and then poured into blocks. When the strength of concrete cubes is not less than 30mPa, they are respectively plastic-sealed with thick plastic sheets and then buried.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method for metallurgy sintering of abandoned SCR flue gas denitrification catalyst
  • Treatment method for metallurgy sintering of abandoned SCR flue gas denitrification catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] Such as figure 1 As shown, the process system for metallurgical sintering treatment of waste SCR flue gas denitrification catalyst includes 100 chimney, 101 induced draft fan, 102 bag filter, 103 sintering machine igniter, 104 pelletizing equipment, 105 fuel, 106 return ore, 107 flux, 108 Iron ore powder, 109 grinding equipment, 111 polishing machine, 110 cutting machine, 112 sintering machine trolley and 113 cooling machine.

[0030] In this embodiment, the metallurgical sintering process of the waste SCR flue gas denitrification catalyst is as follows:

[0031] (1) Catalyst crushing: The waste SCR flue gas denitrification catalyst unit is separated from the module, and each unit is crushed and ground.

[0032] If the waste SCR flue gas denitrification catalyst is a flat-plate denitrification catalyst, the veneer is first ground by a grinder 111 to obtain a catalyst powder of 100 to 200 mesh, and the ground stainless steel mesh is crushed by a cutting machine 110 to o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a treatment method for metallurgy sintering of an abandoned SCR flue gas denitrification catalyst. The method is characterized by comprising the following steps that the catalyst is broken, wherein the abandoned SCR flue gas denitrification catalyst is broken and ground, and catalyst powder being 100 meshes to 200 meshes is obtained; granulating is conducted, wherein the catalyst powder with the weight percent being 1% to 20% is mixed with iron ore powder, a fluxing agent, fuel, return fines and water, and a sintering mixture is obtained through granulating; and sintering is conducted, wherein the sintering mixture is laid on a bedding material of a sintering machine trolley to be sintered, and sintered ores are formed. By means of the method, the abandoned denitrification catalyst can be treated, the leaching amount of heavy metal of a formed sintered body is relatively low, the environment-friendly requirement is met, and meanwhile parts of the sintered ores can meet the performance requirement and used for blast furnace smelting.

Description

technical field [0001] The invention relates to the technical fields of environmental protection and iron and steel metallurgical engineering, in particular to a metallurgical sintering treatment method for a waste SCR flue gas denitrification catalyst. Background technique [0002] Nitrogen oxides (NO x ) is one of the main components of air pollutants and the main cause of photochemical smog and acid rain. In our country 70% NO x Emissions come from the combustion of coal, of which coal consumption in thermal power plants accounts for more than 50% of the country's total, how to effectively control NO x emissions have become the focus of attention in my country and even in the world. Among many treatment methods, Selective Catalytic Reduction (SCR) is the current method to control NO x The most mature and efficient method of emission is also the method with the most industrial application (96%). Catalyst is the core of SCR technology, and its designed service life is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/16
CPCC22B1/16
Inventor 周昊国旭涛周明熙
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products