Optical self-cleaning granite-like paint and preparation method thereof

A real stone paint and self-cleaning technology, which is applied to biocide-containing paints, coatings, antifouling/underwater coatings, etc., can solve the problems of affecting the aesthetic effect, the difficulty of hydrolysis reaction, and the high price of ethyl silicate , to achieve the effect of improving stain resistance, reducing the application of stone materials, and good stain resistance

Inactive Publication Date: 2016-09-28
厦门富思特新材料科技有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, real stone paint is limited to its own formula problem, and its stain resistance problem has been the biggest problem of real stone paint for many years, and it is also a very difficult problem in the industry
After the real stone paint is painted, it will inevitably be stained with some dust, dirt, etc. under natural conditions, which will affect its overall aesthetic effect.
[0004] Chinese invention patent application CN 105060775 A discloses a real stone paint and its preparation method, which is mixed with emulsion, ethyl silicate, zirconium silicate, nano-titanium dioxide, natural coarse colored sand, natural fine colored sand and rock flakes of various colors. The hydrolysis of ethyl silicate results in ortho silicic acid, which reacts with zirconium silicate, but ethyl silicate is insoluble in water at room temperature, so it is difficult to carry out the hydrolysis reaction, and the market price of ethyl silicate is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Prepare raw materials according to the components and contents in Table 1:

[0043] Table 1 embodiment 1 prepares real stone paint component content table

[0044] serial number

material name

Ratio% (mass)

1

Natural colored sand

67

2

polymer emulsion

10

3

Nano Titanium Dioxide

12

4

Hydroxyethyl cellulose

0.5

5

fungicide

0.3

6

antifreeze

1

7

Auxiliary

1

8

water

8.2

[0045] Among them, the particle size of natural colored sand is 40 mesh, the polymer emulsion is acrylic acid emulsion; hydroxyethyl cellulose is a non-ionic water-soluble cellulose ether; the nano-titanium dioxide is anatase type, and its particle size distribution is 10-30nm Antifreezing agent is ethylene glycol; Described bactericide is isothiazolinone bactericide; Auxiliary agent is film-forming aid, defoamer, wetting agent and thickener are 10:10:2 by mass ratio: 5, the film-for...

Embodiment 2

[0050] Prepare raw materials according to the composition and content of Table 2:

[0051] Table 2 embodiment 2 prepares real stone paint component content table

[0052] serial number

material name

Ratio% (mass)

1

Natural colored sand

74

2

polymer emulsion

10

3

Nano Titanium Dioxide

8

4

Hydroxyethyl cellulose

0.2

5

fungicide

0.3

6

antifreeze

0.5

7

Auxiliary

1

8

water

6

[0053] Among them, the particle size of natural colored sand is 120 mesh, the polymer emulsion is acrylic silicon emulsion; hydroxyethyl cellulose is a non-ionic water-soluble cellulose ether; the nano-titanium dioxide is anatase type, and its particle size distribution is 10- 30nm; Antifreezing agent is propylene glycol; Described bactericide is isothiazolinone bactericide; Auxiliary agent is film-forming aid, defoamer, wetting agent and thickener are 10:10:2:5 by mass ratio The mixt...

Embodiment 3

[0057] Prepare raw materials according to the composition and content of Table 3:

[0058] Table 3 embodiment 3 prepares real stone paint component content table

[0059] serial number

material name

Ratio% (mass)

1

Natural colored sand

67

2

polymer emulsion

10

3

Nano Titanium Dioxide

12

4

Hydroxyethyl cellulose

0.5

5

fungicide

0.5

6

antifreeze

1

7

Auxiliary

2

8

water

6

[0060] Among them, the particle size of natural colored sand is 100 mesh, the polymer emulsion is acrylic emulsion; hydroxyethyl cellulose is a non-ionic water-soluble cellulose ether; the nano-titanium dioxide is anatase type, and its particle size distribution is 10-30nm Antifreezing agent is glycerol; Described bactericide is isothiazolinone bactericide; Auxiliary agent is film-forming aid, defoamer, wetting agent and thickener are 10:10:2 by mass ratio: 5, the film-forming aid is a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to optical self-cleaning granite-like paint and a preparation method thereof. The paint is prepared from the following components in percentage by weight: 60-74 percent of natural colored sands, 10-20 percent of polymer emulsion, 8-12 percent of nano-titanium dioxide, 0.2-0.5 percent of hydroxyethyl cellulose, 0.3-0.5 percent of bactericide, 0.5-1.0 percent of an antifreezing agent, 1-2 percent of auxiliary and 6-14 percent of water. Anatase nano-titanium dioxide is applied to manufacture of granite-like paint, so that the granite-like paint has an excellent granite imitation effect, and has the effect which is basically the same as that of existing granite-like paint; the granite-like paint has an excellent fouling resistance, and the fouling resistance of a wall surface can be effectively improved.

Description

technical field [0001] The invention relates to the field of coatings for exterior wall decoration, in particular to a light-energy self-cleaning real stone paint and a preparation method thereof. Background technique [0002] Real stone paint, also known as imitation stone paint, colored glaze quartz sand paint, the construction industry standard is called synthetic resin emulsion sand wall architectural paint, which is based on synthetic resin emulsion and natural colored sand with different particle sizes as aggregate. Thick architectural coatings prepared with various additives. Compared with traditional pasted tiles and dry-hanging stone materials, real stone paint is favored by more and more people because of its obvious advantages such as convenient construction, low cost, safety and non-toxicity, natural and generous, durable, and the decorative effect is closest to stone materials. . Among them, colored sand real stone paint has been highly concerned by the indust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12C09D5/28C09D5/16
CPCC09D133/04C08K2201/011C08L2205/035C09D5/1618C09D5/28C09D7/67C09D143/04C08L1/284C08L91/00C08L33/02C08K13/02C08K2003/2237
Inventor 姜年超林富聪姜向阳
Owner 厦门富思特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products